Content available Assessment of the surface conditions of gas-lubricated face-seal sealing rings
Gacek J., Norymberczyk Ł., Płonka S.
Tribologia
|
2017
|
nr 5
11--21
EN
The paper presents a study of surface condition of stationary and rotary rings of a gas-lubricated face seal before and after 25 hours of operation on a test bench, with 75 cycles of start-ups and stops of the drive. For evaluation of surface conditions, flatness deviation and a selected 2D and 3D roughness parameters were measured. Profiles of the roughness, material ratio curves, topography, and surface maps in colour before and after 25 hours of operations were presented. It has been found that wear of the end faces of the saling rings differs between sintered silicon carbide and carbon graphite. In the case of the stationary ring made of sintered silicon carbide with a hardness of 3000 HV, there is a slight increase in values of almost all (except Sp) measured 3D amplitude parameters: Sa, Sq, Sv, St. In the case of the rotary ring made of carbon graphite with hardness of about 115 HR a noticeable reduction in values of these parameters was found. Changes In 2D and 3D roughness parameters of end faces of the stationary and rotary rings allow confirming the al most contact-free character of the face seal operation.
PL
W artykule przedstawiono badania stanu powierzchni pierścieni stacjonarnego i obrotowego uszczelnienia czołowego smarowanego gazem przed i po 25 godzinach pracy na stanowisku badawczym dla 75 rozruchów i zatrzymań napędu. Do oceny powierzchni pierścieni uszczelniających wykonano pomiary odchyłki płaskości i wybranych parametrów chropowatości 2D i 3D. Zamieszczono profile chropowatości i krzywe udziału materiałowego oraz topografię i mapę barwną powierzchni czołowej przed i po 25 godzinach pracy. Stwierdzono, że zużycie powierzchni czołowych pierścieni przebiega w odmienny sposób: w przypadku pierścienia stacjonarnego ze spiekanego węglika krzemu o twardości ok. 3000 HV następuje nieznaczny wzrost wartości prawie wszystkich zmierzonych parametrów amplitudowych (z wyjątkiem parametru Sp) chropowatości powierzchni 3D, takich jak Sa, Sq, Sv, St, zaś w przypadku pierścienia obrotowego z kompozytu węglowo grafitowego o twardości ok. 115 HR zauważalne ich zmniejszenie. Zmiany wartości parametrów chropowatości 2D i 3D powierzchni czołowej pierścieni stacjonarnego i obrotowego pozwalają na stwierdzenie prawie bezkontaktowego charakteru pracy uszczelnienia.
2
Content available Wpływ wybranych parametrów ablacji laserowej na wydajność obróbki oraz chropowatość powierzchni spiekanego węglika krzemu
Norymberczyk Ł.
Inżynieria Maszyn
|
2017
|
R. 22, z. 1
65--75
PL
W pracy przedstawiono badania wpływu mocy, czasu trwania oraz częstotliwości impulsów lasera ablacyjnego na wydajność obróbki i chropowatość powierzchni spiekanego węglika krzemu. Wydajność obróbki odniesiono do jednego cyklu obróbkowego, zaś do oceny chropowatości przyjęto średnią arytmetyczną rzędnych profilu Ra oraz największą wysokość profilu chropowatości Rz. Stosując plan Hartleya wyznaczono funkcje obiektu badań. Stwierdzono, że największy wpływ na przyjęte kryteria oceny ma czas trwania impulsu lasera, natomiast mniejszy jest wpływ mocy oraz częstotliwości impulsów lasera.
EN
The paper presents the study of influence of power, pulse width and frequency of laser ablation process on the machining efficiency and surface roughness of sintered silicon carbide surface. The machining efficiency was referred to one machining cycle and the arithmetic mean of the ordinates Ra and the highest roughness profile Rz were used to evaluate the roughness. Using Hartley's plan, the mathematical approximation of the model was investigated. It has been found that the maximum influence on considered parameters has the width of the laser pulse.
3
Content available remote Wpływ wybranych parametrów docierania na jakość powierzchni i wydajność obróbki pierścieni z węglika krzemu
Norymberczyk Ł., Płonka S.
Mechanik
|
2016
|
R. 89, nr 8-9
1048--1049
PL
Przedstawiono badania wpływu nacisku jednostkowego i czasu docierania na jakość powierzchni i wydajność obróbki pierścieni wykonanych ze spiekanego węglika krzemu. Obróbkę przeprowadzono na docierarce jednotarczowej z kompozytowym docierakiem i zawiesiną ze ścierniwem diamentowym, przy stałej prędkości obrotowej. Jakość powierzchni pierścieni określono przez pomiary wybranych parametrów chropowatości oraz płaskość powierzchni.
EN
The paper presents the influence of pressure and time of lapping on a surface quality and material removal rate of sintered silicon carbide rings. The machining was performed on a single side lapping machine with composite lapping plate and diamond slurry at constant rotational speed. The surface quality of the rings was determined through measurement of selected roughness parameters and surface flatness.
4
Content available Determination of a face seal’s operational parameters on test bench
Gacek J., Norymberczyk Ł., Płonka S.
Measurement Automation Monitoring
|
2015
|
Vol. 61, No. 12
555--560
EN
The paper presents a method for determination of static characteristics of a gas lubricated face seal on the basis of experiment performed on the test bench. It has been developed a mathematical model QN=f(tg, pg, n) depicting effect of temperature of the gas tg, pressure of the gas pg and rotational speed of the shaft n on flow rate value of the gas QN. This dependency was used to determine pressure of the gas required for a selected operational parameters of the machine. To asses correctness of functioning of the seal it has been performed measurements of a selected 3D roughness parameters of the sealing rings. Slight changes in values of the 3D surface roughness of stationary and rotating rings before and after 25 working hours allow for conclusion about nearly contactless character of operation of the seal.
5
Content available remote Ocena uszczelnień gazodynamicznych sprężarki amoniaku po 9-letniej eksploatacji w Zakładach Azotowych "PUŁAWY" SA
Urbański J., Lasek J., Norymberczyk Ł.
Pompy, Pompownie
|
2011
|
nr 2 (141)
61-63
PL
Omówienie konstrukcji i wyników przeglądu uszczelnienia wału sprężarki o obrotach 10500, zastosowanego celem uniknięcia wprowadzania oleju do czynnika roboczego.
EN
Description of the design applied in order to avoid penetration of oil into the working medium and results of inspection of the compressor shaft seal working at 10,500 rpm.