Microstructure and Microhardness of Piston Alloy Al-10Si-2Cu Irradiated by Pulsed Electron Beam

Zaguliaev D., Konovalov S., Ivanov Y., Abaturova A., Leonov A.

Archives of Foundry Engineering

|

2020

|

Vol. 20, iss. 3

92--98

EN

The paper presents the research data on structure, phase composition, defect substructure state, and microhardness of surface layers in the piston alloy Al-10wt%Si-2wt%Cu irradiated by an electron beam with various energy densities and pulse times. An important finding to emerge from the study is that the processing by an electron beam with an energy density of 10 J/cm2 brings about slight surface melting, whereas a weak thermal impact of an electron beam hardly changes the phase composition. Once an energy density of an electron beam is set 30 J/cm2, intermetallic compounds dissolve and numerous micropores arise. Irradiating by an electron beam with an energy density of 50 J/cm2, randomly located microcracks are detected on the treated surface with no regard to a pulse time. A structure of high-speed cellular crystallization with cells from 500 to 600 nm forms in the surface layer. A thickness of the modified layer is related to a beam energy density. As a beam energy density goes up, a thickness of a high-speed cellular crystallization layer increases. Atoms of Si, Cu, Ni, as well as a small quantity of Fe and Mg are detected in the surface, in thin layers surrounding crystallization cells. In a layer 60-80 μm below the irradiated surface, in material between high-speed crystallization cells, there are Si atoms and an insignificant number of Cu atoms. An analysis of a deeper material part has shown a structure similar to the as cast alloy. A drop of microhardness – if compared with the as cast material – is reported at an energy density of 10 J/cm2 because an energy amount supplied by an electron beam to the alloy surface is insufficient for melting of the material and dissolution of the intermetallic phase. A raise of a beam energy density up to 20-50 J/cm2 causes a max increase of microhardness up to 1.13 GPa for 40 J/cm2, 50 μs, and up to 1.16 GPa for 40 J/cm2, 200 μs.

2

Research into morphology and phase structure in the surface of Al-Si alloy modified by yttrium oxide

Zagulyaev D., Konovalov S., Gromov V., Melnikov A., Shlyarov V.

Bulletin of the Polish Academy of Sciences. Technical Sciences

|

2019

|

Vol. 67, nr 2

173--177

EN

Using methods of physical material studies (scanning electron microscopy and micro X-ray spectral analysis), a study was carried out with focus on alteration of structure and phase composition in surface layers of Al-Si alloy (silumin АК10М2N) treated in electroexplosive alloying with a multiphase plasma jet formed in the process of aluminum foil explosion and carrying particles of Y2O3 weighted powder portion. It was revealed that a porous surface layer with non-homogeneously distributed alloying elements (silicon, yttrium) in it is formed in any conditions of electroexplosive alloying of silumin. Thickness of the modified layer is different, varying 50 to 160 μm, depending on the zone to be examined. The modified surface consists basically of Al, Si and Y. Yttrium in the modified layer is thought to be an indirect evidence of better physical and mechanical properties of the surface layer in comparison with the base material.

3

Dispersion of Al-Si Alloy Structure by Intensive Pulsed Electron Beam

Konovalov S., Gromov V., Zaguliyaev D., Ivanov Y., Semin A., Rubannikova J.

Archives of Foundry Engineering

|

2019

|

iss. 2

79--84

EN

By the method of modern physical material science (optic microscopy scanning and transmission electron microscopy) the analysis of structural phase states, the morphology of the second phase inclusions and defect substructure of Al-Si alloy (silumin) of hypoeutectic composition, subjected to electron beam processing was done with the following parameters: energy density 25-35 J/cm2, beam length 150 μs, pulse number – 3, pulse repetition rate – 0.3 Hz, pressure of residual gas (argon) 0.02 Pa. The surface irradiation results in the melting of the surface layer, the dissolution of boundary inclusions, the stricture formation of high speed cellular crystallization of submicron sizes, the repeated precipitation of the second phase nanodimentional particles. With the increased distance from the irradiation surface the layer containing the second phase inclusions of quasi-equilibrium shape along with the crystallization cells was revealed. It is indicative of the processes of Al-Si alloy structure globalization on electron beam processing.