The Effect of Abrasive Soil Mass Density on the Tribological Properties of Steel

Napiórkowski J., Lemecha M.

Tribologia

2018

nr 5

65--70

Even though soil mass density is among the basic characteristics of a soil mass, it has not been analysed in terms of wear impact on steel. This paper presents the results of testing for the wear of abrasion-resistant steel within a soil mass with varied density. The experiment was carried out under laboratory conditions using the “rotating bowl” method in a medium soil with varied moisture content. The following were determined: mass wear, an assessment of the friction coefficient development, and the image of the surface after the friction test. It was found that, within a soil mass with a significant plastic fraction content, the greatest wear of soil occurred for a density of approx. 1.4 g/cm3.

Gęstości masy glebowej, pomimo że należy ona do podstawowych charakterystyk masy glebowej, dotychczas nie opisano w aspekcie oddziaływania zużyciowego stali. Przedstawiono wyniki badania zużycia stali odpornej na zużycie ścierne w masie glebowej o zróżnicowanej gęstości. Eksperyment przeprowadzono w warunkach laboratoryjnych metodą „wirującej misy” w glebie średniej o zróżnicowanej wilgotności. Wyznaczono zużycie masowe, ocenę kształtowania się współczynnika tarcia oraz obraz powierzchni po badaniu tarcia. Stwierdzono, że w masie glebowej o znacznej zawartości frakcji plastycznych największe zużycie stali wynosi dla gęstości przyjmującej wartość ok. 1,4 g/cm3.

Effect of external load on the process of steel consumption in a soil mass

Napiórkowski J., Lemecha M., Konat Ł.

Tribologia

2017

nr 3

111--117

This paper presents the results of a study on the effect of external load on the course and intensity of Hardox Extreme hardness steel wear in sandy soil. The research was conducted under laboratory conditions using a rotating bowl machine. The abrasive was composed of two types of soil: light and medium. External pressure applied to the sample surface had the following values: 13.08, 39.24, and 65.04 [kPa]. On the basis of the results from the analysis of variance, a significant effect of external load on the values of wear on a differentiated level for particular soil masses was found. The analysis of friction surfaces complements the study. Furrows and micro-cuts prevail in the wearing process, and their intensity depends on the cohesion force between the soil grains.

W pracy przedstawiono wyniki badań wpływu obciążenia zewnętrznego na przebieg i intensywność zużywania stali trudnościeralnej Hardox Extreme w glebowej masie ściernej. Badania przeprowadzono w warunkach laboratoryjnych, wykorzystując maszynę typu „wirująca misa”. Masę ścierną stanowiły dwa rodzaje gleby: lekka i średnia. Zastosowano nacisk zewnętrzny na powierzchnię próbki o wartościach: 13,08; 39,24; 65,04 [kPa]. Na podstawie wyników z analizy wariancji stwierdzono istotny wpływ obciążenia zewnętrznego na wartości zużycia w stopniu zróżnicowanym dla poszczególnych mas glebowych. Badania uzupełnia analiza wyników uzyskanych po zużyciu powierzchni tarcia. W procesie zużywania dominuje bruzdowanie oraz mikroskrawanie, których intensywność oddziaływania uzależniona jest od siły kohezji pomiędzy ziarnami glebowymi.