Effect of chemical composition and plastic deformation on corrosion properties of highMn austenitic steels in alkaline solution

Kozłowska A., Grajcar A

Archives of Materials Science and Engineering

|

2016

|

Vol. 77, nr 1

31--39

EN

Purpose: The aim of the paper is to compare the corrosion properties of two high-Mn austenitic steels with various Al and Si additions in 0.1M NaOH solution using a potentiodynamic method. Design/methodology/approach: The steels used for the investigation were thermomechanically rolled in 3 passes. The final thickness of about 2 mm was obtained at a temperature of 850°C. Three groups of samples were prepared: thermomechanically rolled, thermomechanically rolled and additionally annealed at 900°C for 20 min, thermomechanically rolled and additionally cold deformed in static tensile test to total elongation of 36%. Corrosion resistance of investigated steels was examined using the potentiodynamic method. The metallographic inspection of corrosion damage included scanning electron microscope observations. The chemical analyses of the corrosion pits were carried out using EDS techniques. Findings: It was found that X4MnSiAlNbTi27-4-2 and X6MnSiAlNbTi26-3-3 steels were characterized by relatively high corrosion resistance in 0.1M NaOH solution independently of their state. EDS analysis revealed that corrosion pits nucleated preferentially at nonmetallic inclusions such as MnS and AlN. Results of potentiodynamic tests showed that cold deformation had the highest influence on decreasing the corrosion resistance of investigated steels. Thermomechanically treated and supersaturated specimens showed lower values of corrosion current density and consequently less amount of corrosion damage. Research limitations/implications: To investigate in more detail the corrosion behaviour of high-manganese austenitic steels, the impedance spectroscopy investigations will be carried out. Practical implications: The knowledge of the corrosion resistance of high-Mn steels has a significant effect on their industrial application in the automotive industry. Originality/value: The corrosion resistance of two high-manganese austenitic steels with different initial microstructures was compared in alkaline solution.

2

Oddziaływanie ceru, lantanu i neodymu na morfologię i skład chemiczny wtrąceń niemetalicznych w stalach mikrostopowych

Opiela M.

Hutnik, Wiadomości Hutnicze

|

2014

|

Vol. 81, nr 3

142--148

PL

W artykule opisano modyfikację składu chemicznego wtrąceń niemetalicznych pierwiastkami ziem rzadkich w nowo opracowanych stalach mikrostopowych. Badane stale przeznaczone są do produkcji elementów kutych metodą obróbki cieplno-plastycznej. Wytopy wykonano w indukcyjnym piecu próżniowym, a modyfikację wtrąceń niemetalicznych przeprowadzono miszmetalem w ilości 2,0 g na 1 kg stali. Skład chemiczny i morfologię wtrąceń niemetalicznych modyfikowano dodatkami Ce, La i Nd. Stwierdzono, że stale cechuje duża czystość metalurgiczna związana z małym stężeniem siarki (0,004%), fosforu (od 0,006 do 0,008%) oraz tlenu (6 ppm). Dużej czystości metalurgicznej odpowiada mały udział powierzchniowy wtrąceń niemetalicznych, wynoszący około 0,077%. Zdecydowaną większość stanowią drobne, globularne wtrącenia tlenkowo-siarczkowe lub siarczkowe o średniej powierzchni przekroju 17 mm2.

EN

The modification of the chemical composition of non-metallic inclusions by rare-earth elements in the new-developed microalloyed steels has been discussed in the paper. The investigated steels are assigned for production of forged elements by thermo-mechanical treatment. The steels were melted in a vaccum induction furnace and modification of non-metallic inclusions was carried out by the michmetal in the amount of 2.0g per 1kg of steel. The chemical composition and morphology of non-metallic inclusions was modified by additions of Ce, La and Nd. It was found that using material charge of high purity and a realization of metallurgical process in vacuum conditions result in a low concentration of sulfur (0.004%), phosphorus (from 0.006 to 0.008%) and oxygen (6 ppm). The high metallurgical purity is confirmed by a small surface fraction of non-metallic inclusions averaging 0.077%. A large majority of non-metallic inclusions are fine, globular oxide-sulfide or sulfide particles with a mean cross-section of 17 μm2.

3

Struktura stopu N-155 na odlewy części turbin gazowych

Paduch J., Gazdowicz J., Bąk S.

Archiwum Technologii Maszyn i Automatyzacji

|

2005

|

Vol. 25, nr 1

65-74

PL

Zbadano strukturę i właściwości użytkowe stopu N-155 wdrożonego w Wytwórni Sprzętu Komunikacyjnego PZL - Rzeszów SA do produkcji aparatów kierujących turbin gazowych. Podstawowymi wtrąceniami niemetalicznymi w stopie są glinokrzemiany manganu lub wapnia i manganu oraz tlenki krzemu. W austenitycznej osnowie stopu występują liczne wydzielenia dużych, dyspersyjnych węglików typu M23C6 i węglikoazotków typu MX. Stwierdzono występowanie dwóch typów dyspersyjnych węglików M23C6 w jednym z nich przeważa zawartość molibdenu, a w drugim chromu. Duże wydzielenia węglikoazotków typu MX zawierają giównie niob, wydzielenia dyspersyjne - niob lub niob i chrom.

EN

This paper presents the structure and usable property of N-155 alloy developed in Wytwórnia Sprzętu Komunikacyjnego (Factory of Transport Equipment) PZL - Rzeszów SA for steering apparatus of gas turbines. Manganese or calcium and manganese aluminosilicates as well as silicon oxides are the basic non-metallic inclusions in that alloy. In the austenitic matrix of the alloy, there are numerous precipitations of large and dispersion carbides of M23C6 type as well as carbonitrides of MX type. Occurrence of two types of 23C6 dispersion carbides was found. In one of them the content of Mo predominates, while in the other - Cr. The large precipitations of MX carbonitrides contain mainly Nb, whereas the dispersion ones - Nb or Nb and Cr.