Influence of the corrosive environment on the Portevin–Le Chatelier plastic instability phenomenon in Al–1Mg and Al–3Mg model alloys

Towarek A., Zdunek J., Mizera J., Dobkowska A., Molak R.

Inżynieria Materiałowa

2016

Vol. 37, nr 3

98--103

The aim of this work was to indicate the influence of changes on the surface of materials caused by the corrosive medium (3.5% NaCl solution) on the intensity and character of the Portevin–Le Chatelier effect in model aluminium alloys. For this purpose, two Al alloys, containing 1% and 3% of magnesium, were subjected to tensile testing in the as-cast state and after the exposition in NaCl solution for various time. Several electrochemical measurements were held to determine materials’ corrosive behaviour and microscopic observations to evaluate the surface character of the samples. High corrosion resistance of the materials resulted in a very slight alteration of their surface development, which didn’t lead into any significant variations in the plastic instability phenomenon PLC.

Efekt Portevin–Le Chatelier jest dobrze znanym i szeroko opisanym zjawiskiem pojawiającym się w wielu stopach aluminium. Objawia się on podczas odkształcania w postaci charakterystycznych ząbków na krzywej rozciągania wywołanych gwałtownymi zmianami naprężenia przy niewielkim odkształceniu. Wpływ na to zjawisko jest przypisywany głównie czynnikom wewnętrznym, wynikającym ze struktury materiału, takim jak: wielkość ziarna, obecność wydzieleń czy tekstury. Istotne mogą być jednak również czynniki zewnętrzne, m.in. szybkość odkształcania, środowisko czy stopień rozwinięcia powierzchni próbki. Celem pracy było zbadanie, jak zmiany na powierzchni materiału wywołane przez ekspozycję w środowisku korozyjnym (3,5% roztworze NaCl) wpłyną na intensywność i charakter zjawiska Portevin–Le Chatelier w dwóch modelowych stopach aluminium, Al–1Mg oraz Al–3Mg.

Portevin-Le Chatelier effect in rolled Al-Li based alloys.

Mizera J., Kurzydłowski K.J.

Inżynieria Materiałowa

2001

R. XXII, nr 3

125-129

Studies were carried out on the Portevin-Le Chatelier (PLC) effect in binary, ternary and quarternary Al-Li alloys and in the commercial 8090 alloy. The correlation between the serration characteristic, the rolling degree and the straining orientation has been analysed. The fact that the presence of the Cu-containing precipitates intensifies the PLC effects suggests, that these are primarily related to the interactions between the dislocations and the semi-coherent T1(Al2CuLi) precipitates. The analysis of the PLC effect in AlLi alloys shows that the serrations in the stress-strain curve exhibit a profund degree of anisotropy. Most pronounced PLC effects are observed along the rolling and transverse directions.

Analizie poddano zjawisko Portevin-Le-Chatelier (PLC) w modelowych (dwu-, trój- i czteroskładnikowym) oraz przemysłowym (8090) stopie na osnowie Al-Li. Badano zależność pomiędzy charakterem oscylacji a stopniem zgniotu i anizotropią blach. Obecność w mikrostrukturze badanych stopów wydzieleń zawierających Cu wzmacniających zjawisko PLC sugeruje, że jest ono głównie związane z oddziaływaniem pomiędzy dyslokacjami a półkoherentnymi wydzieleniami T1(Al2CuLi). Analiza zjawiska PLC w stopach na osnowie Al-Li wykazała, że oscylacje na krzywej rozciągania charakteryzują się dużym stopniem niejednorodności. Najintensywniejsze efekty PLC zaobserwowano w próbkach wyciętych wzdłuż kierunku walcowania i kierunku poprzecznego blachy.