Wyniki wyszukiwania - BazTech

1

The analysis of the post-operation microstructure and mechanical properties of the similar welded joint

Merda Agata, Klimaszewska Klaudia

Biuletyn Instytutu Spawalnictwa w Gliwicach

|

2020

|

Vol. 64, No. 6

37--41

EN

The test material was a specimen sampled from sections of a pipe operated for 41,914 hours at a temperature of 575°C and under a steam pressure of 28.2 MPa. The specimen subjected to metallurgical tests was a welded joint made of austenitic steel TP347HFG. The non-destructive tests and the macroscopic tests confirmed the lack of any welding imperfections. The test joint represented quality level B in accordance with related standard requirements. The microstructural tests of the heat-affected zone (HAZ) revealed the presence of the fine-grained austenitic structure with numerous precipitates on grain boundaries – probably M23C6 carbides. In spite of long-lasting operation, the mechanical properties of the test welded joint were high and did not exceed the standard-related requirements concerning the base material.

PL

Materiałem badawczym była próbka pobrana z wycinków rury długotrwale eksploatowanej, przez 105 000 godzin w temperaturze 540°C i przy ciśnieniu pary 12,5 MPa. Obszarem przeprowadzonych badań metaloznawczych było złącze spawane ze stali austenitycznej TP347HFG. Badania nieniszczące oraz obserwacje makroskopowe potwierdziły brak niezgodności spawalniczych. Badane złącze uzyskało poziom jakości „B” zgodnie z wymaganiami normatywnymi. Badania mikrostrukturalne strefy wpływu ciepła (SWC) TP347HFG ujawniły występowanie jednego charakterystycznego obszaru o gruboziarnistej strukturze austenitycznej z licznymi wydzieleniami obserwowanymi na granicach ziaren – najprawdopodobniej węglików M23C6. Właściwości mechaniczne badanego złącza mimo długotrwałej eksploatacji, były wysokie i nie przekraczały wymagań normatywnych dla materiału podstawowego.

2

Effect of additional alloying and heat treatment on phase composition and morphology in Al-Mg-Si-type casting alloy

Boyko V., Czekaj E., Warmuzek M., Mykhalenkov K.

Metallurgy and Foundry Engineering

|

2017

|

Vol. 43, no. 3

219--239

EN

The structure of permanent mold and high pressure die castings of the AlMg5Si2Mn alloy after alloying with Li and Sc has been investigated by scanning and transmission electron microscopy, hardness and microhardness measurements, energy dispersive X-ray analysis. Three conditions, as cast, solution treated and aged, were investigated. It was shown that in as-cast state, the structure of an alloy having the nominal composition AlMg5Si2Mn consists of four phases: first – the Al based solid solution, second – the (Al) + (Mg2Si) eutectic, third – the primary Mg2Si crystals and fourth – the α-Al(Mn, Fe)Si phase. Similar phases were observed in the alloys containing Sc or Li. After two days of storing in an as-cast condition, the solid solution in all tested alloys decomposes and forms zebra-crossing shaped precipitates. TEM examinations revealed that these precipitates nucleate heterogeneously on dislocations. The solution treatment at 575.0°C results in spheroidization of the Mg2Si lamellas, dissolution of the precipitates and formation of α-Al(Mn, Fe)Si dispersoids, nucleating on the surfaces of Mg2Si lamellas. In the Sc containing alloys, the formation of Al3Sc was detected after 120 min soaking. Further heating resulted in the growth of these precipitates. Aging of the Al-Mg-Si alloys leads to an increase of hardness in all studied alloys. This effect is mainly related to precipitation strengthening, via solid solution decomposition and formation of β’’-phase. In Li-alloyed specimens, plates of β Mg2Si phase were observed together with small cubic-shaped δ’ Al3Li precipitates.

PL

Strukturę odlewów wykonywanych w formach stałych i odlewów wysokociśnieniowych ze stopu AlMg5Si2Mn po stopowaniu Li i Sc badano za pomocą skaningowej i transmisyjnej mikroskopii elektronowej, a także wykonując pomiary twardości i mikrotwardości oraz prowadząc analizę rentgenowską z dyspersją energii. Badano trzy warianty: stan po odlaniu, odlew przesycony i starzony. Wykazano, że w stanie po odlaniu struktura stopu o nominalnym składzie AlMg5Si2Mn składa się z czterech faz: pierwsza – roztwór stały na bazie Al, druga – (Al) + (Mg2Si) eutektyczna, trzecia – pierwotne kryształy Mg2Si i czwarta – α-Al(Mn, Fe)Si. Podobne fazy zaobserwowano w stopach zawierających Sc lub Li. Po dwóch dniach przechowywania w stanie po odlaniu roztwór stały we wszystkich testowanych stopach rozkłada się i tworzy wydzielenia w kształcie przejściowym. Badania TEM ujawniły, że wytrącają one heterogenicznie jądro podczas dyslokacji. Obróbka roztworu przy 575,0°C powoduje sferoidyzację płytek Mg2Si, rozkład wydzieleń i tworzenie dyspersoidów oraz zarodkowanie na powierzchniach płytek Mg2Si. W stopie zawierającym Sc fazę Al3Sc wykryto po 120 min wygrzewania. Dalsze ogrzewanie spowodowało wzrost tych wydzieleń. Starzenie stopów Al-Mg-Si prowadzi do wzrostu twardości wszystkich badanych stopów. Efekt ten jest głównie związany z utwardzaniem wydzieleniowym na skutek rozkładu w stanie stałym i tworzenia fazy β’’. W próbkach ze stopu z litem obserwowano płytki fazy β-Mg2Si wraz z małymi sześciennymi wydzieleniami δ’-Al3Li.

3

Stan badań teoretycznych nad omłotem i wydzielaniem ziarna z masy zbożowej

Zagajski P., Dreszer K.A.

Journal of Research and Applications in Agricultural Engineering

|

2006

|

Vol. 51, nr 4

4-9

PL

Przeprowadzono analizę obszernego piśmiennictwa dotyczącego teoretycznych rozważań i eksperymentalnych badań nad procesem omłotu i wydzielania ziarna przez różne zespoły młócące. Celem tej analizy było ustalenie czynników mających wpływ na wyżej wymienione procesy oraz poznanie aspektów (sposobów) matematycznych opisów omłotu i wydzielania ziarna. W podsumowaniu wskazano na możliwości praktycznego i teoretycznego wykorzystania tych prac.

EN

The wide analysis of literature concerning the theoretical considerations and experimental studies of threshing and separation of grain from cereal mass by different threshing units was carried out. The aim of this analysis was to determine the factors which influence the above mentioned processes, as well as to learn the aspects (methods) of mathematical description of threshing and the grain separation. In the summary the possibility of practical and theoretical use of these studies was indicated.

4

Rozpad przesyconego roztworu stałego stopu CuNi13Sn5 podczas nieizotermicznego nagrzewania

Tumidajewicz M., Gryziecki J., Włoch G.

Rudy i Metale Nieżelazne

|

2005

|

R. 50, nr 8

445-447

PL

Przedstawiono zmiany struktury i umocnienia przesyconego roztworu stałego stopu CuNi13Sn5 podczas nieizotermicznego nagrzewania. Zastosowano badania kalorymetryczne, mikroskopii elektronowej oraz makro- i mikrotwardości. Określono zakresy zachodzących zmian strukturalnych podczas nagrzewania przesyconego stopu, dokonano identyfikacji tworzących się faz oraz ustalono rolę składników stopowych w umocnieniu stopu.

EN

Changes in structure and strengthening of saturated solid solution of CuNi13Sn5 alloy during non-isothermal heating are presented. Calorimeter investigations, electron microscopy, micro and macrohardness were applied. Range of changes in the structure during heating of supersaturated alloy was determined. The phases identification was made and the role of alloying constituents in strengthening of alloy was established.

5

Koncepcja procedury wprowadzania modelu zleceń zewnętrznych na warunkach outsourcingu kapitałowego w system organizacji prac geologicznych w polskim przemyśle wydobywczym

Bogacz P.

Prace Naukowe Instytutu Górnictwa Politechniki Wrocławskiej. Konferencje

|

2004

|

Vol. 107, nr 39

105-114

PL

W niniejszej pracy autor przedstawił konstrukcję szczegółowej procedury wprowadzenia modelu outsourcingu kapitałowego dla organizacji prac geologicznych w zakładach górniczych. Przeprowadził on wnioskowanie dotyczące słuszności tego rozwiązania, wskazując na pomocniczy charakter prac geologicznych, ich jednocześnie duży wpływ na prowadzoną w przyszłości działalność eksploatacyjną, jak również na pozytywną dla proponowanych rozwiązań sytuację geograficzną i geologiczną polskich złóż surowców mineralnych. Autor zaproponował algorytm decyzyjny dotyczący wydzielenia budując go na pięciu etapach: analizie, celach, formie, wdrażaniu i kontroli. Podkreślając nowatorstwo analiz zaproponowanych dla pierwszego etapu procedury, a przeprowadził badania sytuacji bieżącej dla organizacji prac geologicznych prowadzonych w KGHM "Polska Miedź" S.A., wskazując na ich podatność na wydzielenie a jednocześnie potrzebę wprowadzenia outsourcingu w KGHM "Polska Miedź" S.A.

EN

This paper presents construction of detailed procedure for detaching geological works organization in mines, through introducing the capital outsourcing method. Author showed how reasonable this process is, pointed at auxiliary character for geological works, simultaneously large influence on mining works in the future. Paper shows also positive geographical and geological situation of Polish ores for author's propositions. Author proposes decisions' procedure in the aspect of detaching. He builds this procedure in five stages: analysis stage, objects stage, form stage, detaching stage and control stage. Author pointed at the innovation of the first stage and showed the summary of analysis for organization of geological works in KGHM "Polska Miedź" S.A., indicating the susceptibility of detaching and simultaneously the necessity of introducing outsourcing.

6

The feasibility of phosphorus compounds recovery and recycling

Hoffmann J., Gluzińska J.

Polish Journal of Chemical Technology

|

2004

|

Vol. 6, nr 2

24-26

EN

This paper describes the current knowledge of phosphates removal and recovery from the municipal and industrial wastes. The removal of the phosphorus from the municipal wastewaters prior to their discharge into the receiving waters is widely practiced. The phosphorus is removed from the aqueous phase into the sludge phase and thus it can be recovered. The feasibility of the phosphate recycling into the phosphate industry and agriculture is discussed. The recovered P-product is likely to be of a better quality than the currently mined phosphate rock. Phosphorus compounds recovery should reduce the total wastewater biosolids production. The biological phosphorus removal has the potential to be used to the pre-concentrate phosphorus from the municipal wastewater prior to recycling via crystallization.

7

Przemiany stopu A14,7%Cu podczas przesycania i izotermicznego starzenia. Analiza dylatometryczna i zmiany twardości

Wierszyłłowski I., Stankowiak A., Wieczorek S.

Inżynieria Materiałowa

|

2003

|

R. XXIV, nr 6

410-412

PL

W oparciu o wcześniej publikowane badania [1] przeprowadzono analizę dylatometryczną przemian zachodzących podczas izotermicznego wygrzewania w 520 stopni Celsjusza i starzenia w 125, 150, 200, 250 i 290 stopniach Celsjusza. Podczas przesycania zachodzi ciągły skurcz próbek trwający około 145 h. Skurcz ten jest spowodowany rozpuszczaniem cząstek CuAl2 i trwającym równocześnie rozrostem ziarna roztworu stałego. Wzrostowi ziarna towarzyszy zmniejszenie się ilości defektów. Badania wykazały, że starzenie w 125 i 150 stopniach Celsjusza prowadzi do początkowego wzrostu wydłużenia, a potem wydłużenie spada. Zmiany te wiążą się z procesami wydzielania, rozpuszczania się wydzieleń i zarodkowania nowych. Podobne zmiany zachodzą ale w znacznie mniejszym stopniu podczas starzenia w 200 stopniach Celsjusza. Starzenie w 250 i 290 stopniach Celsjusza powoduje wzrost wydłużenia spowodowany zubożeniem roztworu stałego alfa w Cu i pojawienie się coraz większej ilości fazy CuAl2. Analiza procesu starzenia wykazała, że wymrożenie w ciekłym azocie po starzeniu powinno spowodować zmiany w roztworze stałym prowadzące do zmian własności mechanicznych. Badania twardości potwierdziły tę hipotezę. Wystąpił 6-16% wzrost twardości dla temperatur starzenia od 175 do 220 stopni Celsjusza w zakresie dłuższych niż 80 min. czasów starzenia. Twardość po przesycaniu i wytrzymywaniu w ciekłym azocie była ok. 20% wyższa niż dla próbek przesycanych i starzonych.

EN

On the basis of former publications [1] dilatometric analysis of transformations during isothermal supersaturation at 520 degrees centigrade and during isothermal aging at temperatures of 125, 150, 200, 250 and 290 degrees centigrade were performed. Alloy Al4,7%Cu was used. During supersaturation continuous decrease of elongation by 145 h was seen. The decrease of elongation was caused by dissolution of CuAl2 particles and increase of grains size. Aging at 125 and 150 degrees centigrade caused the increase of elongation at the beginning and after that gradual decline of elongation. These changes were caused by precipitation in the beginning of processes and dissolution of precipitation later on. The similar changes, but in smaller scale, appeared during aging at 200 degrees centigrade. Aging at 250 and 290 degrees centigrade caused increase of elongation because of decrease of Cu contents in solid solution and precipitation of increasing numbers of Cu Al2 particles. Analysis of aging processes suggested that deep cooling to low temperatures (about - 200 degrees centigrade) can change mechanical properties of alloy. Hardness measurements confirmed this hypothesis. Increase of hardness of 6-16% appeared while aging at 175-220 longer that 80 min. Hardness of specimens supersaturated at 520 degrees centigrade and kept at -196 degrees centigrade by one hour was 20% higher than conventionally supersaturated.

8

Crystallization, the cast structure and the formation of gas blowholes in high-nitrogen steels and alloy steels.

Svyazhin A.G., Siwka J., Skuza Z., Prokoshkina V.G., Kaputkina L.M.

Inżynieria Materiałowa

|

2001

|

R. XXII, nr 5

884-887

EN

In the paper, the results of experimental research concerning the precipitation of nitrogen in the form of gas blowholes during the crystallization of supersaturated Fe-N, Fe-O-S-N alloys and 1Cr13 and Cr18Ni10 steels have been described. It has been found that the precipitation of nitrogen gas blowholes is more intensive and the pressure pN2 is higher at low contents of surface active elements, i.e. oxygen and sulphur. At the concentration ([%O] + 0.5%[%S]) > or = 300 ppm, microingots exhibited a compact macrostructure without gas blowholes. The results of a kinetic analysis of the process of desorption of nitrogen and the thermodynamics of the investigated solution (including surface tension) confirm that the surface reaction plays a decisive role in the formation of gas blowholes. For this reason, it is possible to eliminate the formation of gas blowholes in ingots of ferritic and ferritic-austenitic steels by introducing such SAE admixtures, as Sb, Te or Se. Analytical expressions have been obtained, which define the amount of nitrogen releasing into gas blowholes and describe the conditions for producing ingots or casting of a compact structure at cooling rates of approximately 10 to the 3 K/s.

9

Wpływ wydzieleń fazy gamma' na zjawisko Portevina-LeChateliera podczas odkształcania superstopu niklu EI-867

Poznańska A, Sieniawski J., Kubiak K.

Archiwum Nauki o Materiałach

|

2000

|

T. 21, nr 3-4

189-198

PL

W pracy przedstawiono badania superstopu niklu EI-867 umacnianego wydzieleniowo cząsteczkami fazy gamma', który w celu otrzymania różnych rozmiarów cząsteczek obrobiono cieplnie według czterech wariantów. Wykonano próbę statyczną rozciągania w zakresie temperatury 20-1000 stopni Celsjusza, wyznaczając wytrzymałość na rozciąganie Rm, umowną granicę plastyczności R0,2 oraz podstawowe charakterystyki zjawiska Portevina-LeChateliera (PLC): Tz - zakres temperatury występowania, epsilon c - odkształcenie krytyczne początku ząbkowania, delta sigma a - amplitudę naprężenia ząbków. Stwierdzono wyraźną zależność cech charakteryzujących zjawisko PLC od rozmiarów cząsteczek fazy gamma' i od umocnienia stopu przez cząsteczki fazy gamma'.

EN

The paper presents results of studies on nickel-base superalloy EI-867 precipitation strengthened with gamma' phase particles. The alloy was heat treated according to four schemes giving various sizes of gamma' phase particles. Static tensile tests were performed in the temperature range of 20-1000 degrees centigrade. Determining tensile strength Rm, 0,2 proof stress R0,2 and basic characteristics of the Portevin-LeChatelier effect (PLC) i.e. Tz - temperature range of jerky flow, epsilon c - critical strain of jerky flow onset, delta sigma a - stress serrations amplitude. It was found that the size of gamma' phase particles and intensity of alloy strengthening by gamma' phase particles strongly influence the characteristic features of the PLC effect.

10

Structural and mechanical aspects of dynamic precipitation in some precipitation hardenable alloys.

Błaż L.

Inżynieria Materiałowa

|

1998

|

R. XIX, nr 3

447-454

EN

Recent experimental results and structural analysis of hot deformation processes in some precipitation hardenable alloys, with reference to experiments on dynamic precipitation presented in professional literature, are reviewed. In particular, the interaction of continuous and discontinuous precipitation in Cu-Ni-Si-Cr-Mg and Cu-Ti alloys was discussed on the basis of mechanical tests and structural observation results. Nonuniform deformation and dynamic coarsening of discontinuously grown particles within shear bands has followed the flow stress maximum during hot deformation of solution treated alloys at intermediate temperatures and was responsible for efficient material softening at larger strains. Dynamic precipitation in an Al-Mg-Si alloy was found to affect the strain rate sensivity. It was suggested that the strain rate sensivity, in the presence of nonuniform mode of deformation, could be accepted as a parameter which describes a specific mechanical property for a hot material only. Any analysis of dislocation movement affected by diffusion controlled solutes interaction or dynamic precipitation, as was suggested in the literature, seems to be doubtful. Hot deformation of copper and Cu-Cr alloy was found to result in an increase of the structural stability and, in consequence, mechanical properties of the material during post deformation annealing/aging.

11

Analysis of precipitation kinetics in the CuNi14A13 alloy by the differential scanning calorimetry DSC).

Sierpiński Z., Czeppe T., Gryziecki J.

Inżynieria Materiałowa

|

1998

|

R. XIX, nr 3

479-482

EN

Calorimetric investigations of non-commercial, precipitation strengthened CuNi14A13 alloy were carried out using a non-isothermal method, at a constant heating rate. The activation energy of the precipitation process was determined and kinetics equation proposed, derived by the method of kinetic analysis proposed by E-S. Lee and Y.G. Kim, on the basis of the modified Johnson-Mehl-Avrami/Austin-Rickett equation. The activation energy of the precipitation in the CuNi14Al3 alloy was estimated to be about 220 kJ/mole. Parallel structural processes occuring during strengthenning.