Wurtzite InP phase formation during swift Xe ion irradiation

Gaiduk P.I., Komarov F.F., Herre O., Wendler E., Wesch W.

Nukleonika

1999

Vol. 44, nr 2

189-194

Ion beam-induced amorphization and crystallization in InP implanted at room temperature with swift (250 and 340 MeV) Xe+ ions to doses of 5x1013 and 1x1014cm-2, respectively, are investigated by the transmission electron microscopy. For the ion fluences above 5x1013cm-2 the formation of amorphous InP of two different atomic structures is registered after swift Xe ion implantation as a consequence of electron and nuclear energy deposition. In the case of the highest ion dose implanted (1x1014cm-2) a partial crystallization of the amorphous surface layer to polycrystalline InP is observed. The crystallization process passes a stage of wurtzite InP phase formation which is found to be metastable.

Za pomocą transmisyjnego mikroskopu elektronowego badano efekty amorfizacji i rekrystalizacji wywołane przez implantację InP (w pokojowej temperaturze) prędkimi jonami Xe (250 i 340 keV) z dozami, odpowiednio do 5x1013 i 1x1014cm-2. Dla dawek jonów powyżej 5x1013cm-2 zaobserwowano formowanie się dwóch różnych atomowych struktur amorficznego InP powstających na skutek deponowania energii w procesie elektronowego i jądrowego spowalniania. W przypadku implantacji z dozą 1014cm-2 obserwowano częściową rekrystalizację powierzchniowej warstwy amorficznej InP do postaci polikrystalicznej. Zauważono, że proces rekrystalizacji InP przechodzi poprzez utworzenie metastabilnej fazy o strukturze wurcytu.