Wyniki wyszukiwania - BazTech

1

Hygric properties of HPC exposed to salt attack

Mňahončáková E., Tesárek P., Černý R.

Roczniki Inżynierii Budowlanej

|

2007

|

z. 7

57--60

EN

The progressive building materials development improves their quality and utility value. In order to achieve better material properties, besides the new technologies also specific admixtures are employed. The accurate admixtures dosage and technological conditions observation can improve the material parameters like strength and durability. Most frequently, the mineral admixtures, for example pozzolana, fly ash or flue cinder, are used in concrete production. Fine siliceous materials usually called silica fume belong to relatively newly applied materials improving concrete quality. Despite the gradual shift in the HPC design and application philosophy towards a generally recognized necessity to measure a wider scale of HPC parameters the mechanical properties still remain the far most frequent parameters investigated in the research work being done on HPC. Water and water vapor transport and storage properties of HPC were not yet in the center of interest of most researchers until now although they possess a very high predicative potential concerning the HPC quality. In this paper, basic hygric properties of two types of high performance concrete are measured after salt attack being induced by immersion in 3-M NH4NO3 solution for three months and compared to the properties in reference state.

CS

V článku jsou studovány základní vlhkostní parametry dvou záměsí vysokohodnotných betonů v referenčním stavu a po vystavení působení 3-M roztoku NH4NO3 po dobu tří měsíců. Výsledky experimentů ukazují, že transportní parametry vody i vodní páry jsou u obou studovaných materiálů v důsledku působení NH4NO3 redukovány, což je v dobrém souladu se snížením pórovitosti. Pozorované změny vlhkostních parametrů jsou pravděpodobně způsobeny chemickou reakcí NH4NO3 s cementovou matricí, jejíž produkty způsobují částečné zaplnění pórového prostoru.

2

Monitoring the course of hydration heat development of gypsum

Tesárek P., Tydlitát V., Černý R.

Roczniki Inżynierii Budowlanej

|

2006

|

z. 6

141--144

CS

V článku je studován vliv plastifikačních a hydrofobizačních přísad a vodního součinitele na průběh hydratace energosádry ve srovnání s průběhem naměřeným na referenční energosádře bez přísad. Měření provedená pomocí kalorimetru KC 01 ukazují výskyt β-anhydritu III v sádře, který poněkud zvyšuje naměřená hydratační tepla ve srovnání s tabulkovými hodnotami. Vliv přísad se projevuje pouze v určitém zpomalení hydratační reakce, ale neovlivňuje celkové hydratační teplo. Vliv teploty na průběh hydratace energosádry v rozmezí 1-40°C se ukazuje jako významný a projevuje se přibližně lineární závislostí maxima výkonu na teplotě.

3

Właściwości zaprawy wapiennej z dodatkiem metakaolinitu

Tesárek P., Tydlitát V., Drchalová J., Rovnaniková P., Černý R.

Cement Wapno Beton

|

2005

|

R. 10/72, nr 4

175-182

PL

Oznaczono podstawowe mechaniczne, cieplne i wilgotnościowe własności zapraw wapiennych z dodatkiem metakaolinitu i porównano je z własnościami zwykłej zaprawy wapiennej. Zbadano również wpływ hydrofobizacji na zachowanie się badanej zaprawy wapienno-kaolinitowej w warunkach wilgotnych. Na podstawie przeprowadzonych badań stwierdzono, że badana zaprawa nadaje się do zastosowania przy rekonstrukcjach historycznych budowli. Stwierdzono również, że stosowanie jako dodatku pucolanowego metakaolinitu uzyskiwanego przez prażenie w temperaturach 800 - 900 stopni C jest korzystniejsze, niż metakaolinitu prażonego w niższych temperaturach, a hydrofobizacja badanej zaprawy przy użyciu stearynianu cynku w ilości 0-1% bardzo korzystnie wpływa zwłaszcza na zachowanie się zaprawy w warunkach działania wilgoci.

EN

Basic mechanical, thermal and hydric properties of lime plasters with metakaolin admixture have been determined and compared with the properties of common lime plaster. The effect of hydrophobization on the hydric properties of the studied melakaolin plaster using zinc stearate has been studied as well. On the basis of experiments performed it can be concluded that the analyzed plaster is suitable for an application in reconstruction of historical buildings. It has been stated furthermore that the use - as pozzolana admixture - of metakaolin obtained by burning a kaolin at temperatures of 800°-900°C is preferable to metakaolins burnt at lower temperatures and the hydrophobization of studied plasters using zinc stearate in the amount of 0-1% has an advantageous effect especially upon their mechanical and hydric properties.

4

Właściwości hydrofobowego gipsu z odsiarczania spalin

Tesárek P., Rovnaniková P., Kolisko J., Černý R.

Cement Wapno Beton

|

2005

|

R. 10/72, nr 5

255-264

EN

The measurements of mechanical, hygric and thermal parameters of hardened FGD gypsum modified by the addition of three different hydrophobization substances are performed in the paper and compared to the properties of the reference material without any admixtures. Two of the applied hydrophobization admixtures are found to have a good potential for practical applications because they decrease the apparent moisture diffusivity by about two orders of magnitude. The negative effect of applied hydrophobization admixtures on the mechanical properties of hardened FGD gypsum is clearly evidenced for the short-time measurements only. The measurements of compressive and bending strength after 300 days do not show any significant decrease of these parameters due to the hydrophobization. The effect of high water content on both compressive strength and bending strength of all studied materials is found very significant, resulting in a reduction of these parameters down to 50% of the values corresponding to the hygroscopic moisture content.

PL

Zbadano właściwości mechaniczne, cieplne i odporność na wodę stwardniałego gipsu z materiału z odsiarczania spalin, z dodatkiem trzech domieszek hydrofobizujących i porównano z właściwościami materiału bez domieszek. Dwie z zastosowanych domieszek hydrofobizujących posiadają potencjalnie dobre właściwości praktycznego wykorzystania ponieważ zmniejszają pozorną dyfuzyjność wilgoci o około dwa rzędy wielkości. Ujemny wpływ zastosowanych domieszek hydrofobizujących na właściwości mechaniczne stwardniałego gipsu uzyskanego z materiału z odsiarczania spalin został stwierdzony tylko w pomiarach po dwóch dniach. Pomiary wytrzymałości na ściskanie i zginanie przeprowadzone po 300 dniach nie wykazują, znaczącego zmniejszenia tych właściwości pod wpływem hydrofobizacji. Wpływ dużej zawartości wody na oba rodzaje wytrzymałości: na ściskanie i na zginanie wszystkich badanych materiałów jest bardzo duży i powoduje zmniejszenie tej wytrzymałości o około 50% w porównaniu z wilgotnością higroskopijną.