The synthesis of zeolites from sewage sludge ash

Latosińska J.

Proceedings of ECOpole

|

2017

|

Vol. 11, No. 1

29--36

EN

The chemical composition of sewage sludge ash is similar to the chemical composition of substrates used for the synthesis of zeolites. The study shows the results of sewage sludge ash zeolitization with a fusion method. The research on sewage sludge ash before and after the process of zeolitization included the identification of a phase composition (XRD method) as well as the evaluation of both grain structure change (SEM method) and the cation exchange capacity (a method with the use of ammonium acetate). After zeolitization, sewage sludge ash contained hydroxysodalite, zeolite X and hydroxycancrinite. It was stated that zeolitization caused a positive increase of the cation exchange capacity.

PL

Skład chemiczny popiołów z osadów ściekowych jest podobny do składu chemicznego substratów stosowanych do syntezy zeolitów. W pracy przedstawiono wyniki zeolityzacji popiołów z osadów ściekowych metodą fuzji. Badania popiołów z osadów ściekowych przed oraz po procesie zeolityzacji obejmowały identyfikację składu fazowego (metoda XRD) oraz ocenę zmiany struktury ziaren (metoda SEM) i pojemności wymiany kationowej (metoda z wykorzystaniem octanu amonu). W popiołach z osadów ściekowych podanych zeolityzacji zidentyfikowano hydroksy sodalit, zeolit X oraz hydroksy kankrynit. Stwierdzono, że zeolityzacja spowodowała korzystny wzrost pojemności wymiany kationowej.

2

Low-temperature synthesis of zeolite from perlite waste — Part I: review of methods and phase compositions of resulting products

Król M., Morawska J., Mozgawa W., Pichór W.

Materials Science Poland

|

2014

|

Vol. 32, No. 3

503--513

EN

In this paper a review of the recent studies on the synthesis of zeolites from expanded perlite under hydrothermal conditions is presented. Attention is paid to possible outcomes of synthesis from low cost glass material, such as perlite. The study also investigates the phase composition of zeolitic materials obtained by modification of by-product derived from an expanded perlite production process. The synthesis was made using the hydrothermal method with sodium hydroxide under autogenous pressure at a temperature below 100 °C for 1 to 72 h. It was possible to obtain a zeolitic material at a temperature as low as 60 °C using 4.0 M NaOH. The X-ray diffraction pattern showed the biggest peak intensity of zeolite X with 4.0 M NaOH at the temperature of 70 °C. During synthesis at higher temperature zeolite Na-P1 (with 3.0 M NaOH at 90 °C) and hydroxysodalite (with 5.0 M NaOH at 90 °C) were obtained.

3

Materiał zeolitowy typu X otrzymany z popiołu lotnego w wyniku syntezy hydrotermalnej i niskotemperaturowej

Franus W.

Budownictwo i Architektura

|

2010

|

vol. 7, nr 2

25-34

PL

W pracy przedstawiono wyniki badań nad możliwością transformacji popiołu lotnego klasy F w materiał zeolitowy. Wykorzystano dwie metody syntezy: hydrotermalną i niskotemperaturową. W wyniku alkalicznych reakcji popiołów lotnych z NaOH w obu przypadkach otrzymano materiał zeolitowy bogaty w fazę Na-X. Zbadano charakter mineralogiczny i właściwości fizykochemiczne otrzymanego materiału oraz przedstawiono możliwości praktycznego wykorzystania.

EN

This study presents the results of experiments dealing with the possibility of transforming F class fly ash into a zeolitic material. Two types of synthesis methods were used in the research: hydrothermal and low-temperature synthesis. As a result of alkaline reaction of fly ash with NaOH, all experimental cases yielded zeolitic material which is rich in Na-X phase. The mineralogical composition as well as the physico-chemical properties in Na-X phase was obtained. The mineralogical composition as well as the physico-chemical properties of the obtained material are explored and the feasibility of practical application is shown.