Effect Of Heat-Treatment On Microstructure And Magnetic Properties Of Nanocrystallized Mn-Zn Ferrite Powders

Lee W. H., Hong C. S., Chang S. Y.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 2B

1347--1350

The initial ferrite powders were subjected to high energy ball milling at 300rpm for 3h, and subsequently heat-treated at 573-1273K for 1h. Based on the observation of microstructure and measurement of magnetic properties, the heat-treatment effect was investigated. The size of initial powders was approximately 70μm. After milling, the powders with approximately 230nm in size were obtained, which were composed of the nano-sized particles of approximately 15nm in size. The milled powders became larger to approximately 550nm after heat-treatment at 973K. In addition, the size of particles increased to approximately 120nm with increasing temperature up to 973K. The coercivity of initial powders was almost unchanged after milling, whereas the saturation magnetization increased. As the heat-treatment temperature increased, the saturation magnetization gradually increased and the maximum coercivity was obtained at 773K.

Identification of nanostructure in aluminium alloys by X-ray diffraction

Żelechowski J., Kłyszewski A.

Archives of Metallurgy and Materials

2008

Vol. 53, iss. 1

301-305

A number of physical properties of polycrystalline materials, including the mechanical properties, greatly depend on grain size and therefore grain size is a very important parameter in the technology of modern structural materials. Adaptation of optical microscopy in evaluation of crystallite size is frequently limited by basic parameters of this technique, and the result represents only a small area of the specimen surface. Therefore, it has been decided to use an alternative method in evaluation of the crystallites size. The method determines the width of the X-ray diffraction reflections according to a relationship expressed by Scherrer's formula. Easy analysis of the large material volume seems to be significant advantage of this method. The size of the crystallites was calculated by mathematical modelling of the profiles of small-angle diffraction reflections obtained by the Bragg-Brentano technique. The applicability range of this method was established along with the conditions indispensable for its correct application. The described method was used to determine the size of crystallites in the selected aluminium products, in ribbons made by the process of rapid solidification, and in nanometric materials prepared from commercial aluminium alloys. The results obtained were compared with optical microscopy and transmission electron microscopy, and showed enough by the X-ray measurement satisfactory consistency of the measured quantities.

Wiele własciwości fizycznych, w tym właściwości mechaniczne materiałów polikrystalicznych w istotny sposób zależą od wielkości ziarna i dlatego rozmiar ziarna jest znaczącym parametrem w technologii nowoczesnych materiałów konstrukcyjnych. Zastosowanie mikroskopii świetInej do oceny wielkości krystalitów jest ograniczone możliwościami technicznymi, a wynik uzyskiwany jest z niewielkiego obszaru powierzchni próbki. Do oceny wielkości krystalitów przyjęto metodę alternatywną, poddającą analizie szerokość rentgenowskich refleksów dyfrakcyjnych zgodnie z zależnością wyrażoną wzorem Scherrera. Niekwestionowaną zaletą metody dyfrakcyjnej jest łatwość analizy znacznej objętości materiału. Pomiar wielkości krystalitów zrealizowano przy użyciu modelowania matematycznego profili niskokątowych refleksów dyfrakcyjnych (111) uzyskanych w technice Bragg-Brentano. Określono również zakres stosowalności metody i warunki niezbędne do prawidłowego jej użycia. Opisaną metodą oznaczono wielkość krystalitów w wybranych wyrobach aluminiowych, w taśmach wytwarzanych metodą szybkiej krystalizacji oraz w nanometrycznych preparatach sporządzonych z komercyjnych stopów aluminium. Uzyskane wyniki zweryfikowano przy użyciu mikroskopii świetInej i elektronowej wykazując zadowalającą zgodność oceny mierzonych wielkości.