Peculiarities of simulation of the additive process of forming of 3D products from steel 09G2S

Grigorenko G. M., Kostin W. A., Mossokovskaya I. A.

Przegląd Spawalnictwa

|

2017

|

R. 89, nr 9

42--48

EN

The results of modeling of thermal fields, stresses, deformations and displacements in formation of an additive structure of 09G2S steel on a substrate are presented. An interdisciplinary research computational package COMSOL Multiphysics was used for computer modeling. Effect of the temperature on physicochemical parameters of steel was taken into account in the work. The results for modeling were obtained using Gleeble 3800 a complex for simulation of thermal deformation state of welding thermal cycle. Some physical-thermal properties of 09G2S steel were calculated using JmatPro 6.0 software package. Carried investigation showed that the highest level of residual stresses and deformations in additive deposition of 09G2S steel layers on the substrate is reached at the boundary of the first layer and substrate and makes 280–320 MPa. Stresses between the layers of deposited metal are significantly lower (to 50 MPa). It is determined that the increase of the number of deposited layers provokes nonlinear rise of a level of stress at the additive layer/substrate boundary and does not depend on the number of deposited layers in time. In additive manufacturing process, preheating to at least 300÷320 °C temperature should be used to prevent noticeable deformation of the substrate. Developed software can be used for mathematical modeling of additive process of formation of steel, titanium and aluminum alloys structures.

PL

Przedstawiono wyniki modelowania pól termicznych, naprężeń, odkształceń i przemieszczeń przy formowaniu konstrukcji addytywnej ze stali 09G2S na podkładce. Dla dokonanego modelowania komputerowego wykorzystano pakiet dla międzydyscyplinarnych badań COMSOL Multiphysics. W pracy uwzględniono wpływ temperatury na parametry fizykochemiczne stali. Wyniki dla modelowania otrzymano z wykorzystaniem kompleksu imitowania stanu termo-odkształceniowego cyklu termicznego spawania Gleeble 3800. Właściwości fizyko-termiczne stali 09G2S obliczono za pomocą pakietu JmatPro 6.0. Przeprowadzone badania świadczą, że przy nanoszeniu addytywnym warstw stali 09G2S na podkład największy poziom naprężeń resztkowych i odkształceń osiąga się na granicy pierwszej warstwy i podkładki i stanowi 280÷320 MPa. Naprężenia miedzy warstwami metalu napawanego są znacznie niższe (do 50 MPa). Ustalono, że ze wzrostem ilości warstw naniesionych poziom naprężeń na granice warstwa addytywna/podkład wzrasta nieliniowo i z czasem nie zależy od ilości warstw nanoszonych. Przy procesie addytywnym dla zapobiegania odkształcenia podkładu należy stosować poprzednie nagrzewanie do temperatur 300÷320 °С. Te programy mogą być stosowane dla modelowania matematycznego procesu formowania konstrukcji ze stali i stopów aluminiowych.

2

Effect of nanoparticles on the structure and properties of welds made of high strength low-alloy steels

Grigorenko G. M., Kostin W. A., Gołowko W. W., Żukow W. W.

Biuletyn Instytutu Spawalnictwa w Gliwicach

|

2016

|

Vol. 60, No. 6

64--69

PL

Przedstawiono wyniki badań struktury metalu spoin wysokowytrzymałej niskostopowej stali 14HGNDC, do roztopionego materiału której wprowadzano nanoproszkowe cząstki różnych związków trudno topliwych - tlenków, węglików i azotków (TiC, TiN, SiC, VC, NbC, TiO2, Al2O3, MgO, ZrO2). Przeprowadzone badania wykazały efektywność zastosowania nanotlenków tytanu TiO2 i cyrkonu ZrO2, co pozwoliło zapewnić wysokie wartości własności mechanicznych metalu spoin (Rm -708 MPa i 621 MPa, KCV-20- 60 J/cm2 i 72,9 J/cm2, a - 21 i 19%). Zastosowanie symulatora cykli cieplnych Gleeble 3800 pozwoliło na ustalenie zależności między temperaturowymi zakresami przemian, ilością składników strukturalnych i typem modyfikujących nanocząstek.

EN

The article presents test results concerning the structure of welds made of high strength low-alloy steel 14HGNDC which, in the molten state, was provided with nanoparticles of various refractory compounds including oxides, carbides and nitrides (TiC, TiN, SiC, VC, NbC, TiO2, Al2O3, MgO, ZrO2). The performed tests revealed the effective use of the nano-oxides of titanium (TiO2) and zirconium (ZrO2) enabling the obtainment of high mechanical properties of the weld metal Rm -708 MPa and 621 MPa, KCV-20 - 60 J/cm2 and 72,9 J/cm2, a - 21 and 19%). The use of a Gleeble 3800 welding cycle simulator made it possible to determine the dependence between temperature ranges of transformations, amount of structural constituents and types of modifying nanoparticles.

3

Osobliwości przekształceń strukturalnych w strefie wpływu ciepła złączy spawanych MAG stali wysokowytrzymałej WELDOX 1300

Grigorenko G. M., Kostin W.A., Poznjakow W. D., Żdanow S.L., Żukow W.W.

Przegląd Spawalnictwa

|

2015

|

R. 87, nr 6

42--46

PL

W artykule przedstawiono wyniki badań właściwości struktury w metalu strefy wpływu ciepła stali konstrukcyjnej wysokowytrzymałej typu WELDOX 1300 wykonane metodą MAG. Opracowano wykresy CTPC-s, ustalono i opisano przyczyny obniżenia właściwości mechanicznych połączeń spawanych stali WELDOX 1300.

EN

The article studied the features of the formation of structure in the HAZ metal high-strength structural steel WELDOX 1300, made by MAG welding, built thermokinetic diagram decomposition of austenite (CCT diagram) and installed reason for the decline of the mechanical properties of welded joints in steel WELDOX 1300.

4

Spawalność stali i kryteria jej oceny

Grigorenko G. M., Kostin W. A.

Przegląd Spawalnictwa

|

2013

|

R. 85, nr 7

11--17

PL

W artykule przeprowadzono analizę terminu spawalność, dokonano doboru metod oceny spawalności stali, przeanalizowano rozumienie i traktowanie przez różnych badaczy terminu spawalność i wskazano opinię autorów o możliwej liczbowej ocenie spawalności. Uzasadniono wzajemny związek spawalności wykorzystywanych materiałów inżynierskich z technologią i konstrukcją. Ustalono następujące poziomy spawalności: dostateczna (wszystkie eksploatacyjne wymagania spełnione); niedostateczna (chociażby 1 wymóg niespełniony); dobra; zadowalająca (konieczność zmiany warunków spawania); ograniczona (konieczność zmiany sposobu spawania); zła (nie ma możliwości osiągnięcia pozytywnego wyniku).

EN

It has been analized the term of weldiability, selected the methods of steels weldiability estimation, compared the understanding and applications by different investigators the term of weldiability, presented the authors opinion about numerical estimation of weldiability. Grounded the mutual connnection of using materials weldability with technology and construction. It has been established the weldability levels: acceptable (all service requirements has satisfied); non acceptable (even 1 service requirements has not satisfied); good; compatible (to change the welding circumstances); limited (to change the welding methods); bad (no possibility to achieve the positive results).