The Influence of Surface Free Energy on Tribological Properties of Oxide Layers Formed on Aluminium Alloy EN AW-5251

Niedźwiedź M., Bara M., Skoneczny W.

Tribologia

|

2018

|

nr 4

71--79

EN

This paper presents the influence of the parameters of the formation of oxide layers on the surface free energy and the tribological properties of these layers. The layers were formed electrochemically on aluminium alloy EN AW-5251, with variable values of electrolyte temperature and current density. A three-component electrolyte was used to produce oxide layers. The surface free energy was determined by the droplet deposition method by measuring the wetting angles, while the van Oss-Chaunhury-Good method was used for the calculations. Tribological tests were performed on a T-17 tribological tester under conditions of technically dry friction for reciprocating motion. T7W composite was used as a specimen in tribological tests.

PL

W artykule przedstawiono wpływ parametrów wytwarzania warstw tlenkowych na swobodną energię powierzchniową oraz właściwości tribologiczne tych warstw. Warstwy zostały wytworzone na stopie aluminium EN AW-5251 metodą elektrochemiczną, przy zmiennych wartościach temperatury elektrolitu oraz gęstości prądowej. Do wytwarzania warstw tlenkowych zastosowano elektrolit trójskładnikowy. Swobodna energia powierzchniowa wyznaczona została metodą osadzonej kropli poprzez pomiar kątów zwilżania, natomiast do obliczeń zastosowano metodę van Ossa-Chaunhury’ego-Gooda. Testy tribologiczne przeprowadzono na testerze tribologicznym T-17 w warunkach tarcia technicznie suchego dla ruchu posuwisto-zwrotnego. W testach tribologicznych jako próbki użyto kompozytu T7W.

2

The Effect of Active Diluent Addition on the Energy and Adhesive Properties of Epoxy Adhesive

Krawczuk Anna, Domińczuk Jacek

Advances in Science and Technology. Research Journal

|

2018

|

Vol. 12, no 1

19--25

EN

The paper reports values of surface free energy and its components of an epoxy adhesive modified by the addition of an active diluent. Wetting envelopes are determined and they serve as a basis for a wettability analysis and determining the possibility of maximizing the work of adhesion between the liquid and the solid. Static strength tests of adhesive joints made with the analysed adhesive compositions were also conducted. The results are used to determine the effect of active diluent addition on the energy and adhesive properties of the epoxy adhesive

3

Wpływ domieszkowania Tb na zwilżalność i wolną energię powierzchniową cienkich warstw TiO2

Wojcieszak D., Kaczmarek D., Domaradzki J., Prociów E., Placido F., Kavanagh J., Mazur M.

Elektronika : konstrukcje, technologie, zastosowania

|

2011

|

Vol. 52, nr 3

76-78

PL

W pracy przedstawiono wpływ domieszkowania terbem na zwilżalność i wolną energię powierzchniową cienkich warstw TiO2 . Nanokrystaliczne warstwy zostały wytworzone za pomocą wysokoenergetycznej metody rozpylania magnetronowego. Do analizy wybrano niedomieszkowaną warstwę TiO2 oraz warstwy domieszkowane terbem w ilości 0,4% at, 2% at i 2,6% at. Analiza wyników pokazała, że nanokrystaliczna matryca TiO2 miała właściwości hydrofilowe, a domieszkowanie terbem spowodowało uzyskanie warstw hydrofobowych. Na podstawie pomiarów kąta zwilżania określono wartości wolnej energii powierzchniowej oraz krytycznego napięcia powierzchniowego. Analiza wyników pokazała, że parametry te zależały w głównej mierze od struktury matrycy TiO2 i wielkości krystalitów w wytworzonych warstwach.

EN

In this work influence of terbium dopant on wettability and surface free energy of nanocrystalline TiO2 thin films have been presented. Thin films were manufactured by high energy reactive magnetron sputtering process. For analysis undoped TiO2 and TiO2 doped with 0.4% at., 2% at. and 2.6% at of Tb have been selected. Analysis of results has shown that nanocrystalline TiO2 matrix was hydrophilic, while doping with Tb results in hydrophobic films receiving. Based on contact angle measurements analysis surface free energy and critical surface tension was determined. Results have shown that those parameters were mainly dependent on the structure of TiO2 - matrix and crystallite sizes in manufactured samples.

4

Analysis of thickness influence on wettability of ITO thin films

Mazur M., Wojcieszak D., Domaradzki J., Sieradzka K., Kaczmarek D., Song S., Placido F., Gornicka B.

Elektronika : konstrukcje, technologie, zastosowania

|

2011

|

Vol. 52, nr 3

71-73

EN

In this paper contact angle and surface free energy of ITO thin films prepared by microwave-assisted magnetron sputtering process with thick-nesses of 280, 200, 100 and 50 nm were investigaled. The measurement of surface energy and contact angle was carried out with a computer controlled goniometer system with water, ethylene glycol and diodomethane. Contact angle measurements were performed according to the sessile drop method. Results have shown that manufactured ITO thin films with thickness of 280, 200 and 100 nm were hydrophobic, while 50 nm ITO thin film was hydrophilic. Contact angle was about 105 degrees for thin films with thickness above 100 nm. Decrease of thickness down to 50 nm results in 30% decrease of contact angle value (down to 75 degrees). The effect of ITO thin films thickness on the dispersive and polar components of the surface energy was also investigated. Analysis of surface free energy has confirmed that samples with lower surface free energies exhibit higher values of water contact angles.

PL

W artykule przedstawiono wyniki badań kąta zwilżania i wolnej energii powierzchniowej cienkich warstw ITO o grubościach odpowiednio 280, 200, 100 i 50 nm, wytworzonych za pomocą rozpylania magnetronowego wspomaganego mikrofalami. Pomiary energii powierzchniowej oraz kąta zwilżania zostały wykonane za pomocą specjalistycznego stanowiska używając wody, glikolu etylowego oraz diodometanu. Kąty zwilżania określono za pomocą pomiaru osadzonych kropli na powierzchni cienkich warstw. Wyniki pokazały, że wytworzone cienkie warstwy ITO o grubościach 280, 200 oraz 100 nm były hydrofobowe, podczas gdy warstwa ITO o grubości 50 nm wykazała właściwości hydrafilowe. Kąt zwilżania wynosił około 105° dla próbek o grubościach 100, 200 oraz 280 nm. W wypadku próbki ITO o grubości 50 nm kąt zwilżania zmniejszył się o 30% (do 75°). Zbadano również wpływ grubości warstw ITO na składową dyspersyjną i polarną energii powierzchniowej. Analiza wolnej energii powierzchniowej potwierdziła, że próbki z niższą energią powierzchniową odznaczają się wyższymi kątami zwilżania.