Wyniki wyszukiwania - BazTech

1

Theoretical and experimental analysis of the evolution of the pearlitic structure of wires drawn with a change in deformation direction

Muskalski Z., Wiewiórska S.

Hutnik, Wiadomości Hutnicze

|

2018

|

Vol. 85, nr 12

433--439

EN

The change of drawing direction, especially for the last drawn, can influence on the decreasing the mechanical properties and period fatigue strength of the wires as revealed from industrial practice. The numerical and experimental analysis the influence of friction coefficient and strain intensity on the change the cementite lamella orientation in the pearlite colony with different orientation relative to axis of drawn wires, has been shown in the work. It can be stated that for wire surface, for process with change of drawing direction, we observe the decrease strain intensity what causes the increase in the lamella inclination angle relative to wire axis. The results of theoretical analysis were confirmed by experimental research. It can be stated that decrease in cementite lamella orientation for wire surface, caused by the change of drawing direction, influences in essential way on the decrease of fatigue strength of high carbon steel wires.

PL

Jak wynika z praktyki przemysłowej zmiana kierunku ciągnienia, szczególnie w przypadku ostatniego ciągu, może wpłynąć na spadek własności mechanicznych i wytrzymałość zmęczeniową drutów. W pracy przedstawiono numeryczną i eksperymentalną analizę wpływu współczynnika tarcia i intensywności odkształcenia na zmianę orientacji płytek cementytu w kolonii perlitu o różnej orientacji względem osi w ciągnionych drutach. Stwierdzono, że dla powierzchni drutu, dla procesu ciągnienia zmianą kierunku ciągnienia obserwujemy spadek intensywności odkształcenia, co powoduje wzrost kąta nachylenia płytek cementytu względem osi drutu. Wyniki analizy teoretycznej zostały potwierdzone badaniami eksperymentalnymi. Zostało dowiedzione, że zmniejszenie orientacji płytek cementytu na powierzchni drutu, spowodowane zmianą kierunku ciągnienia, w istotny sposób wpływa na obniżenie wytrzymałości zmęczeniowej drutów ze stali wysokowęglowej.

2

The influence of heat treatment on toughness of extruded profiles from EN AW-6082 aluminium alloy

Romański P., Stradomski G., Wiewiórska S., Szarek A.

Hutnik, Wiadomości Hutnicze

|

2017

|

Vol. 84, nr 1

66--69

EN

The aim of this work was to analyze the influence of heat treatment on toughness of hot extruded aluminium profiles from EN AW-6082 aluminium alloy. The result of the conducted research has shown that the heat treatment had a significant effect on the toughness of aluminium profiles. In the study was found that the highest values of toughness were achieved after annealing process of hot extruded aluminium profiles.

PL

Celem pracy była analiza wpływu obróbki cieplnej na udarność wyciskanych na gorąco profili ze stopu aluminium EN AW-6082. Wyniki przeprowadzanych badań wykazały, że obróbka cieplna ma istotny wpływ na udarność profili aluminiowych. W badaniach stwierdzono, że najwyższą wartość udarności uzyskano po przeprowadzonym procesie wyżarzania wyciskanych na gorąco profili aluminiowych.

3

The influence of aging process parameters on selected mechanical properties of profiles from EN AW-6106 aluminium alloy

Romański P., Pilarczyk J. W., Wiewiórska S., Muskalski Z.

Hutnik, Wiadomości Hutnicze

|

2017

|

Vol. 84, nr 1

62--65

EN

The aim of this article was to analyze the influence of temperature and time period of artificially aging process on selected mechanical properties: Brinell hardness, yield strength, tensile strength, and elongation of hot extruded profiles from EN AW-6106 aluminum alloy. The result of the conducted research has pointed out that the temperature and the time of aging process had a significant effect on the selected mechanical properties. In the study it was found that the highest mechanical properties such as the yield strength and tensile strength for analyzed aluminum alloy were achieved for samples aged in temperature of 165°C for time period of 6 hours. The value of mechanical properties required be the standards for T6 temper were achieved after 2 hours of artificial aging in temperature of 165°C.

PL

Celem pracy była analiza wpływu temperatury i czasu procesu sztucznego starzenia na wybrane właściwości mechaniczne: twardość Brinella, umowną granice plastyczności, wytrzymałość na rozciąganie i wydłużenie wyciskanych na gorąco profili ze stopu aluminium EN AW-6106. Wyniki przeprowadzanych badań wykazały, że temperatura i czas procesu sztucznego starzenia ma istotny wpływ na wybrane do badań właściwości mechaniczne. W badaniach stwierdzono, że najwyższą wartość własności mechanicznych takich jak: umownej granicy plastyczności oraz wytrzymałości na rozciąganie uzyskano po przeprowadzonym procesie sztucznego starzenia w temperaturze 165°C przez czas 6h. Niezbędny poziom własności mechanicznych wymaganych przez normy dla stanu T6 osiągnięto już po dwóch godzinach procesu starzenia w temperaturze 165°C.

4

Wpływ sposobu ciągnienia drutów ze stali wysokowęglowej na naprężenia własne i wytrzymałość zmęczeniową

Bartosiński P., Muskalski Z., Wiewiórska S., Kucharska M.

Hutnik, Wiadomości Hutnicze

|

2012

|

Vol. 79, nr 8

540--543

PL

Naprężenia własne w warstwie przypowierzchniowej, najczęściej rozciągające, mogą wpłynąć na obniżenie wytrzymałości zmęczeniowej drutów, co jest istotne np. w pracującej linie. Aby zminimalizować wpływ naprężeń własnych poszukuje się rozwiązań umożliwiających zmianę rozkładu naprężeń lub ich obniżenie, już w czasie procesu ciągnienia. Taki efekt można uzyskać przez zastosowanie ciągnienia z małym gniotem końcowym. W pracy przeanalizowano 2 warianty procesu ciągnienia z małym gniotem końcowym, tj. przez ciągadło o zmodyfikowanej stożkowej części kalibrującej oraz przez dwa ciągadła w układzie tandem. Dla obu wariantów określono naprężenia własne I rodzaju oraz wytrzymałość zmęczeniową drutów finalnych. Przeprowadzone badania wykazały, że sposób realizacji małego gniotu końcowego w ciągadle o układzie tandem umożliwia istotne obniżenie naprężeń własnych I rodzaju w ciągnionych drutach oraz wpływa zasadniczo na wytrzymałość zmęczeniową drutów ze stali wysokowęglowej.

EN

The residual stresses in surface layer, usually stretching, can influence on the decrease of fatigue strength of wires. It is very important in working ropes. In order to reduce the influence of residual stresses, the methods of decreasing of residual stresses in wire drawing process i.e. small final reduction in last draft are introduced. In the work two variants of drawing process with small final reduction i.e. by die with modified conical bearing part and by two dies with tandem system, has been analyzed. For both variants the residual stresses of first kind and fatigue strength of final wires were done. It was proved that the application of small final reduction in tandem system during wire drawing process makes possible to decrease of residual stresses of first kind in drawn wires and also significant influences on fatigue strength of high carbon steel wires.

5

The comparison analysis of mechanical properties and fatigue strength for wires made from TRIP steel and from high carbon steel

Wiewiórska S.

Hutnik, Wiadomości Hutnicze

|

2012

|

Vol. 79, nr 12

904--907

EN

The TRIP steels are multiphase steels from the group AHSS (Advanced High Strength Steel) which contain in the structure bainite, ferrite and the most important component - retained austenite. The retained austenite is responsible for very high mechanical properties drawn wires, which can be obtain as the result of phase change retained austenite into martensite. On the base of research shown in the literature can be state that the increase of retained austenite in structure of steel through, for example, the increase of carbon content, can allow to obtaining the ﬁnal wires with high mechanical properties. Such wires can be alternative for wires made from high carbon steel. In the work the values of mechanical properties and fatigue strength for wires from TRIP steel (0.29% C), and for wires from GD 75A steel has been comprised.

PL

Stale TRIP stanowią przykład stali wielofazowych zaliczanych do grupy stali AHSS (Advanced High Strength Steel), które w swej strukturze zawierają bainit, ferryt oraz najbardziej istotny składnik - austenit szczątkowy. Austenit szczątkowy jest odpowiedzialny za wysokie własności mechaniczne ciągnionych drutów, które uzyskuje się w rezultacie przemiany austenitu szczątkowego w martenzyt. Na podstawie analizy literatury, można stwierdzić, że wzrost zawartości austenitu szczątkowego w strukturze drutów poprzez podwyższenie zawartości węgla, może pozwolić na otrzymanie z nich drutów charakteryzujących się wysokim własnościami mechanicznymi. Tego typu druty mogą stanowić alternatywę dla drutów wykonanych ze stali wysokowęglowych. W pracy przedstawiono analizę porównawcza własności mechanicznych i wytrzymałości zmęczeniowej drutów ze stali TRIP (0, 29% C) z własnościami drutów ze stali wysokowęglowej w gatunku GD 75A.

6

Intensification of the transformation of retained austenite to martensite under the influence of change in the stress state in wires of TRIP-type steel

Wiewiórska S.

Hutnik, Wiadomości Hutnicze

|

2012

|

Vol. 79, nr 8

659--661

EN

Both the magnitudes and dynamics of the stress state occurring in drawing processes may cause a considerable acceleration of the transformation of retained austenite to martensite in wires of TRIP-type steel. The paper presents an investigation to determine the amount of transformed retained austenite in the structure of wires made of TRIP-type steel resulting from the change in the stress state upon loading the material with cyclical and variable-sign stress under rotary bending conditions. The value of the stress acting on the material was smaller than the value of the proof stress R0.2. The carried out investigations made possible to determine whether and to what extent the loading of wire with cyclical external stresses of magnitudes lower than the R0.2 value might influence the amount of transformed retained austenite and, consequently, the mechanical properties of utility products.

PL

Występujące w procesach ciągnienia wartości, jak i dynamika stanu naprężenia może powodować znaczne przyspieszenie przemiany austenitu szczątkowego w martenzyt w drutach ze stali typu TRIP. W pracy przedstawiono badania dotyczące określenia ilości przeminionego austenitu szczątkowego w strukturze drutów ze stali typu TRIP, w efekcie zmiany stanu naprężenia, po obciążeniu materiału, cyklicznym, zmiennym co do znaku naprężeniem w warunkach zginania obrotowego. Wartość naprężeń oddziaływujących na materiał była mniejsza od wartości umownej granicy plastyczności R0,2. Przeprowadzone badania pozwoliły na stwierdzenie, czy i w jakim stopniu obciążenie drutów cyklicznymi naprężeniami zewnętrznymi o wartościach mniejszych od R0,2 może wpływać na ilość przemienionego austenitu szczątkowego, tym samym na własności mechaniczne wyrobów użytkowych.

7

Analiza wpływu parametrów dwustopniowej obróbki cieplnej na własności mechaniczne walcówki ze stali z efektem TRIP

Wiewiórska S., Muskalski Z., Michoń P.

Hutnik, Wiadomości Hutnicze

|

2012

|

Vol. 79, nr 2

89--94

PL

W celu otrzymania walcówki o strukturze z efektem TRIP należy przeprowadzić dwustopniową obróbkę cieplną, polegająca na wyżarzaniu stali w zakresie dwufazowym austenityczno-ferrytycznym i następującym po nim wygrzewaniu w zakresie przemiany bainitycznej. Odpowiednio dobrane parametry obróbki cieplnej mają decydujący wpływ na ilość otrzymanego w strukturze austenitu szczątkowego, a co za tym idzie, na własności wytrzymałościowe i plastyczne. W pracy przedstawiono analizę wpływu parametrów dwustopniowej obróbki cieplnej na własności mechaniczne walcówki z efektem TRIP.

EN

By the aim to obtaining the wire rod structure with TRIP effect we have to conduct two-stage heat treatment process consisted in annealing in austenitic-ferritic diphase range and in soaking in bainitic transformation range. The essential influence on the amount of retained austenite and mechanical and plastic properties of wire rod have right determined parameters of heat treatment process. The analysis of influence the parameters of two-stage heat treatment process on mechanical properties of wire rod with TRIP effect has been shown in the work.

8

Analiza porównawcza metod trawienia ujawniających wielofazową strukturę stali z efektem TRIP

Kucharska M., Wiewiórska S., Muskalski Z., Bartosiński P.

Hutnik, Wiadomości Hutnicze

|

2012

|

Vol. 79, nr 8

620--622

PL

W pracy przedstawiono wykorzystanie istniejących technik trawienia do obserwacji mikrostruktury stali z efektem TRIP za pomocą mikroskopu optycznego. Badania wykonano dla średniowęglowej stali z efektem TRIP. Przeprowadzono obserwacje mikrostruktur otrzymanych w wyniku trawienia i oceniono najbardziej efektywną z metod, pozwalającą na jak najdokładniejsze oszacowanie udziału objętościowego austenitu szczątkowego w strukturze.

EN

The usage of existing etching methods to observation of TRIP steel microstructure with use of optical microscope has been presented in the work. The investigations for medium carbon steel with TRIP effect has been done. The observations of microstructure obtained as a result of different etching methods has been made and the most effective method, allowed to the most accurate estimation of volume fraction of retained austenite in the structure, has been carried out.