Influence of the thin-wall ratio on the limiting spinning ratio and the thinning of the AMS 5504 sheet in spinning

Kut Stanisław, Ryzińska Grażyna, Mrugała Tomasz

Hutnik, Wiadomości Hutnicze

|

2023

|

Vol. 90 nr 4

15--19

EN

The paper contains the results of experimental research on the AMS 5504 sheet spinning process. The research was carried out on a Leifeld SFC 800 V500 two-roller metal spinning machine with a vertical axis. Various shapes of rollers and different thicknesses of sheet metal were used.The relationships between the limiting spinning ratio, thin-wall ratio and the fillet radius of roller were determined, and the occurrence of negative phenomena during the spinning process, such as wrinkling or cracking, was taken into account. The conclusions contained in the work and the developed methodology allow for a practical assessment of the possibility of producing drawpiece with given parameters by spinning.

PL

W pracy przedstawiono wyniki badań eksperymentalnych procesu wyoblania blachy AMS 5504. Badania przeprowadzono na dwurolkowej wyoblarceLeifeld SFC 800 V500 o osi pionowej. Zastosowano różne kształty rolek i różną grubość blachy. Określono zależności pomiędzy granicznym współczynnikiem wyoblania, współczynnikiem cienkościenności i promieniem zaokrąglenia rolki, a także uwzględniono występowanie negatywnych zjawisk podczas procesu wyoblania, takich jak fałdowanie czy pękanie. Wnioski zawarte w pracy oraz opracowana metodologia pozwalają na praktyczną ocenę możliwości wytwarzania wytłoczki o zadanych parametrach metodą wyoblania.

2

A parametric investigation of roller hemming operation on a curved edge part

Gürgen Selim

Archives of Civil and Mechanical Engineering

|

2019

|

Vol. 19, no. 1

11--19

EN

This study presents the roller hemming operation of a curved edge sheet metal which is critical in terms of dimensional accuracy and deformation. The investigation is focused on the process parameters such as bending angle, sheet thickness and roller diameter to observe their influence on roll-in, deformation, undesired wrinkling formation and hemming force which are directly related to material reliability and visual quality in the operation. A set of numerical simulations was designed and through the regression analysis of the results, the magnitude of each input parameter was investigated. The verification of the numerical model was carried out using experimental results. In the light of the results, the influence of input parameters was discussed for designing proper roller hemming operations for curved edge parts.

3

Weld line displacement during deep drawing of tailor welded blanks consisting of different sheet materials or sheet thicknesses

Svec P., Schrek A., Gabrisova Z.

Hutnik, Wiadomości Hutnicze

|

2017

|

Vol. 84, nr 8

383--386

EN

Deep drawing process of rectangular parts deep drawn from tailor welded blanks was studied. Two different types of tailor welded blanks were used in experiments. One consisting of different sheet materials: bake hardening steel BH220 and dual phase steel DP600 and with the same sheets thickness of 1.2 mm. Second one consisting of sheets from the same material TRIP steel 690T but with different thicknesses 1.2 and 1.0 mm. Three various weld line positions: longitudinal, transverse and diagonal were compared at both types of tailor welded blanks. Deep drawing process was characterised with uneven plastic flow and weld line displacement. The most significant weld line displacement was measured at using tailor welded blank consisting of different sheets materials and diagonal orientation of the weld line. Deep drawing of tailor welded blanks consisting of sheets with different materials was accompanied by earing of BH220 steel sheet. Deep drawing of tailor welded blanks consisting of sheets with different thicknesses was accompanied by wrinkling of thinner sheet.

PL

Badano wpływ głębokiego tłoczenia części prostokątnych łączonych spawanych prętów spawanych. W eksperymentach użyto dwóch różnych typów spawów. Jedna składa się z różnych materiałów: blach stalowych HB220 i DP600 o tej samej grubości 1,2 mm. Drugi, składający się z arkuszy z tego samego materiału TRIP typu 690T, ale o różnych grubościach 1,2 i 1,0 mm. Porównano trzy różne położenia linii spawania: wzdłużne, poprzeczne i przekątne w obu typach zgrzewanych krawędzi spawanych. Proces głębokiego tłoczenia charakteryzował się nierównomiernym płynięciem plastycznym i przesunięciem linii spawu. Największe przesunięcie linii spoiny obserwowano przy spawaniu różnych gatunków z ukośną orientacji linii spawania. Głębokie tłoczenie blach o różnych grubościach powodowało zmarszczeniu cieńszej blachy.

4

The influence of the core orthotropy on the wrinkling of sandwich panels

Pozorska J., Pozorski Z.

Journal of Applied Mathematics and Computational Mechanics

|

2015

|

Vol. 14, nr 4

133--138

EN

The paper concerns the phenomenon of wrinkling of compressed facing of a sandwich panel. The parametric analysis of the numerical model of the sandwich panel with a soft core is presented. The core was assumed as an elastic orthotropic material. The results of numerical simulations show the sensitivity of a sandwich structure to the variations of the core parameters. The results are evaluated qualitatively and quantitatively.

5

Face wrinkling of sandwich beams under pure bending

Jasion P., Magnucki K.

Journal of Theoretical and Applied Mechanics

|

2012

|

Vol. 50 nr 4

933-941

EN

The paper is devoted to sandwich beams under pure bending. The local buckling problem is analysed. The analytical description of the upper face wrinkling is proposed. From the principle of stationary total potential energy, formulae describing critical stresses in the faces of the beam are derived. The algorithm for determining the critical stresses is shown. Two particular cases of the solution following the core properties are mentioned. The finite element model of the sandwich beam is formulated. The comparison of the results obtained from the proposed analytical model and from FEM analysis is shown for a family of sandwich beams with different thicknesses and core properties.

PL

W pracy omówiono zagadnienie lokalnej stateczności belki trójwarstwowej poddanej czystemu zginaniu. Zaproponowano analityczny model marszczenia górnej, ściskanej okładziny. Z zasady stacjonarności energii potencjalnej wyprowadzono równanie opisujące naprężenia krytyczne. Zaproponowano algorytm pozwalający określić wartość naprężeń krytycznych w zależności od własności rdzenia. Opracowano model numeryczny MES belki trójwarstwowej. Dla rodziny belek przeprowadzono analizę numeryczną na wartości własne, a wyniki porównano z otrzymanymi z zaproponowanego modelu analitycznego.

6

Trwałość zmęczeniowa oraz analiza stanu naprężenia cienkiej płyty ze szczeliną w warunkach cyklicznego rozciągania

Kopecki T., Zacharzewski J.

Eksploatacja i Niezawodność

|

2006

|

nr 3

19-26

PL

Przedmiot badań stanowi cienka, prostokątna płyta ze szczeliną o grubości 0.7mm poddana cyklicznie zmiennemu obciążeniu rozciągającemu. Wskutek tego rodzaju obciążenia następuje propagacja szczeliny w czasie, aż do osiągnięcia długości krytycznej. W trakcie obciążania obserwuje się w obszarze szczeliny zjawisko lokalnej utraty stateczności, zwane marszczeniem konstrukcji (wrinkling). W wyniku, w obszarze szczeliny oprócz wywołanego rozciąganiem błonowego stanu naprężenia pojawia się stan giętny. Nie pozostaje to bez wpływu na proces propagacji szczeliny, rozkład naprężeń na jej froncie, a w konsekwencji na trwałość zmęczeniową. Celem niniejszej pracy jest jakościowa i ilościowa analiza wspomnianych powyżej zjawisk, zmierzająca do określenia krytycznej długości szczeliny, a tym samym trwałości zmęczeniowej konstrukcji. Płyta wykonana jest z poliwęglanu o znanych: charakterystyce natychmiastowej oraz właściwościach polaryzacyjno-optycznych. Równolegle z badaniami doświadczalnymi przeprowadzono obliczenia numeryczne metodą elementów skończonych mające na celu określenie rozkładu naprężeń w warunkach wyboczenia, począwszy od szczeliny o długości 30mm oraz dla dalszych zaawansowanych stanów deformacji. W celu rozwiązania geometrycznie i fizycznie nieliniowego zadania wykorzystano procedurę Riksa w programie ABAQUS. Obliczenia przeprowadzono dla trzech stanów deformacji odpowiadających długościom szczeliny: 30mm, 50mm, 70mm.

EN

The object of investigation constitutes rectangular, cracked thin-walled the plate subjected to axial cycles tension. As a result of such loading follows the crack propagation in time, all the way to critical length achieve. In the middle of cycles changing tension the plate sustains the local buckling wrinkling), as a result apart of membrane stress appears bending state as well. Growth of the crack length in time causes increasing of wrinkling area. It has an influence on the value of the stress, and in result on the speed of crack propagation and fatigue life. The purpose of the paper is qualitative and quantitative analysis of above described phenomene, since assumed an initial length to the critical value. The plate is made of polycarbonate, known of instantaneous characteristics and photo-elastics properties. At the same timewerede termineted, numerical calculations of critical loading and stress distribution in the buckling state, for initial crack 30mm and the next steps of deformation were det. Contemporaneous to experiments, numerical calculation were executed by FEM method. For the purposethe the geometricallynonlinear problemswas applied the Riks procedure by using ABAQUS program. Computations were carried out for three phases of deformation, at three next lengths of the crack: 30mm, 50mm, 70mm. Forms of deformation and effective stress distribution are presented.

7

The system for sheet forming design

Gronostajski J., Gronostajski Z., Matuszak A., Niechajowicz A., Zimniak Z.

Archives of Metallurgy

|

2001

|

Vol. 46, iss. 1

119-132

EN

In the paper the modern sheetmatal forming process design and diagnostic system is described. The system incorporates the forming limit stress diagrams and the wrinkling stress diagrams as the limit conditions of rorming into the commercial finite element method programme MARC.

PL

W pracy przedstawiono nowoczesny system do projektowania i diagnozowania procesów kształtowania plastycznego blach. W opracownym systemie połączono wykresy naprężeń granicznych dla procesów kształtowania blach i wykresy napręzeń fałdowania z profesjonalnym programem MARC wykorzystującym metodę elementów skończonych.