Formation of crystallographic texture during severe plastic deformation

Alexandrov I. V., Zhilina M. V., Scherbakov A. V., Korshunov A. I., Nizovtsev P. N., Smolyakov A. A., Solovyev V. P., Beyerlein I. J., Valiev R. Z.

Archives of Metallurgy and Materials

2005

Vol. 50, iss. 2

281-294

The current paper represents the results of recent investigations, aimed at revealing of regularities and establishing of crystallographic texture evolution mechanisms during equal-channel angular pressing (ECAP). Pure Cu was used as material for investigation. The investigations were conducted with the help of computer simulation. The variable parameter was the friction coeffcient. Accumulated strain fields, as well as strain rate gradients, were calculated using the variation-diffrence method (VDM) and the simplest isotropic material model. The strain rate gradients from the VDM program served as input parameters for the viscous-plastic self-consistent model (VPSC), simulating the texture formation processes. Results of modeling are compared to experimental texture measurements.

W pracy przedstawiono wyniki najnowszych badań dotyczących prawidłowości mechanizmu formowania się tekstury krystalograficznej czystej miedzi podczas wyciskania w kanale kątowym (ECAP). Parametrem zmiennym był współczynnik tarcia. Badania wsparto symulacją komputerową. Za pomoca metody wariacyjno-różniczkowej (VDM) oraz uproszczonego modelu materiału izotropowego obliczono skumulowane pola odkształceń i gradienty prędkości odkształcenia. Gradienty prędkości odkształcenia z programu VDM posłużyły jako parametry wejściowe dla samouzgodnionego, visko- plastycznego modelu (VPSC) symulującego proces formowania się tekstury.Wyniki modelowania porównano z doświadczalnymi pomiarami tekstury.

Analysis of texture formation homogeneity processes during equal-channel angular pressing

Zhilina M. V., Bonarski J., Scherbakov A. V., Alexandrov I. V., Makarychev K.

Archives of Metallurgy and Materials

2005

Vol. 50, iss. 2

479-485

Experimental investigations of texture formation processes were conducted in selected zones of cross section of bulk billets, subjected to equal channel angular (ECA) pressing. Pure Cu and Ti with fcc and hcp lattices, respectively were chosen as investigated materials. There was considered a case of 12 ECA pressing passes (route Bc). The angle of channels’ intersection during ECA pressing was 90°. ECA pressing rate was 6 mm/s. In the case of Cu deformation was carried out at room temperature and in the case of Ti it was elevated to 450°C. Experimental tests were carried out by means of X-ray diffraction technique. For both investigated materials, the incomplete back-reflection pole figures in selected areas of prepared samples were registered. The texture functions calculated on the basis of such incomplete pole figures enabled to calculate both the complete and inverse pole figures, and to perform the qualitative and quantitative texture analysis. Conclusions on texture homogeneity during ECA pressing of bulk Cu and Ti ingots were drawn.

Eksperymentalne badania procesu tworzenia tekstury przeprowadzono w wybranych obszarach przekroju poprzecznego litych próbek poddanych wyciskaniu w kanale kątowym (ECA) o przekroju kwadratowym. Materiałami wybranymi do badań były Cu i Ti o strukturze odpowiednio fcc i hcp. Rozważano przypadek 12 przepustów wyciskania (droga Bc), przy czym kąt zakrzywienia kanału wynosił 90°. Szybkość wyciskania wynosiła 6 mm/s. W przypadky Cu deformacje przeprowadzono w temperaturze pokojowej, podczas gdy Ti w 450°C. Badania tekstury uzyskanych materiałów przeprowadzono metodą dyfrakcji rentgenowskiej. Wyznaczono niekompletne figury biegunowe wybranych obszarów uzyskanych próbek. Obliczone na podstawie niekompletnych figur biegunowych funkcje tekstury umożliwiły obliczenie kompletnych i odwrotnych figur biegunowych oraz pozwoliły na jakościową i ilościowa analizę tekstury. Wyciągnieto wnioski o jednorodności tekstury podczas wyciskania ECA sztabek Cu i Ti.