Internal Friction of Li7La3Zr2O12 Based Lithium Ionic Conductors

Wang X. P., Song L., Hu J., Xia Y. P., Xia Y., Gao Y. X., Zhang L. C., Magalas L. B., Fang Q. F.

Archives of Metallurgy and Materials

2016

Vol. 61, iss. 1

21--24

The diffusion mechanisms of lithium ions in tetragonal phase as well as in Al and Nb stabilized cubic Li7La3Zr2O12 compounds were investigated by low-frequency internal friction technique. In the cubic Li7La3Zr2O12 phase, a remarkable relaxation-type internal friction peak PC with a peak height up to 0.12 was observed in the temperature range from 15°C to 60°C. In the tetragonal phase however, the height of the PT peak dropped to 0.01. The obvious difference of the relaxation strength between the cubic and tetragonal phases is due to the different distribution of lithium ions in lattice, ordered in the tetragonal phase and disordered in the cubic phase. Based on the crystalline structure of the cubic garnet-type Li7La3Zr2O12 compound, it is suggested that the high internal friction peak in the cubic phase may be attributed to two diffusion processes of lithium ions: 96h↔96h and 96h↔24d.

The Internal Friction of Single Crystals, Bicrystals and Polycrystals of Pure Magnesium

Jiang W. B., Kong Q. P., Magalas L. B., Fang Q. F.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 1

371--375

The internal friction of magnesium single crystals, bicrystals and polycrystals has been studied between room temperature and 450°C. There is no internal friction peak in the single crystals, but a prominent relaxation peak appears at around 160°C in polycrystals. The activation energy of the peak is 1.0 eV, which is consistent with the grain boundary self-diffusion energy of Mg. Therefore, the peak in polycrystals can be attributed to grain boundary relaxation. For the three studied bicrystals, the grain boundary peak temperatures and activation energies are higher than that of polycrystals, while the peak heights are much lower. The difference between the internal friction peaks in bicrystals and polycrystals is possibly caused by the difference in the concentrations of segregated impurities in grain boundaries.

Badania tarcia wewnętrznego w monokryształach, bikryształach i polikryształach magnezu przeprowadzono w zakresie temperatur między temperaturą pokojową a 450°C. W monokryształach magnezu nie występuje pik tarcia wewnętrznego, ale wyraźny pik relaksacyjny pojawia się przy około 160°C w polikryształach. Energia aktywacji piku wynosi 1,0 eV, co jest zgodne z energią autodyfuzji Mg przez granice ziaren. Z tego względu pik tarcia wewnętrznego występujący w polikryształach można przypisać relaksacji granic ziaren. W przypadku trzech badanych bikryształów temperatury pików pochodzących od granic ziaren i ich energie aktywacji są wyższe niż w przypadku polikryształów, ale wysokości tych pików są znacznie niższe. Różnica między pikami tarcia wewnętrznego w bikryształach i polikryształach jest prawdopodobnie spowodowana przez różnicę stężeń zanieczyszczeń segregujących na granicach ziaren.