Investigation of properties of Cu-Al explosively welded bimetals

Lokaj Ján, Sahul Miroslav, Sahul Martin, Nesvadba Petr

Materiały Wysokoenergetyczne

2019

T. 11(2)

31--37

Explosion welding of cooper C10200 to AW 5083 aluminium alloy was performed. The C10200 was proposed as a flyer plate. A parallel setup was used during explosive welding. Bimetals were characterized by regular wavy interface. The intermetallic compound (IMC) layer was observed at the interface of bimetals after 12 month, however, no annealing was performed. EDX analyses revealed that the interface layer consists of the intermetallic compound CuAl. Microhardness at the interface increased due to the presence of the IMC and work hardening as well.

Przedstawiono wyniki zgrzewania wybuchowego miedzi C10200 ze stopem aluminiowym AW 5083. Płytka wykonana z miedzi C10200 była elementem napędzanym. Zgrzewanie wybuchowe prowadzono równolegle na dwóch stanowiskach. Otrzymane bimetale charakteryzowały się regularną falistą powierzchnią łączenia. Badania warstwy związku międzymetalicznego, w obszarze połączenia bimetalicznego, przeprowadzono po upływie 12 miesięcy, jednakże bez wyżarzania. Analiza EDX wykazała, że warstwa łącząca składa się z związku międzymetalicznego CuAl. Mikrotwardość w obszarze łączenie wzrasta zarówno w wyniku obecności związku międzymetalicznego, jak i przeprowadzonego zgrzewania.