TEM studies of <001> oriented single crystal CM186LC superalloy creep deformed at 750 degrees centigrade.

Dubiel B., Grodowski P., Czyrska-Filemonowicz A.

Archives of Materials Science

2005

Vol. 26, nr 1-2

137-144

The microstructure of creep tested CM186LC Ni-base single crystal alloy was studied to assess its suitability for use in the gas turbine environment. Creep tests were conducted at 750 degrees C and at stresses 560 and 675 MPa up to 11440 h. Microstructure of fractured and terminated specimens was investigated in detail. TEM microstructural analysis revealed dislocations in gamma channels piled-up mainly at the gamma/gamma' interfaces. Beside dislocations in gamma channels, shearing of gamma' particles by partial dislocations separated by stacking faults was observed.

Microstructural study of creep deformed as cast Ni-base single crystal alloy CM186LC for advanced gas turbines

Dubiel B., Grodowski P., Czyrska-Filemonowicz A.

Inżynieria Materiałowa

2004

R. XXV, nr 3

339-342

The microstructure of creep tested CM186LC Ni-base single crystal alloy was studied to assess its suitability for use in the industrial gas turbine environment. Creep tests were conducted at 750°C and at stresses 560 and 675 MPa up to 11440h. Microstructure of fractured and terminated specimens was detaily investigated. SEM analysis of CM186LC specimens creep tested at 750°C showed mixed brittle and quasi-ductile character of the fracture facets. Creep cracks were seen to initiate at fractured primary MC carbides. TEM microstructural analysis revealed dislocations in gamma channels piled-up mainly at the gamma/gamma' interfaces. Beside dislocations in gamma channels, shearing of gamma' particles by partial dislocations separated by stacking faults was observed.

Zbadano mikrostrukturę stopu CM186LC w aspekcie zastosowania tego materiału na łopatki turbin gazowych. Przeprowadzono próby pełzania w temperaturze 750°C przy naprężeniach 560 i 675 MPa, trwające do 11 440 godzin. Przebadano szczegółowo mikrostrukturę próbek po zerwaniu i po przerywanych próbach pełzania. Badania faktograficzne, przeprowadzone metodami SEM, wykazały mieszany kruchy i quasi-ciągliwy charakter przełomów próbek pełzanych w temperaturze 750°C. Zaobserwowano, że źródła pęknięć w trakcie pełzania powstają wewnątrz wydzieleń pierwotnych węglików MC. Badania mikrostruktury metodami TEM ujawniły spiętrzenia dyslokacji na powierzchniach międzyfazowych gamma/gamma'. Oprócz dyslokacji w kanałach fazy gamma obserwowano przecinanie cząstek fazy gamma' przez dyslokacje częściowe i błędy ułożenia .