Carbon materials such as glassy carbon or C/C composites do not always meet the requirements set down for them in technical and biomechanical applications. The most important problem of the manufacturing process that the authors have managed to overcome was the elimination of internal cracks, which cause splitting, in the finished samples. The resulting uniform research material, due to the extremely sensitive implantation site, must meet the following numerous requirements: have high mechanical and chemical strength, exhibit biotolerance, and have high resistance to tribological wear. The paper presents the results of tribological, stereometric, and micromechanical tests of carbon materials that were annealed in a graphite furnace at temperatures of 1500°C, 2000°C, and 2500°C. In order to analyse tribological characteristics, a methodology for performing tests on the ball-on-disk apparatus (T-01 testing machine) was developed that reflect load conditions prevailing in the real node. The tribological tests of glassy carbon confirmed predictions that the temperature of manufacturing has a big impact on its tribological properties, and a higher temperature of annealing does not always improve the material properties.
PL
Materiały węglowe typu węgiel szklisty lub kompozyt C/C nie zawsze spełniają wymagania im stawiane w zastosowaniach technicznych i biomechanicznych. Najistotniejszym problemem procesu wytwarzania, który udało się autorom pokonać było wyeliminowanie pęknięć wewnętrznych w gotowych próbkach powodujących ich podzielenie. Uzyskany jednolity materiał badawczy ze względu na niezwykle newralgiczne miejsce wszczepienia musi spełniać liczne wymagania: wykazywać wysoką wytrzymałość mechaniczną i chemiczną, biotolerancję oraz wysoką odporność na zużycie tribologiczne. W pracy przedstawiono wyniki badań tribologicznych, stereometrycznych i mikromechanicznych materiałów węglowych, które zostały wygrzane w piecu grafitowym, w temperaturach odpowiednio: 1500°C, 2000°C i 2500°C. W celu przeprowadzenia analiz charakterystyk tribologicznych opracowano metodykę badań na stanowisku kula-tarcza (tester T-01), która powinna odzwierciedlić warunki obciążeniowe panujące w rzeczywistym węźle. Przeprowadzone badania tribologiczne węgla szklistego potwierdziły przypuszczenia, iż temperatura wytwarzania tego materiału ma duży wpływ na jego własności tribologiczne, a wyższa temperatura wygrzewania nie zawsze oznacza poprawę właściwości materiału.
PL
Do produkcji elementów mechanicznych zastawek serca są stosowane różnego typu materiały węglowe (węgiel szklisty lub kompozyt C/C). Ze względu na niezwykle newralgiczne miejsce ich wszczepienia muszą one spełniać liczne wymagania: wykazywać wysoką wytrzymałość mechaniczną i chemiczną, biotolerancję oraz wysoką odporność na zużycie tribologiczne. W pracy przedstawiono wyniki badań tribologicznych i mikromechanicznych materiałów węglowych na różnym etapie ich wytwarzania. W celu przeprowadzenia analiz charakterystyk tribologicznych opracowano metodykę badań na stanowisku kula–tarcza (tester T-01), która może posłużyć do porównania z wynikami uzyskanymi na nanotribometrach.
EN
Carbon materials (glassy carbon or C/C composite) are used for the production of mechanical heart valves. Due to the extremely sensitive place of their implantation, they must meet numerous requirements: mechanical strength, chemical resistance, biotolerance, and a high resistance to tribological wear. The paper presents tribological and micromechanical research results of carbon materials at various stages of their production. In order to perform the analysis of tribological characteristics, the measurement methodology for the ball-on-disk tester (T-01) has been developed. This may allow a comparison of the results obtained with those received on the nanotribometers.
PL
Zbadano adsorpcję powierzchniowo aktywnych substancji (PAS) na trudno rozpuszczalnych osadach nieorganicznych (spreparowanych i naturalnych). Użyto również kwasowego, obojętnego i zasadowego tlenku glina Badano adsorpcję kationowych surfaktantów: bromku cerylopirydyniowego (CPBr), bromku cetylotrimetyloamoniowego (CTMABr), chlorku trioktylometyloanioniowego (Aliquat 336), chlorowodorku tetradecyloaminy (TDAC1) i heksadecyloaminy (HDAC1) oraz surfaktantu anionowego siarczanu dodecylosodowego (SDS). Oznaczenie PAS wykonywano metodą spektrofotometryczną dla kompleksów barwnika z surfaktantem: surfaktanty kationowe z oranżem II a surfaktant anionowy z błękitem metylenowym. Dla tlenku glinu o różnym odczynie powierzchni oprócz pomiarów adsorpcji wykonano pomiary potencjału elektrokinetycznego. Stwierdzono, że zdolność adsorpcyjna PAS zmienia się w następującym szeregu: Aliquat 336
EN
Adsorption of surface active agents onto insoluble precipitates (natural and prepared) was investigated. Acidic, neutral and basic aluminas were also studied. Cationic surfactants: cetylpyridinium bromide (CPBr) cetyltrimethylammonium bromide (CTMABr), trioctylmethylammonium chloride (Aliquat 336), tetradecylamine chloride (TDAC1) and hexadecylamine chloride (HDACl) as well as anionic one sodium dodecylsulfate (SDS) were used in the investigation. Concentration of surface active agents was determined by means of spectrometric method for complexes with a suitable dye, i.e. cationic surfactants with orange II and anionic ones with methylene blue. For alumina the zeta potential measurements were additionally performed. It was stated, that adsorption ability changed in a sequence Aliquat 333 < CTMABr < CPBr, and that HDAC1 adsorbed stronger than TDAC1 on feldspar. For alumina adsorption appeared dependent on the nature of its surface and correlated with the changes in zeta potential.