Interaction of Titanium with Ceramic Molds in the Conditions of Electron Beam Casting Technology

Kaliuzhnyi P., Voron M., Mykhanian O., Tymoshenko A., Neima O., Iangol O.

Archives of Foundry Engineering

2021

Vol. 21, iss. 3

27--32

For the manufacture of near net shape complex titanium products, it is necessary to use investment casting process. Melting of titanium is promising to carry out by electron beam casting technology, which allows for specific processing of the melt, and accordingly control the structure and properties of castings of titanium alloys. However, the casting of titanium in ceramic molds is usually accompanied by a reaction of the melt with the mold. In this regard, the aim of the work was to study the interaction of titanium melt with ceramics of shell molds in the conditions of electron beam casting technology. Ceramic molds were made by using the following refractory materials – fused corundum Al2O3, zircon ZrSiO4 and yttria-stabilized zirconium oxide ZrO2, and ethyl silicate as a binder. Melting and casting of CP titanium was performed in an electron beam foundry. Samples were made from the obtained castings and electron microscopic metallography was performed. The presence and morphology of the altered structure, on the sample surface, were evaluated and the degree and nature of their interaction were determined. It was found that the molds with face layers of zirconium oxide (Z1) and zircon (ZS1) and backup layers of corundum showed the smallest interaction with the titanium melt. Corundum interacts with titanium to form a non-continuous reaction layer with thickness of 400-500 μm. For shell molds with face and backup layers of zircon on the surface of the castings, a reaction layer with thickness of 500-600 μm is formed. In addition, zirconium-silicon eutectic was detected in these layers.

Influence of Sand Fluidization on Structure and Properties of Aluminum Lost Foam Casting

Kaliuzhnyi P.

Archives of Foundry Engineering

2020

Vol. 20, iss. 1

122--126

The article presents investigation results of the effect of sand fluidization on the structure and mechanical properties of AlSi9 aluminum alloy. Castings were made by lost foam casting process with sand fluidization in mold at the stages of their solidification and cooling. Sand fluidization was achieved by blowing sand bed with compressed air in a foundry container. The metallographic study was carrying out on samples cut from different sections of the castings. Mechanical properties were determined on specimens made from cast samples. Microstructural analysis showed that sand fluidization increases the cooling rate, as a result, the main microstructural components of the alloy – SDAS, eutectic silicon and needles of the rich-iron phase – decrease. Moreover, in different sections of the casting structure is more uniform. With an increasing the air flow rate, a greater refinement of the structure is observed. Through the use of sand fluidization, the mechanical properties of LFC aluminum alloys increase to the level of gravity die castings.