NanEffect of SiO2 Nanoparticles on the Wear Resistance of Starch Films

Wu M., Wang Y., Wang M., Ge M.

Fibres & Textiles in Eastern Europe

2008

Vol. 16, no. 4 (69)

96--99

Nanoparticles have been increasingly used to improve the properties of polymer materials. In this study, SiO2 nanoparticles were added to starch for sizing applications in the textile industry. The effects of the content of SiO2 nanoparticles on the abrasion properties of the starch film were measured using a wear tester. The wearing surfaces were observed with Scanning Electronic Microscope, an Atom Force Microscope and a High Magnification Optical Microscope in order to better understand the wearing mechanism. The results showed that the best wear resistance was achieved when the content of SiO2 nanoparticles was about 3%. The wear resistance mechanism of starch film containing SiO2 nanoparticles was analysed.

Nanocząstki są coraz częściej stosowane dla polepszenia właściwości materiałów polimerowych. W przedstawionych badaniach Nanocząstki SiO2 były dodawane do preparacji skrobiowych stosowanych w przemyśle włókienniczym. Mierzono wpływ zawartości nanocząstek SiO2 na wytrzymałość na ścieranie powłok skrobiowych za pomocą urządzenia do badania ścieralności. Powierzchnie ścierane były obserwowane za pomocą elektronowego mikroskopu skaningowego, mikroskopu sił atomowych i mikroskopu optycznego umożliwiającego duże powiększenie. Pozwoliło to lepiej zrozumieć mechanizm ścierania. Wyniki wskazują, że najlepszą odporność na ścieranie otrzymano kiedy zawartość nanocząstek SiO2 wynosiła około 3%. Analizowano mechanizm odporności na ścieranie folii skrobiowych z dodatkiem nanocząstek SiO2.