EN
Chapter VI includes a wide range of microstructure description of steels (carbon steels: K55, N80-1, highly alloyed H13 and stainless steel 316) and composites (GRE — Glassfibre Reinforced Epoxy and HDPE — High-Density Polyethylene), and its influence on their corrosion resistance, leading to elaboration of the database of materials used in the shale gas production system due to their kinetics of degradation. In this Chapter, the modern methods within the study of electrochemical and mechanical properties of selected materials were used. The mechanism and kinetics of corrosion and erosion degradation were measured using electrochemical DC methods (LPR, LSV, potentiostatic and galvanostatic), AC methods — electrochemical impedance spectroscopy (EIS), gravimetric methods and morphological studies of material degradation with the use of image analysis. The composition and structure of corrosion products were investigated by XRD technique, FTIR spectroscopy, and SEM followed by EDS analysis. The Authors focused on four main tasks, the first one included the description of research on the corrosive-erosive wear resistance of steel and composite materials in the crevice fluid and the second comprised of the research on the corrosion resistance of steel and composite materials in the H2O-CO2-H2S atmosphere. The third part of the results presented in this chapter related to the microbiological corrosion resistance SRB (Sulfate Reducing Bacteria) of steel and composite materials in the H2O-CO2-H2S atmosphere. An important part of the investigations described in Chapter 6 was to make the comparison of the corrosive behaviour of steels, which are in frequent use in the shale-gas production system, and composites under the neutral salt spray conditions. Based on the above mentioned experiments, the authors compiled an extensive data- base, where a broad description of corrosion resistance of materials for shale-gas production systems is included. The matching of microstructural features with corrosion resistance and mechanical properties of various types of steel and new generation composite materials would have a strong influence on future experiments conducted in such a common aspect in the shale-gas production system, as materials degradation is.
2
Content available remote Corrosion monitoring of the internal surfaces of tubing in shale gas wells
PL
A corrosion monitoring station was designed and built into a shale gas extraction pipeline. The station is universal and can be used in conventional oil and gas extraction systems. The device has been tested on wells in operational conditions during the fracturing process in Wysin 3H (flowback, flow stimulation with gas lift). The station’s operating pressure ranged from 3 to 40 bar for unsettled outflow of liquid and gas from the well. The proposed monitoring station makes it possible to carry out corrosion (LPR, EIS, ER), as well as physico-chemical (pH, redox potential) “on-line” measurements during the operation of a gas well. Laboratory and field tests have shown that the impedance method of measuring the polarization resistance is sensitive enough to allow both the monitoring of the corrosion rate (including pitting corrosion) as well as the performance of studies that help in the selection of materials and inhibitors.
EN
Zaprojektowano i zbudowano stację monitorowania korozji w liniach wydobycia gazu szczelinowego. Stacja ma charakter uniwersalny i może mieć zastosowanie w konwencjonalnych instalacjach wydobycia ropy i gazu. Urządzenie zostało przetestowane w warunkach ruchowych podczas czynności zabiegowych w odwiertach w Wysinie (odbieranie cieczy wypływowej – flowback, stymulacja złoża dźwigiem gazowym). Ciśnienie pracy stacji wynosiło od 3 do 40 bar przy nieuspokojonym wypływie cieczy i gazu z odwiertu. Proponowana stacja monitorowania pozwala na prowadzenie pomiarów korozyjnych (LPR, EIS, ER) oraz fizykochemicznych (pH, potencjał red-ox) „on line” w trakcie eksploatacji odwiertów gazu. Testy przeprowadzone w laboratorium i w warunkach polowych wykazały, że impedancyjna metoda pomiaru oporu polaryzacyjnego jest czułą metodą pozwalającą zarówno na monitorowanie szybkości korozji (w tym korozji wżerowej) jak i prowadzenie badań w zakresie selekcji materiałów, doboru inhibitorów.
PL
Jednym z ważnych problemów determinujących koszty eksploatacji wód geotermalnych jest korozja rur wydobywczych, instalacji obiegu geotermalnego, armatury oraz kolmatacja otworów zatłaczających. Zjawiska te związane są z korozją mikrobiologiczną w anaerobowym środowisku wody geotermalnej zawierającej CO2. W niniejszym artykule przedstawiono kompleksowe badania korozyjne i mikrobiologiczne w Geotermii Mazowieckiej S.A. Badania mikrobiologiczne wykazały obecnoś bakterii redukujących siarczany (SRB) w osadach ko rozyjnych i mineralnych. Identyfikację bakterii przeprowadzono techniką reakcji amplifikacji PCR fragmentu genu 16S rRNA i stwierdzono występowanie: Desulfovibrio – Desulfomicrobium, Desulfobacter oraz Desulfotomaculum. Obecność tych bakterii jest przyczyną tworzenia warstwy produktów korozji zbudowanej w głównej mierze z amorficznego siarczku żelaza. Woltamperometryczne i impedancyjne pomiary elektrochemiczne pro- wadzone w laboratorium oraz w stacji korozyjnej Geotermii pozwoliły na przedstawienie wpływu obecności bakterii SRB na mechanizm korozji stali węglowej i stali stopowej. Stacja prowadzi monitorowanie i akwizycję danych fizykochemicznych i korozyjnych z możliwością zarządzania z poziomu centrum dyspozycyjnego Geotermii Mazowieckiej S.A.
EN
One of the important issues that determine the operating costs of a geothermal plant is the corrosion of casing, geothermal installations, fittings and deposit colmatation. These phenomena are connected with microbially induced corrosion in anaerobic environment of geothermal water containing CO2. The paper presents a com- prehensive study of corrosion and microbiological corrosion in the Geotermia Mazowiecka plant. Microbiological investigations showed the presence of sulphate-reducing bacteria (SRB) in mineral and corrosion deposits. Identification of the bacteria was performed by PCR amplification of the 16S rRNA gene and the following bacteria have been identified: Desulfovibrio – Desulfomicrobium, Desulfobacter and Desulfotomaculum. The presence of these bacteria is the cause of the formation of a corrosion products layer containing mainly amorphous iron sulfide. Voltammetric and impedance measurements conducted in the laboratory and in the corrosion station at Geotermia Mazowiecka S.A. allowed the influence of SRB on the corrosion mechanism of carbon and alloyed steel to be studied. The station is able to monitor the corrosion and acquisition of physico-chemical data to managed from the Geotermia Mazowiecka S.A. dispatch centre level.
4
Content available remote Wpływ wielkości ziarna na odporność korozyjną stopu aluminium 7475
PL
W pracy przedstawiono wyniki badań odporności na korozję wżerową stopu aluminium 7475, o różnej wielkości ziarna i różnych wydzieleniach, w roztworze chlorku sodu o stężeniu 0,1 M. Badania potencjodynamiczne wykazały, że próbka o strukturze nanokrystalicznej charakteryzuje się niższym potencjałem korozyjnym i niższym prądem korozyjnym niż próbka o mikrometrycznej wielkości ziarna. We wszystkich próbkach zaobserwowano korozję galwaniczną związaną z obecnością dużych cząstek faz międzymetalicznych. Ponadto w próbce o strukturze mikrometrycznej zaobserwowano korozję międzykrystaliczną.
EN
In this study, the corrosion resistance of 7475 aluminium alloy with nano- and micrograin size and various precipitates was investigated in 0.1M NaCl. The potentiodynamic polarization measurements showed that nanocrystalline samples have a lower corrosion potential and lower corrosion current compared to microcrystalline one. The observations of surface morphology revealed the galvanic corrosion related to the presence of intermetallic particles. For microcrystalline sample, the intergranular corrosion attack was observed.
5
Content available remote Wpływ rozdrobnienia ziarna na odporność korozyjną niklu 200
PL
Rozdrobnienie ziarna jest jedną z efektywnych metod kształtowania właściwości materiałów. Zmniejszenie rozmiarów ziaren przyczynia się między innymi do wzrostu wytrzymałości i zwiększenia reaktywności. Publikacje na temat odporności korozyjnej materiałów o małej wielkości ziaren przedstawiają odmienne wnioski - niekiedy korozja zachodzi szybciej, niekiedy wolniej. W niniejszym artykule przedstawiono wyniki badań prowadzonych na niklu 200 po procesach wyciskania hydrostatycznego. Scharakteryzowano mikrostrukturę, wykonano pomiary mikrotwardości oraz zbadano odporność korozyjną. Wykazano, że metoda wyciskania hydrostatycznego umożliwia otrzymanie ultra-drobnoziarnistego niklu, czemu towarzyszy znaczny wzrost mikrotwardości. Badania odporności korozyjnej wykazały, że rozdrobnienie ziarna wpływa niekorzystnie na odporność korozyjną niklu.
EN
Grain refinement is effective method of strengthening of metals. Reduction of grain size increases strength and reactivity. Publications on the corrosion resistance of fine grained metals differ in conclusions - sometimes corrosion proceeds faster, sometimes slower. This paper presents the results of research carried out on Nickel 200 after hydrostatic extrusion. The microstructure, microhardness and corrosion resistance were examined of the samples subjected to this process. It was found that the hydrostatic extrusion results in ultrafine grained nickel structure and is accompanied by a signifi -cant increase in microhardness. The study also shows that the grain refinement has a negative influence on the corrosion resistance of nickel.
PL
Celem przeprowadzonych badań było określenie wpływu rozdrobnienia ziarna na odporność na korozję w sztucznym płynie ustrojowym (SBF) komercyjnego tytanu Grade 2. Badaniom podano tytan w stanie wyjściowym o strukturze mikrometrycznej (μ-Ti) i po procesie hydroekstruzji o strukturze nanometrycznej (n-Ti) stosując polaryzację potencjodynamiczną, elektrochemiczną spektroskopię impedancyjną (EIS) oraz analizując zmiany potencjału korozyjnego w czasie. Na podstawie otrzymanych wyników stwierdzono, że n-Ti ma wyższy potencjał korozyjny niż jego grubokrystaliczny odpowiednik. Przebiegi obu krzywych polaryzacyjnych są podobne, a istotne różnice występują powyżej 1200 mVSCE. Badania impedancyjne wskazują, że warstwa pasywna wytworzona na n-Ti jest mniej zwarta i bardziej porowata.
EN
Nanocrytalline titanium (n-Ti) produced by hydroextrusion process was evaluated in terms of corrosion resistance in simulated body fluid (SBF) using variation of corrosion potential, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The results obtained revealed higher corrosion potential of n-Ti and similar polarization behavior to that of μ-Ti. The EIS results indicate that the passive film formed on n-Ti is less compact and more porous.
first rewind previous Strona / 1 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.