Effect of non-zero mean stress bending-torsion fatigue on fracture surface parameters of 34CrNiMo6 steel notched bars

Macek Wojciech, Szala Mirosław, Trembacz Jarosław, Branco Ricardo, Costa José

Production Engineering Archives

2020

Vol. 26, Iss. 4

167--173

Modern methods of testing materials require the use of the latest technologies and combining measurement and calculation methods. It is important to find a quantitative way of describing, among other things, the failures so that it can help to design with high accuracy. This paper studies loading orientations on crack shape and fracture surface changes. The advantage of the entire fracture surface method is simplicity and applicability in studies on other materials, shapes and loadings. A higher values of fracture surface parameters (Sx, Vx) was observed in failure specimens with lower σ/τ (B/T) ratios. It has been observed that largest crack lengths with a small number of cycles occur for loading combinations different then B=T. As well as analyzed surface parameters Sx, Vx, are higher for larger number of cycles to crack initiation (Ni) values.

Identification of the cause of the stem neck fracture in the hip joint endoprosthesis

Ryniewicz A. M., Bojko Ł., Ryniewicz A., Pałka P., Ryniewicz W.

International Journal of Applied Mechanics and Engineering

2018

Vol. 23, no. 1

223--234

Endoprosthesis stem fractures are among the rarest complications that occur after hip joint arthroplasty. The aim of this paper is to evaluate the causes of the fractures of the Aura II stem neck, which is an element of an endoprosthesis implanted in a patient. In order to achieve it, a radiogram was evaluated, the FEM analysis was carried out for the hip joint replaced using the Aura II prosthesis and scanning tests as well as a chemical analysis were performed for the focus of fatigue. The tests performed indicate that the most probable causes leading to the fatigue fracture of the Aura II stem under examination were material defects in the process of casting and forging (forging the material with delamination and the presence of brittle oxides and carbides) that resulted in a significant reduction of strength and resistance to corrosion. In the light of an unprecedented stem neck fracture, this information should be an indication for non-destructive tests of ready-made stems aiming to discover the material and technological defects that may arise in the process of casting and drop forging.