1

Impact of moisture conditions on early shrinkage of ordinary concrete with changing w/c ratio

Jasiczak J., Szymański P., Nowotarski P.

Archives of Civil Engineering

|

2014

|

Vol. 60, nr 2

241--256

EN

Article presents the results of the effect of humidity on early shrinkage of normal concrete with variable W/C ratio. As known for a long time, shrinkage is dependent of many factors. One of them is the W/C ratio and the quantity of water which is located in the concrete mix. In article there were discussed changes taking place in the concrete mix, the methods of research and the partial results obtained by the authors of the paper. Shrinkage is a phenomenon well known and studied by various research centers. The total amount of shrinkage may depend on various factors such as humidity, temperature, composition of the concrete mix, the W/C ratio, the size of the item. The study was conducted to determine the amount of shrinkage in its early stages. It is very important for concrete floors contractors, precast manufacturers to start at the right time finishing work and prevent the formation of shrinkage cracks.

2

Rozwój mikrostruktury podczas hydratacji ultra BWW

Pfeifer C., Moeser B., Stark J.

Cement Wapno Beton

|

2010

|

R. 15/77, nr 3

123-131

PL

Przeprowadzono obserwacje mikrostruktury próbek betonu z proszków reaktywnych po różnym okresie hydratacji, przy zastosowaniu najnowszych typów mikroskopów skaningowych. Są to mikroskopy o zmiennej próżni i z zastosowaniem pary wodnej, o wysokiej zdolności rozdzielczej. W wyniku badań stwierdzono, że dodatek superpastyfikatora znacznie opóźnia proces hydratacji i zakłóca wzrost kryształów ettringitu. W początkowym okresie hydratacji ziarna klinkieru < 2 um ulegają częściowemu lub całkowitemu rozpuszczeniu, co powoduje powstawanie pustek z otoczkami w mikrostrukturze matrycy. Wiązanie pomiędzy matrycą i kruszywem jest bardzo mocne i w strefie przejściowej nie występują pory. Natomiast reakcja pucolanowa pyłów krzemionkowych jest słabo zaawansowana, z uwagi na mały stosunek w/c.

EN

The UHPC microstructure, after different time of hydration, was examined with high resolution SEM imaging techniques. ESEM in WET mode for early hydration process and NanoSEM for extremely dense microstructure. The obtained results have shown that high addition of superplasticizer caused the strong retardation of hydration process. The growth of ettringite is also influenced. At early hydration the clinker particles < 2 um are often partially or completely dissolved, resulting in hollow shells formation in the microstructure. The bond between matrix and aggregate is very strong and the interfacial zone shows no gaps. However, the pozzolanic reaction of silica fume shows low advancement, because of water shortage caused by very small w/b ratio.

3

O wpływie zawilgocenia betonu na trwałość konstrukcji betonowych i żelbetowych

Bogucka J., Grabiec-Mizera T.

Inżynieria i Budownictwo

|

2005

|

R. 61, nr 10

572-575

PL

Omówiono wpływ wody i warunków wilgotnościowych środowiska na właściwości betonu i zachodzące w nim procesy związane z jego trwałością, takie jak wytrzymałość na rozciąganie, granice mikrozarysowania, mrozoodporność, współczynnik rozszerzalności termicznej, karbonatyzacja. Wykazano istotny wpływ wilgotności betonu i środowiska na przebieg procesu degradacji konstrukcji betonowych i żelbetowych.

EN

This paper deals with influence of moisture content in concrete and humidity of the environment on the properties and process influenced concrete durability. These properties include tension strength, microcracing limits, freeze resistance, thermal coefficient of expansion, carbonation. Authors proved that moisture and humidity have strong influence on the process of degradation of concrete and RC structures.