Effects Of Anodic Protection On SCC Behavior Of X80 Pipeline Steel In High-pH Carbonate-Bicarbonate Solution

Zhao W., Zou Y., Xia D. X., Zou Z. D.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 2A

1009--1013

The potentiodynamic polarization test and slow strain rate tensile tests of X80 pipeline steel were performed in 0.5M Na2CO3-1M NaHCO3 solution to study the electrochemical and stress corrosion cracking properties. The results of potentiodynamic polarization test show that there is an obvious stable passive region, about from 0v to 0.8V (SCE), indicating that anodic protection is feasible. The results of slow strain rate tensile tests show that the stress corrosion cracking sensibility is high and cathodic protection effect is restricted due to the hydrogen permeation. However, the elongation, yielding strength and tensile strength all increase with anodic protection. The higher anodic protection potential in the stable passive region is benefit to improve tensile strength and yielding strength. However, the higher elongation is obtained at 0.5V (SCE) anodic protection potential.

Badania polaryzacji potencjodyniamicznej oraz próby powolnego rozciągania (SSRT) przeprowadzono na stali typu X80 w roztworze 0,5M Na2CO3-1M NaHCO3. Określono odporność na korozję elektrochemiczną oraz zbadano zjawisko naprężeniowego pękania korozyjnego. Rezultaty badań polaryzacji potencjodynamicznej wykazały istnienie stabilnego obszaru pasywacji w zakresie potencjału od 0V do 0,8V (SCE: półogniwo odniesienia – elektroda kalomelowa). Próby powolnego rozciągania pokazały wysoką wrażliwość materiału na naprężeniowe pękanie korozyjne i ograniczenia ochrony katodowej w związku z przenikaniem wodoru. Ochrona anodowa natomiast, zwiększa znacząco wydłużenie próbki, granicę plastyczności oraz wytrzymałość na rozciąganie. Ponadto zwiększanie wartości potencjału w stabilnym obszarze pasywacji dodatkowo poprawia te właściwości.

Corrosion Resistance Of Electroless Ni-P/Cu/Ni-P Multilayer Coatings

Zhao G. L., Zou Y., Hao Y. L., Zou Z. D.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 2A

1003--1008

Ni-P/Cu/Ni-P multilayer coatings were prepared by deposition of Cu layer between two Ni–P layers. The Cu layer was deposited by metal displacement reaction between Cu2+ and Fe atoms. Corrosion behavior of single-layer Ni-P coatings, double-layer Ni-P/Cu coatings, and three-layer Ni-P/Cu/Ni-P coatings were investigated by electrochemical tests in 3.5% NaCl solution. The three-layer coatings exhibited more positive Ecorr and decreased Icorr compared with conventional single-layer Ni-P coatings, which indicated an improved corrosion resistance. The polarization curves of the three-layer coatings were characterized by two passive regions. The improved corrosion resistance was not only attributed to the function of the blocked pores of Cu. The Cu interlayer also acted as a sacrificial layer instead of a barrier in the coatings, which altered the corrosion mechanism and further improved the corrosion resistance of the coatings.

Wielowarstwowe powłoki Ni-P/Cu/Ni-P wytworzono metodą osadzania miedzi pomiędzy dwoma warstwami Ni-P. Warstwę Cu otrzymano dzięki reakcji wypierania metalu przez metal (dla miedzi i żelaza). Aby określić właściwości korozyjne jednowarstwowej powłoki Ni-P, dwuwarstwowej Ni-P/Cu oraz trójwarstwowej Ni-P/Cu/Ni-P przeprowadzono pomiary elektrochemiczne w 3,5% roztworze NaCl. Powłoki trójwarstwowe w porównaniu do jednowarstwowych wykazały się większą wartością Ecorr, przy malejącej wartości Icorr. Wskazuje to na poprawę odporności na korozję. Krzywe polaryzacji dla powłok trójwarstwowych charakteryzują się występowaniem dwóch obszarów pasywacji. Poprawa odporności na korozję jest skutkiem nie tylko tzw. zjawiska blokowania porów w miedzi. Powłoka z Cu działała także jako warstwa protektorowa, modyfikując mechanizm korozji i poprawiając odporność korozyjną powłok.