PLA/PBAT blends for blown film extrusion

Ostrowska Justyna, Sadurski Waldemar, Paluch Magdalena, Dębowski Maciej, Wrona Olga, Sołtan Karolina, Tyński Piotr

Polimery

2024

Vol. 69, nr 7-8

420--429

Films of biodegradable PLA/PBAT blends with PBAT content of 10–90 wt% were obtained by extrusion blowing. PLA/PBAT blends were characterized by FT-IR, DSC, TGA and SEM. Tensile properties and tear strength of the films were also determined. It was shown that despite thermodynamic immiscibility of PLA and PBAT, addition of PBAT in amounts above 50 wt% allows obtaining films with good functional properties. Optimal properties were obtained with PBAT content of 60 or 70 wt%. Tensile strength was 36.7–38.7 MPa, elongation at break 357–388% and tear strength 11–22 N/mm.

Metodą wytłaczania z rozdmuchiwaniem otrzymano folie z biodegradowalnych mieszanin PLA/PBAT, w których zawartość PBAT wynosiła 10–90% mas. Mieszaniny PLA/PBAT scharakteryzowano za pomocą FT-IR, DSC, TGA i SEM. Określono również właściwości mechaniczne przy rozciąganiu i wytrzymałość na rozdzieranie folii. Wykazano, że pomimo termodynamicznej niemieszalności PLA i PBAT, dodatek PBAT w ilości powyżej 50% mas. umożliwia otrzymanie folii o dobrych właściwościach użytkowych. Optymalne właściwości uzyskano przy zawartości PBAT wynoszącej 60 lub 70% mas. Wytrzymałość na rozciąganie wynosiła 36,7–38,7 MPa, wydłużenie przy zerwaniu 357–388%, a wytrzymałość na rozdzieranie 11–22 N/mm.