Assessment of Polylactide Properties for Use in Knitted Clothing Products

Pinar Anna, Mielicka Elżbieta

Fibres & Textiles in Eastern Europe

2021

Vol. 29, no. 5 (149)

66--74

The article presents the results of a study work on the assessment of selected structural and performance characteristics of weft knitted fabrics, produced from the commercial multifilament polylactide yarn PLA 6201D. The work was carried out on PLA materials with the aim of application in lightweight outerwear. The materials presented are examples of solutions used in the industrial process of the manufacturing and finishing of so-called seamlesswear products. The structure of the materials in the solutions of left-right stitch applied was determined by the indicator of the degree of filling of the knitted fabric "k", used in the filling characteristics of the linear structure of knitting materials made from the same type of yarn. The functional properties of the materials were determined in the scope of selected indicators, important in the aspect of physiological comfort and clothing's quality of wear. The PLA yarn was subjected to the assessment selected qualitative and hygroscopic indicators, which was carried out in relation to selected multifilament polyester yarns of similar linear mass.

Artykuł przedstawia wyniki z prac badawczych z zakresu oceny wybranych właściwości strukturalnych i użytkowych dzianin rządkowych, wytworzonych z komercyjnej multifilamentowej przędzy polilaktydowej PLA 6201D. Prace zrealizowano dla odzieżowego kierunku aplikacji materiałów PDLA na lekkie wyroby wierzchnie. Prezentowane materiały stanowią przykłady rozwiązań technologicznych, stosowanych w przemysłowym procesie wytwarzania i wykończenia tzw. wyrobów seamlesswear. Strukturę materiałów w zastosowanych rozwiązaniach konstrukcyjnych splotu lewoprawego określono wskaźnikiem stopnia zapełnienia dzianiny k, stosowanym w charakterystyce zapełnienia liniowego struktury materiałów dziewiarskich, wykonanych z tego samego rodzaju przędzy. Właściwości użytkowe materiałów określono w zakresie wybranych wskaźników, istotnych w aspekcie komfortu fizjologicznego i jakości użytkowej odzieży. Przędzę PDLA poddano ocenie w zakresie wybranych wskaźników jakościowych i higroskopijnych, którą przeprowadzono w odniesieniu do wybranych multifilamentowych przędz poliestrowych o podobnej masie liniowej.

Właściwości trybologiczne kompozytów na osnowie stali szybkotnącej

Madej M., Leżański J.

Kompozyty

2008

R. 8, nr 1

87-92

Przedstawiono wyniki badań w zakresie badania odporności na zużycie cierne i współczynnika tarcia infiltrowanych kompozytów na osnowie stali szybkotnącej. Materiał badawczy stanowiły kształtki ze stali szybkotnącej gatunku M3/2 i stali szybkotnącej z dodatkiem 7,5% Cu, 0,3% C, 20% Fe, 50% Fe oraz 10 i 30% węglika wolframu WC. Porowate kształtki przeznaczone do infiltracji prasowano pod ciśnieniem 800 MPa, część z nich poddano spiekaniu w piecu próżniowym w temperaturze 1150°C przez 60 minut. Następnie porowate kształtki infiltrowano miedzią, metodą nakładkową w piecu próżniowym w temperaturze 1150°C przez 15 minut. Badania odporności na zużycie cierne oraz współczynnika tarcia przeprowadzono testerem T-05.

High hardness, mechanical strength, heat resistance and wear resistance of M3/2 high speed steel (HSS) make it an attractive material for manufacture of valve train components such as valve seat inserts and valve guides. Since technological and economical considerations are equally important, infiltration of high-speed steel skeleton with liquid cooper has proved to be a suitable technique whereby fully dense material is produced at low cost. Attempts have been made to describe the influence of the production process parameters and additions of powders: copper, graphite, iron and tungsten carbide on the tribological properties of copper infiltrated HSS based composites. The compositions of powder mixtures were M3, M3+7.5Cu, M3+0.3C, M3+20Fe, M3+50Fe, M3+10WC and M3+30WC. The powder mixtures were prepared by mixing for 30 minutes in the 3-D pendulum motion TurbulaŽ T2C mixer. Then the powders were cold pressed in a rigid cylindrical die at 800 MPa. The infiltration process was carried out in vacuum better than 10(-3) Pa. Both green compacts and compacts pre-sintered for 60 minutes at 1150°C in vacuum were contact infiltrated with copper. Carefully pre-weighed performs of copper were placed on top of the rigid skeletons of predetermined porosity, heated to 1150°C, held at temperature for 15 minutes, and cooled down with the furnace to the room temperature. From the analysis of the obtained results it may be concluded that the mechanical properties is mainly affected by the manufacturing route and powders characteristics (M3/2 HSS, Höganäs iron, tungsten carbide WC) and powder composition of porous skeleton for infiltration. From it is evident that the as-infiltrated properties of the investigated composites are a complex function of the manufacturing route and tungsten carbide content. The molten copper is drawn into the interconnected pores of the skeleton, through a capillary action, and fills virtually the entire pore volume to yield final densities exceeding 97% of the theoretical value. Wear quality of the as-infiltrated composites increases with the increased content of tungsten carbide, whereas the bending strength seems to be adversely affected by the addition of the tungsten carbide powder. Considerable differences in hardness between the materials obtained from the two infiltration routes have been observed, with higher wear quality numbers achieved with direct infiltration of green compacts. As can be seen, the additions of iron didn't worse wear quality of composites obtained from infiltration of green compacts.