Influence of Chemical and Mineralogical Composition of Steelmaking Slags on their Next Utilization

Baricova D., Pribulova A., Bulko B., Demeter P.

Hutnik, Wiadomości Hutnicze

2018

Vol. 85, nr 11

389--393

The major waste products of metallurgical production are slags. The amount of steelmaking slag is about 65-150 kg per tonne of crude steel produced. At present, there is an effort to reduce the amount of slag arising, which is possible by pretreatment of pig iron, secondary metallurgy of molten steel and careful selection of batch materials. Despite all efforts, the amount of slag produced represents about 13% of the total batch. The paper focuses exclusively on primary slags from the steelmaking process in the oxygen converter and the electric arc furnace. The chemical and mineralogical composition of the steelmaking slag will be the most significant factor affecting its further potential use. Authors describes hydraulicity of slags as function of composition, and also their next utilization in concrete construction.

Głównymi odpadami metalurgicznymi są żużle. Ilość żużla stalowniczego wynosi około 65-150 kg na tonę wyprodukowanej surowej stali. Obecnie dąży się do zmniejszenia ilości powstających żużli, co jest możliwe dzięki obróbce wstępnej surówki, wtórnej metalurgii stali i starannej selekcji materiałów wsadowych. Pomimo wszystkich zabiegów, ilość wytwarzanego żużla stanowi około 13% całkowitej produkcji. Artykuł koncentruje się głównie na żużlach z procesów stalowniczych z konwertora tlenowego i elektrycznego pieca łukowego. Skład chemiczny i mineralogiczny żużla stalowniczego jest najważniejszym czynnikiem wpływającym na jego dalsze potencjalne wykorzystanie. Autorzy opisują hydrauliczność żużli jako funkcję składu, a także ich kolejne wykorzystanie w konstrukcjach betonowych.

The influence of chemical composition of steel on steel desulphurization

Bulko B., Kijac J., Borovský T.

Archives of Metallurgy and Materials

2011

Vol. 56, iss. 3

605-609

The steel desulphurization in ladle furnace depends on temperature, oxygen and sulphur content in the steel, but mainly on chemical composition and physical properties of slag. Necessary requirement for effective desulphurization is also minimum content of easily reducible oxides in the slag. There are many correlations for expression of slag desulphurization capability, where their functional dependency on each other can be found, mainly between sulphur distribution coefficient, optical basicity, basicity, sulphide capacity, desulphurisation potential of slag and also calcium - aluminate ratio of oxides in slag or content of easily reducible oxides in slag. This work presents statistical and graphical correlation between manganese and slag parameters using the set of approximately 768 heats and based on these, the optimal parameters for slag desulphurization capability are expressed especially for steel grades internally marked as OR1, OR3 in Železiarne Podbrezová, a.s. Steel grades OR1 and OR3 were chosen because of difference in manganese content with similar chemical composition of other elements. The MnO content in the slag is one of the most important parameters. Despite the higher scatter of obtained values, the distribution coefficient of sulphur (Ls) is one of the wide range of parameters for whom exists very close dependence on MnO content in slag.

Odsiarczanie stali zależy od temperatury, zawartości tlenu i siarki w stali, ale przede wszystkim od składu chemicznego i właściwości fizycznych żużla. Dla skutecznego odsiarczania konieczna jest również minimalna zawartość łatwo redukowalnych tlenków w żużlu. Istnieje wiele zależności do wyrażenia zdolności żużla do odsiarczania, dla których można znaleźć funkcyjną zależność pomiędzy współczynnikiem podziału siarki, optyczną zasadowością, zasadowością, zawartością siarczków, potencjałem odsiarczania żużla, a także stosunkiem tlenków wapnia do glinu w żużlu lub zawartością łatwo redukowalnych tlenków w żużlu. W pracy przedstawiono statystyczną i graficzną korelację pomiędzy zawartością manganu i parametrami żużla uzyskaną z około 768 wytopów, i na ich podstawie optymalne parametry zdolności żużla do odsiarczania przedstawione zostały dla stali wewnętrznie oznaczonych jako OR1, OR3 w Železiarne Podbrezová, a.s. Gatunki stali OR1 i OR3 zostały wybrane ze względu na różnice w zawartości manganu przy podobnej zawartości innych składników. Zawartość MnO w żużlu jest jednym z najważniejszych parametrów. Mimo większego rozrzutu uzyskanych wartości, współczynnik podziału siarki (Ls) jest jednym z wielu parametrów, dla których istnieje bardzo ścisła zależność od zawartości MnO w żużlu. Keywords