1
Content available remote Physical and technological preconditions of melting-crystallisation temperature stabilisation
Prokhorenko V., Prokhorenko S., Mudry S., Bylica A.
Archives of Materials Science and Engineering
|
2008
|
Vol. 32, nr 1
29-32
EN
Purpose: The precise temperature measurements need the using of temperature reference points - "temperature fixpoints" (TFP). The increase of measuring temperature interval and other reasons require of new TFP with high stability in different working conditions. On that reason the studying of liquid metals and metallic eutectic alloys has been carried out in this work. Design/methodology/approach: For experimental studies the physical properties measurements were used. Findings: Non-reproducibility of temperature fixpoints exist due to some reasons: no accounting the structural - thermodynamic state of melt; mass-heat processes are not enough taken into account. It is fixed, that the temperature fluctuations (and non-stability of crystallization plateau) are of two types: small fluctuations (up to (1-2) mK) are caused by phases (stages) of crystallization process; major fluctuations (at us: ±0,2K) crystallizations are caused convectional streams at the front. Fluctuations can be essentially reduced by approach to requirements of thermodynamic balance, but their complete elimination - is problematic. Research limitations/implications: The main parameters obtained from them are analysed. It is shown that melting-crystallization phase transition is influenced by structural state of melt and cooling condition. Practical implications: The results obtained here can be used in analysis of errors at high-precision temperature measurements and constructing of new temperature measuring and holding systems of high stability. Originality/value: The results of this study can be useful for researches in field of metrology, material science and physics of metals.
2
Content available remote The effect of GTAW processing on the structure and microhardness of C45 Steel
Bylica A., Adamiak S.
Archives of Foundry Engineering
|
2008
|
Vol. 8, iss. 1 spec.
45--48
EN
The work presented test results of surface upgrading of C45 Steel with concentrated heat flux using GTAW method. The surface layer of C45 Steel was remelted with stable speed of 200 mm/min welding head advance and using the intensity of electric arc current form 50 up to 300A and 300 A stable intensity of electric arc current the speed of head advance was changed in the rangę from 200 mm/min up to 800 mm/min. Microscope tests of obtained structure and measures of the hardness of remelted surface layers were conducted. The correlation between the intensity of electric arc current of its the feed rate and material microhardness was derived.
PL
W pracy przedstawiono wyniki badań uszlachetniania powierzchniowego stali C45 skoncentrowanym strumieniem ciepła z zastosowaniem metody GTAW. Dokonano nadtopienia warstwy wierzchniej stali C45 przy stałej szybkości przesuwu głowicy spawalniczej 200 mm/min i zastosowaniu natężenia prądu łuku elektrycznego od 50 do 300A oraz stałym natężeniu prądu luku elektrycznego 300 A zmieniano prędkość przesuwu głowicy od 200 mm/min do 800 mm/min. Przeprowadzono badania mikroskopowe otrzymanej struktury oraz wykonano pomiary twardości nadtopionych warstw. Podano zależność pomiędzy natężeniem prądu łuku elektrycznego i szybkością jego przesuwu a mikrotwardością struktury.
3
Content available remote Microhardness changes of surface layer of HS 6-5-2 steel in the areas overlapping remelting obtained with the use of GTAW method
Bylica A., Dziedzic A.
Archives of Foundry Engineering
|
2008
|
Vol. 8, iss. 3
25-28
EN
The work presents test results of microhardness of surface layer of HS 6-5-2 high-speed steel from areas overlapping remelting. The surface layer of the steel was remelted using the GTAW method. The microhardness was measured using the Vickers method. The work shows that the area, where the heat influence zone of the second remelting overlapping on the first remelting zone is characterizes by the microhardness lower about approx. 200 HV0,065.
4
Content available remote The structure of liquid eutectic as a gowerning factor in crystallization processes
Prokhorenko W., Mudry S., Prokhorenko S., Bylica A., Navotska J.
Archiwum Odlewnictwa
|
2006
|
R. 6, nr 18/2
527--530
EN
The structure of Ga-In-Sn eutectic melt has been studied by means of x-ray diffraction method. The structure factors and pair correlation functions are analyzed. It is shown that inhomogeneous structure exists within some temperature range and can be changed by outside energetic influence.
PL
W pracy przedstawiono wyniki porównawczych badań stukturalnych eutektycznego stopu Ga-In-Sn. Uzyskane wyniki potwierdziły występowanie w tym stopie struktur niehomogenicznych w szerokim zakresie temperatury oraz możliwość zmiany takich struktur przez zewnętrzne oddziaływanie energetyczne.
5
Content available remote Naprężenia własne w stali C45 nadtapianej laserowo
Bylica A., Bochnowski W., Więcek G.
Archiwum Odlewnictwa
|
2006
|
R. 6, nr 19
43-48
PL
W pracy przedstawiono wyniki badań metalograficznych SEM, pomiarów mikrotwardości HV0,1 oraz wyznaczono naprężenia własne w warstwie wierzchniej stali C45 nadtopionej wiązką lasera CO2.
EN
The paper presents the results of laser surface modification on the C45 medium carbon steel. The laser heat treatment has been carried out by CO2 laser beam. Scanning electron microscopes and Vickers hardness tester were used to investigate structure and microhardness of the surface layer. Residual stresses in the laser remelted zone measurement by Waissman - Phillips method. In the microstructure after laser remelting three zone have been observed: remelted zone (of microhardness 480 -610 HV0,1), heat affected zone to solidus temperature (of microhardness 450 -550 HV0,1) and heat affected zone to temperature with range A1 - A3. This surface layer performs different residual stresses: compression (ab. 300 MPa) and tenssion (ab. 150 MPa).
6
Content available remote Mikrostruktura i właściwości stali narzędziowych nadtapianych laserem CO2
Bylica A., Dziedzic A., Bochnowski W., Adamiak T.
Archiwum Odlewnictwa
|
2005
|
R. 5, nr 15
45--52
PL
W pracy przedstawiono wyniki badań mikrostruktury SEM, mikrotwardości, odporności na zużycie tribologiczne stali narzędziowych nadtapianych wiązką lasera. Badano stale narzędziowe - do pracy na zimno: X45NiCrMo4, X100CrMoV5-1, 100MnCrW4 i X155CrVMo12-1, na gorąco X38CrMoV5-1 oraz stal szybkotnącą HS 6-5-2. Po laserowej obróbce przeprowadzono konwencjonalne odpuszczanie. Pokazano, że korzystne jest przeprowadzenie procesu odpuszczania dla stali X100CrMoV5-1, X155CrVMo12-1, X38CrMoV5-1 oraz HS 6-5-2. Zachowanie stosunkowo wysokiej twardości narzędziowych stali stopowych po wysokim odpuszczaniu jest wynikiem wystąpienia efektu twardości wtórnej - wydzielania węglików stopowych koherentnych z osnową martenzytu i przemianą austenitu szczątkowego.
EN
The following types of steels were the object of examinations - cold-work tool steels: X45NiCrMo4, X100CrMoV5-1, 100MnCrW4 and X155CrVMo12-1, hot-work tool steel X38CrMoV5-1, high-speed steel HS 6-5-2. Samples were remelted with laser CO2 and tempered conventionally. The following observations were performed: the metallographic SEM, measurements of micro hardness, abrasion resistance. The laser remelting of tool-grade steels leads to growth of abrasions resistance in comparison to steels subjected to conventional heat treatment. It is beneficial to perform tempering for the following steel types: X100CrMoV5-1, X155CrVMo12-1, X38CrMoV5-1 and HS 6-5-2. The preservation of relatively high hardness of tool-alloy steels after high tempering is the result of secondary hardness - precipitations of alloy carbides coherent with martensite matrix and the transformation of residual austenite.
7
Content available remote Zmiany składu fazowego stali szybkotnących po obróbce laserowej
Bylica A., Bochnowski W., Major B.
Archiwum Odlewnictwa
|
2004
|
R. 4, nr 12
209--216
PL
W pracy przedstawiono wyniki badań rentgenowskiej analizy fazowej stali szybkotnących HS 2-10-1-8, HS 6-5-2, HS 10-2-5-8 po konwencjonalnej i laserowej obróbce cieplnej. Przetopienie warstwy wierzchniej stali wykonano laserem diodowym dużej mocy (HPDL) w atmosferze gazów ochronnych. W badanych stalach ujawniono martenzyt, austenit szczątkowy oraz zależnie od gatunku stali węgliki typu M6C, M2C, MC. Szybka krystalizacja strefy nadtopionej sprzyja powstawaniu węglików pierwotnych typu MC. Wysoki (ok. 60% obj.) udział austenitu szczątkowego w strefie przetopu ulega obniżeniu (do 2% obj.) w wyniku odpuszczania w temperaturze 530oC/ 3x2 godz.
EN
This paper presents results of phase analysis (with using XRD method) of high speed steel HS 2-10-1-8, HS 6-5-2, HS 10-2-5-8 after conventional heat treatment and laser modification. The laser heat treatment has been carried out by high power diode laser (HPDL). Martensitic phase, retained austenite and primary carbide M6C, M2C, MC additional for grade steels in the all examined steels shown. Rapid solidification of laser melting zone favorable solidification primary carbide phase MC type. A high retained austenite portion in melting zone (about 60% vol.) falls after tempering at the temperature 530oC/ 3 times x 2 hours to the 2% vol.
8
Content available remote Wpływ obróbki laserowej na strukturę i właściwości wybranych stali narzędziowych do pracy na zimno
Bylica A., Adamiak S., Dziedzic A.
Archiwum Odlewnictwa
|
2004
|
R. 4, nr 11/1
96--101
PL
W pracy przedstawiono wyniki badań stali narzędziowych do pracy na zimno X45NiCrMo4, X100CrMoVS-1, 100MnCrW4 i X155CrVMo12-1 nadtopionych laserem CO2. Stale narzędziowe do pracy na zimno zajmują szerokie zastosowanie w produkcji narzędzi o wysokiej odporności na ścieranie, zwiększonej ciągliwości czy pracujących pod dużym obciążeniem. W pracy zamieszczono wyniki badań metalograficznych, odporności na ścieranie przeprowadzonych w warunkach tarcia suchego za pomocą testera T-01M typu trzpień - tarcza oraz pomiary mikrotwardości.
EN
This work presents results of changes microstructure and some properties cold-work tool steel X100CrMoVS-1, 100MnCrW4, X45NiCrMo4 and X155CrVMo12-1 remelted with using laser. Showed examine the steels of SEM microscopy, abrasion resistance with using pin-on disc tester, and measurements microhardness.
9
Content available remote Wpływ nadtopienia laserowego na mikrostrukturę i wybrane właściwości stali narzędziowych X38CrMoV5-1 i HS 6-5-2
Bylica A., Dziedzic A., Adamiak S.
Archiwum Odlewnictwa
|
2004
|
R. 4, nr 11/1
86--95
PL
W pracy przedstawiono wpływ nadtopienia laserowego na mikrostrukturę i wybrane właściwości stali narzędziowej do pracy na gorąco X38CrMoV5-I i stali szybkotnącej HS 6-5-2 stosowanej na wiertła spiralne, narzędzia do nacinania gwintów, segmenty do pił tarczowych, przeciągacze. Zamieszczono wyniki badań metalograficznych SEM, pomiarów mikrotwardości oraz zużycia tribologicznego w warunkach tarcia technicznie suchego na testerze typu trzpień-tarcza T-01M.
EN
Laser beam treatment (with parameters how in work) of high speed steel HS 6-5-2 and hot-work tool steel X38CrMoV5-1 remelting surface layer causes. Remelted zone characterize increase of microhardness and abrasion resistance. Unfavourable occurrence is in remelted zone of X38CrMoVS-1 steel of phenomenon of cracks. This is result of thermal stresses during laser treatment appearing.
10
Content available remote Structure of a melt, thermal and ultrasonic properties during gallium alloys crystallization
Prokhorenko S., Prokhorenko W., Mudry S., Bylica A., Navrotska J.
Archiwum Odlewnictwa
|
2004
|
R. 4, nr 11/2
123--130
EN
The temperature and concentration dependences of the structure parameters of Ga-In &Ga-Sn melts have been studied. The configurational component of the entropies of melts have been calculated using the results of x-ray research and hard sphere approach. Acoustical emission and heat effects accompanying the processes of crystallization have been explored. The presence of correlation dependence between the structural - thermodynamic condition of the melt and the freezing point is found.
XX
Przeanalizowana zależność temperaturowa i koncentracyjna parametrów struktury stopów Ga-In oraz Ga-Sn w stanie ciekłym. Z wykorzystaniem wyników rentgenografii a także w przybliżeniu modeli twardych sfer obliczona entropia konfiguracyjna cieczy. Zbadano emisję akustyczną oraz właściwości cieplne towarzyszące procesom krystalizacji. Ustalono korelację między strukturalno-termodynamicznym stanem cieczy oraz mechanizmem krystalizacji.
11
Content available remote Zmiany struktury w obszarze nakładających się ścieżek laserowych w stali HS 6-5-2
Bylica A., Dziedzic A.
Archiwum Odlewnictwa
|
2003
|
R. 3, nr 7
223-228
PL
W pracy przedstawiono zmiany mikrostruktury i mikrotwardości stali szybkotnącej HS 6-5-2 w obszarze nakładających się ścieżek laserowych. Badano wpływ nakładania się ścieżek laserowych na własności warstwy wierzchniej stali. Przy zachowaniu parametrów obróbki jak w pracy, w obszarach nakładających się nadtopień nie stwierdzono wyraźnych zmian mikrostruktury i mikrotwardości w porównaniu do obszarów pojedynczych nadtopień.
EN
In result of laser beam treatment of surface layer HS 6-5-2 steel was obtained in remelted zone strong refinement of structure. It is caused high cooling rate of liquid metal in remelted zone about [...]. In the area of the laser tracks overlapping didn't confirm visible changes of microstructure and microhardnesses in comparison with area, where tracks didn't overlap.
12
Content available remote Wpływ obróbki laserowej na kształtowanie warstwy wierzchniej żeliwa sferoidalnego
Bylica A., Adamiak S.
Archiwum Odlewnictwa
|
2003
|
R. 3, nr 7
229-235
PL
W pracy przedstawiono wyniki badań dotyczące wpływu obróbki laserowej na strukturę i właściwości żeliwa sferoidalnego: GJS 400-15, GJS 500-07 i GJS 600-03. Przedstawiono procesy zachodzące podczas krystalizacji żeliwa po laserowym przetopieniu oraz ich wpływ na strukturę warstwy wierzchniej. Pomimo uzyskania po hartowaniu laserowym znacznego wzrostu twardości struktury nie uzyskano spodziewanej odporności na zużycie ścierane. Wzrost współczynnika tarcia na styku próbka - przeciwpróbka powodował wzrost temperatury powierzchni ścieranej oraz zmniejszenie odporności na zużycie ścierne.
EN
This work present results microstructure and properties spheroidal graphite iron (GJS 400-15, GJS 500-07 i GJS 600-03) after laser treatment examined. Process solidification influence, to the microstructure in zone remelted was show. Increase coefficient friction, caused to increase temperature and decrease abrasion resistance.
13
Content available remote Naprężenia własne w hartowanych laserowo stalach SK5MC, SW7M, 45
Bylica A., Adamiak S., Bochnowski W., Dziedzic A.
Archiwum Odlewnictwa
|
2003
|
R. 3, nr 8
33--44
PL
Badano rozkład naprężeń własnych w warstwie przetopionej laserem stali SK5MC, SW7M, 45 - metodą Weissmana–Philipsa. Badano również wpływ odpuszczania po hartowaniu laserowym oraz wpływ wielkości przekroju próbek hartowanych laserowo na rozkład i wielkość naprężeń własnych. Badania naprężeń własnych w warstwie przetopionej laserem stali ujawniły występowanie naprężeń ściskających. Ich wartość malała wraz ze wzrostem odległości od powierzchni przetopu. Naprężenia własne zwiększają się bardzo wyraźnie ze wzrostem przekroju próbki poddanej laserowemu hartowaniu. Odpuszczanie wpływa w nieznacznym stopniu na wartość naprężeń w warstwie wierzchniej - zmniejsza je o ok. 30 MPa do 50 MPa, w zależności od temperatury odpuszczania.
EN
This paper presents results of examined residual stress in high speed steels: HS 7-4-2-5, HS 6-5-2 and carbon steel C45 were used Weissman–Philips method. Temperature tempering and dimension cross-section of materials after laser hardened influence to distribution and value residual stresses examined too. In laser hardened lager measurement press residual stresses. Value stresses decrease with disbince from the surface treated. It shows that, as growth area cross-section very increase value residual stresses. Tempering steels after laser treated led to residual stresses, in crease value about 30 to 50 MPa, related to temperature tempering.
14
Content available remote Laserowe umacnianie stali niestopowych
Bylica A., Adamiak S.
Archiwum Odlewnictwa
|
2002
|
R. 2, nr 6
43-54
PL
W pracy przedstawiono badania wpływu parametrów obróbki laserowej oraz konwencjonalnej po hartowaniu laserowym na strukturę, mikrotwardość i odporność tribologiczną stali 15, 45 i N9E. Przetopienie stali wiązką laserową zmienia w istotny sposób własności warstwy wierzchniej. W stali 15 otrzymano martenzyt listwowy natomiast w stali 45 i N9E martenzyt płytkowy i austenit szczątkowy. Mikrotwardość po hartowaniu laserowym wynosiła do 1000 HV0,065 natomiast odporność na zużycie ścierne była 6 razy większa niż próbek niehartowanych.
EN
The paper presents the result of the effect of laser-beam and conventional treatment parameters on the structure, microhardness and abrasion resistance of the steel 15, 45 and N9E. Remelting of steel with laser beam changes significantly the properties of surface layers. In steel 15 had lamellar martensite and in steel 45 and N9E plate martensite and residual austenite. Following laser hardening, microhardness was max. 1000 HV0,065. Abrasion resistance was 6 times greater than in unhardened samples.
15
Content available remote Determination of structural and thermal-physics requirements of stabilization of an equilibrium crystallization of a eutectic alloys
Prokhorenko S., Stadnyk B., Bylica A.
Archiwum Odlewnictwa
|
2002
|
R. 2, nr 6
189-194
EN
Some considerations that have been prepared by the authors as a preliminary basis for creation of the national temperature reference points using metal alloys of eutectic concentration as a working element are presented. The substantiation of the possibility of eutectics application done with the account of modern achievements of physics of metals is given. For addilional control of melting / crystallization cycles parameters invariance the Procedure of Spectrum Comparison of the parameters of Acoustic Emission from the alloy is suggested to be used.
PL
W artykule podano uzasadnienie z pozycji ostatnich osiągnięć fizyki metali ciekłych możliwości wykorzystania eutektyk w jakości dodatkowych punktów odniesienia skali temperaturowej ITS-90. Jako metodę uzupełniającej kontroli zaproponowano użyć metodę porównywania parametrów spektrów Emisji Akustycznej, szczególnie parametru katastroficzności Kp.
16
Content available remote Hartowanie laserowe żeliwa
Bylica A., Adamiak S.
Archiwum Odlewnictwa
|
2001
|
R. 1, nr 1
140--148
PL
W pracy przedstawiono zmiany struktury i właściwości żeliw po hartowaniu laserowym. W mikrostrukturze strefy przetopionej występowały kryształy kolumnowe i dendrytyczne o twardości 700 - 900 HV0,065 zawierające martenzyt, austenit (szczątkowy) oraz cementyt. W strefie przejściowej żeliwa szarego o strukturze martenzytycznej wokół nierozpuszczonego grafitu obserwowano zabielenie struktury. Mikrotwardość po hartowaniu laserowym wynosiła około 1000 HV0,065 i była o 20–40% większa niż po hartowaniu objętościowym. Odporność na zużycie ścierne była 3-4 razy większa niż próbek niehartowanych oraz o 15-20% większa od żeliw hartowanych objętościowo.
EN
This research analyses changes in structure and characteristics of cast irons after laser hardening. In the microstructure of remelted zone the following could be found: columnad and dendritic crystals with hardness of 700-900 HV0,065 containing marten-site, residual austenite and cementite. In transition zone of grey cast iron with martensite structure whitening of structure could be observed around undissolved graphite. Following laser hardening, microhardness was about 1000 HV0,065, which was 20-40% greater as compared to volumetric hardening. Wear resistance was 3-4 times greater than in unhardened samples and 15-20% greater as compared to cast irons samples treated by volumetric hardening.
17
Content available remote Zmiana własności stali szybkotnącej SK5M po obróbce laserowej
Bylica A., Bochnowski W.
Krzepnięcie Metali i Stopów
|
2000
|
R. 2, nr 42
285--290
PL
Laserowe nagrzewanie , przetopienie lub stopowanie powierzchni metali prowadzi do uformowania warstwy wierzchniej o pożądanych własnościach użytkowych. Poprzez dobór technologii obróbki laserowej można modyfikować warstwę wierzchnią w celu podwyższenia jej twardości, odporności na ścieranie, żaroodporności, odporności na korozję, trwałości zmęczeniowej stykowej a także rezystywności. [...]
18
Content available remote Wpływ parametrów obróbki laserowej i konwencjonalnej na strukturę i własności stali szybkotnącej SW7M
Bylica A., Dziedzic A.
Krzepnięcie Metali i Stopów
|
2000
|
R. 2, nr 42
275--283
PL
Stale szybkotnące są dominującym materiałem stosowanym na narzędzia (frezy, wiertła, przeciągacze) do obróbki materiałów. Zapotrzebowanie na nowe, bardziej wytrzymałe i trwalsze narzędzia spowodowało, że zaczęto poszukiwać nowych sposobów obróbki cieplnej. Jednym ze sposobów otrzymywania struktur bardziej przesyconych o większym niż w obróbce konwencjonalnej rozdrobnieniu ziarna, które powstają w wyniku działania na materiał dużych energii w krótkim czasie jest obróbka laserowa, ponadto niski koszt, możliwość pełnej automatyzacji oraz wysoka dokładność przyczyniły się do wykorzystywania laserów do celów przemysłowych. [...]
19
Content available remote Teplovaâ, zvukovaâ i magnitnaâ obrabotka rasplavov s cel'û ulučšeniâ kačestva lit'â
Prohorenko V., Bylica A., Prohorenko S.
Krzepnięcie Metali i Stopów
|
2000
|
R. 2, nr 43
479--485
20
Content available remote Wpływ węgla na strukturę i właściwości stopów Fe-C hartowanych laserowo
Bylica A., Adamiak S.
Krzepnięcie Metali i Stopów
|
1998
|
nr 36
243--249
PL
Szczególnie ważnym zagadnieniem w procesie laserowej obróbki cieplnej jest właściwy dobór materiału oraz prawidłowych parametrów obróbki laserowej zapewniających uzyskanie najkorzystniejszych właściwości technologicznych i eksploatacyjnych dla określonych wyrobów. Uwarunkowane jest to znajomością rozkładu pola temperaturowego, szybkości nagrzewania i chłodzenia, czasu austenityzacji oraz kinetyki przemian zachodzących podczas laserowej obróbki cieplnej. [...]
first rewind previous Strona / 2 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.