The Effect of Nanostructure Modification on the Silicate Binder on Its Binding Characteristics and Functional Properties

Izdebska-Szanda I., Baliński A., Angrecki M., Palma A.

Archives of Metallurgy and Materials

|

2014

|

Vol. 59, iss. 3

1033--1036

EN

A method for the chemical modification of silicate binder (hydrated sodium silicate) affecting the distribution of its nanostructure elements was disclosed. The effect of silicate binder modification on the resulting technological properties of moulding sands, determined under standard conditions and at elevated temperatures in the range from 100°C to 900°C, was discussed. Modification of this type is done on inorganic binders in order to reduce their unfavourable functional properties. It is particularly important when moulding sands with the silicate binder are used for casting of low-melting alloys. Therefore special attention was paid to the impact that modification of inorganic binders may have on the knocking out properties of sands prepared with these binders, when they are used in the process of casting non-ferrous alloys.

PL

Przedstawiono sposób modyfikacji chemicznej spoiwa krzemianowego (uwodnionego krzemianu sodu) wpływającej na rozkład elementów jego nanostruktury. Omówiono wpływ modyfikacji spoiwa krzemianowego na uzyskane właściwości technologiczne masy formierskiej wykonanej z jego udziałem, określone zarówno w warunkach znormalizowanych, jak i w warunkach podwyższonej temperatury w zakresie od 100°C do 900°C. Zastosowanie tego rodzaju modyfikacji spoiw nieorganicznych ma na celu ograniczenie ich niekorzystnych cech użytkowych. Jest to szczególnie istotne w przypadku zastosowania masy formierskiej ze spoiwem krzemianowym do wytwarzania odlewów ze stopów metali charakteryzujących się małą wartością temperatury topnienia. Dlatego szczególną uwagę zwrócono na wpływ modyfikacji spoiw nieorganicznych na wybijalność mas z ich udziałem przy odlewaniu stopów metali nieżelaznych.

2

Wybijalność mas ze szkłem wodnym modyfikowanym nanocząstkami MgO

Kmita A., Hutera B.

Archives of Foundry Engineering

|

2014

|

Vol. 14, iss. 4 spec.

55--58

PL

Przedmiotem pracy była modyfikacja szkła wodnego 5% mas. koloidalnym roztworem nanocząstek MgO w propanolu i dokładnej homogenizacji spoiwa. Celem przeprowadzonych badań było określenie wpływu modyfikacji szkła wodnego na wytrzymałość końcową na ściskanie Rctk oraz wybijalność mas z tym spoiwem oznaczonymi w próbie technologicznej zalecanej przez polską normę PN-85/H-11005. Wykazano, że zastosowana modyfikacja korzystnie wpływa na przebieg krzywej Rctk, powodując przesunięcie występowania II maksimum wytrzymałości masy w kierunku wyższych wartości temperatury. Pozytywne oddziaływanie zastosowanej modyfikacji szkła wodnego potwierdzone zostało próbami technologicznymi, w których stwierdzono poprawę wybijalności tych mas o 50% w porównaniu z wybijalnością mas ze szkłem wodnym niemodyfikowanym.

EN

Moulding sands with water glass belong to the group of environment friendly moulding sands. However, due to some disadvantageous technological properties of these sands, such as e.g. difficult knocking out and poor reclamation ability [1, 2], they are not widely applied in the foundry industry. Therefore numerous endeavours aimed at improving the quality of moulding sands with water glass are undertaken. Apart from the modification of the moulding sand matrix composition or controlling the hardening process the quality improvement of these sands can be achieved by means of binder modifications, either chemical or physicochemical. Reactions between water glass components and inoculants are essential in chemical processes. The progress of nanotechnologies occurring during last years, causes that nanomaterials are more and more often applied in several industries including also the foundry industry. Nanoparticles introduced into a binding material can react with it influencing and modifying its selected properties. The subject of the study is the water glass modification by the colloidal solution of MgO nanoparticles in propanol [3]. The aim of the performed investigations is the determination of the binder modification influence on the final compression strength Rctk and knock out property of moulding sands with the modified water glass (marked in the technological test according to the Polish standard: PN-85/H-11005).

3

Kryteria oceny wybijalności mas ze szkłem wodnym

Major-Gabryś K., Dobosz S. M., Zych J.

Archiwum Odlewnictwa

|

2005

|

R. 5, nr 17

163--168

PL

Artykuł dotyczy metod oceny wybijalności mas ze szkłem wodnym i nowym dodatkiem Glassex. Szczególny nacisk położono na nowo zaproponowaną ocenę wybijalności mas opartą o badania ultradźwiękowe. Metoda okazała się szybka, precyzyjna i bardzo przydatna.

EN

The article concerns the method of estimating the knock-out properties of moulding sands with water glass and new Glassex additive. Especially the lately proposed estimation of knock-out properties based on the ultrasound researches is taken into consideration. This method seems to be quick, precise and very useful.