Wyniki wyszukiwania - BazTech

1

The torsional and shear behavior of steel fiber reinforced RC members

Aydin Abdulkadir Cüneyt, Kiliç Mahmut, Maali Mahyar, Bayrak Bariş, Tunç Erkan

Architecture Civil Engineering Environment

|

2021

|

Vol. 14, no. 2

47--65

EN

Beams and columns are one of the important structural elements of buildings to take up transverse loads such as axial load, bending moment, shear, and torsion. Present work is an experimental investigation on the shear, torsion, and axial load behavior of the structural members like columns and/or beams. The reinforced concrete members with 0, 30, and 60 kg/m3 of steel fibers were tested for torsion, shear and axial loading for this study. The twist angle, the load-deflection behavior, the ultimate shear strength, the torsional moment, and the critical moments were obtained for the loading type and steel fiber ratios. The results show that the increasing steel fiber ratio, increased the torsional moment capacity and decreased the shear strength capacity. On the other hand, increasing the steel fiber content increased the both axial load and moment capacity of RC columns. The shear strength and the torsional moment capacities are defined by the provision of current codes of practice such as ACI318-19, Eurocode-2, British, Australian and Turkish Standards.

2

Mikrostruktura betonów z proszków reaktywnych

Grzeszczyk S., Matuszek-Chmurowska A., Černý R., Vejmelková E.

Cement Wapno Beton

|

2018

|

R. 21/83, nr 1

1--15

PL

Przygotowano specjalny skład betonu z proszków reaktywnych zawierający mączkę kwarcową i pył krzemionkowy, a także włókna stalowe. Skład ten pozwolił na osiągnięcie wytrzymałości betonu wynoszącej 145 MPa po dwóch dniach, a 198 MPa po 28 dniach dojrzewania w wodzie. Dodatek włókien stalowych o długości 12 mm pozwolił na osiągnięcie wytrzymałości na zginanie przekraczającej 48 MPa po 2 dniach i 52 MPa po 28 dniach. Zastosowany skład zapewnił bardzo zwartą mikrostrukturę matrycy cementowej oraz bardzo dobre wiązanie fazy C-S-H z ziarnami kwarcu, bez występowania strefy przejściowej.

EN

The produced special composition of reactive powder concrete contained the quartz powder and silicafume as well as steel fibres addition. This composition the compressive strength of 145 MPa after two days and 198 MPa after 28 days of water curing concrete samples. The steel fibres of 12 mm length addition have increased the flexural strength to higher than 48 MPa after 2 days and 52 MPa after 28 days of concrete cured in water. The special concrete composition the very compact microstructure with very good bond of C-S-H phase with quartz grains was caused, without interfacial transition zone.

3

An advanced approach to derive the constitutive law of UHPFRC

Mészöly T., Randl N.

Architecture Civil Engineering Environment

|

2018

|

Vol. 11, no. 1

89--96

EN

More than 200 specimens were tested in a comprehensive experimental campaign using ultra-high performance concrete with a mean compressive strength between 150 and 210 MPa and with different amounts of steel fibre reinforcement (0%, 1% and 2% by volume) from the first 2 days to 1.5 years after casting. From the large set of experimental tests related material parameters were derived. Based on compression tests with strain transducers and laser displacement transducers, the compression side of the constitutive law was derived, and based on the splitting tensile tests and flexural bending tests, the tensile side of the constitutive law was derived and the results are presented. For derivation of the tensile behaviour of ultrahigh performance fibre-reinforced concrete an advanced approach was applied by using a photogrammetric camera system with digital image correlation (DIC).

PL

Ponad 200 próbek zostało zbadanych w kompleksowej serii badań betonów bardzo wysokowartościowych o średnich wytrzymałościach na ściskanie od 150 do 210 MPa i przy zróżnicowanej ilości zbrojenia rozproszonego z włókien stalowych (0%, 1% i 2% objętości). Próbki badano w wieku od 2 dni do 1.5 roku po ułożeniu betonu. W poszczególnych seriach zbadano parametry materiałowe. W próbach ściskania, przy użyciu tensometrów i laserowych czujników przemieszczeń wyznaczono wartości ściskań do wykorzystania w równaniach konstytutywnych, a na podstawie prób rozciągania (w próbie rozłupywania przy ściskaniu wzdłuż pobocznicy) i wytrzymałości na zginanie wyznaczono wartości rozciągań do równań konstytutywnych. Do wyznaczenia wytrzymałości na rozciąganie betonu bardzo wysokowartościowego zbrojonego włóknami stalowymi zastosowano metodę fotogrametryczną z cyfrową korelacją obrazu (DIC).