Corrosion properties of Ni/Al2O3/Cgraphite hybrid composite layers

Bartoszek W., Cieślak G., Skroban K., Mazurek A., Trzaska M.

Ochrona przed Korozją

|

2018

|

nr 2

36--39

EN

The paper presents the results of studies of composite layers with nickel matrix and dispersed phase in the form of: alumina oxide (Al2O3) and graphite (Cgraphite) produced by electrodeposition on steel substrate. Three variants of composite layers were produced: Ni/Al2O3, Ni/Cgraphite, Ni/Al2O3/Cgraphite and for comparison purpose a nickel layer was also produced. Alumina oxide and graphite powders were used as dispersion phases. The dispersed phases were characterized by scanning electron microscopy (SEM) and Raman spectroscopy for graphite powder. The results of investigations of the structures of the produced layers with SEM, EDS, and results of Vickers hardness measurements as well as results of corrosion tests using electrochemical potentiodynamic method are presented. Damage characteristics after corrosion studies were obtained using a light microscope.

PL

W pracy przedstawiono wyniki badań warstw kompozytowych z niklową osnową oraz wbudowanymi w nią cząstkami faz dyspersyjnych w postaci: tlenku glinu (Al2O3) oraz grafitu (C grafit) wytwarzanych w procesie elektroosadzania na podłożu stalowym. Wytworzono trzy warianty powłok kompozytowych: Ni/Al2O3, Ni/C grafit, kompozytową warstwę hybrydową Ni/Al2O3/C grafit oraz w celach porównawczych warstwę niklową. Jako fazy dyspersyjne stosowano proszki Al2O3 oraz grafitu rozproszone w kąpieli Wattsa. Charakterystykę faz dyspersyjnych realizowano za pomocą skaningowej mikroskopii elektronowej (SEM) oraz spektroskopii Ramana dla proszku grafitu. Przedstawiono wyniki badań struktury oraz składu chemicznego wytworzonych warstw za pomocą SEM z przystawką EDS, wyniki pomiarów twardości metodą Vickersa, a także wyniki badań korozyjnych za pomocą elektrochemicznej metody potencjodynamicznej. Charakterystykę zniszczeń po badaniach korozyjnych dokonano za pomocą mikroskopu świetlnego.

2

Kształtowanie struktury i właściwości niklowych warstw powierzchniowych metodami redukcji chemicznej i elektrochemicznej

Trzaska M.

Inżynieria Powierzchni

|

2013

|

nr 4

3--8

PL

W pracy przedstawiono wyniki badań zarówno struktury, jak i właściwości warstw niklowych wytworzonych metodami redukcji chemicznej i elektrochemicznej. Za pomocą elektronowej mikroskopii transmisyjnej i skaningowej oraz dyfrakcji rentgenowskiej zbadano strukturę warstw Ni-P oraz Ni. Analizę składu chemicznego warstw Ni-P wykonano za pomocą detektora EDS. Badania adhezji wytworzonych warstw do podłoża zrealizowano techniką kontrolowanego zarysowania powierzchni za pomocą scratch testera. Metodą Vickersa określono mikrotwardość badanych warstw Ni-P oraz Ni. Zrealizowane badania wykazały, że składem kąpieli można kształtować strukturę krystaliczną warstw niklowych wytwarzanych metodą elektrokrystalizacji, która decyduje o ich właściwościach. Warstwy Ni oraz Ni-P charakteryzują się dobrym połączeniem z materiałem podłoża oraz dużą twardością.

EN

The paper presentsresults of studiesof the structure andproperties ofnickel layersproducedbychemical and electrochemicalreduction methods. Ni-P andNi layer structureswere examined by usingtransmission andscanning electron microscopiesandX-ray diffraction technique. The analysis ofthe chemical composition ofthe Ni-P layerwas performed usingEDSdetector. Studiesof adhesionof the layersto the substratewere tested by the controlled surface scratching techniquewith using a scratchtester.Vickersmicro-hardnesstestswere performed forofNi-Pand Ni layers. Completedstudies have shown that by the composition of the electrolyte bath the crystal structure ofnickel layersproducedbyelectrocrystallization process can be shaped that determinestheirproperties.NiandNi-P layers are characterized by goodconnectionwith the substrate materialand exhi-bithigh hardnesses.

3

Zużycie ścierne warstw niklowych modyfikowanych dyspersyjną fazą ceramiczną

Trzaska M., Kowalewska M., Wyszyńska A.

Prace Naukowe Instytutu Konstrukcji i Eksploatacji Maszyn Politechniki Wrocławskiej. Konferencje

|

2002

|

Vol. 87, nr 27

340-345

PL

W pracy przedstawiono wyniki badań zużycia ściernego powierzchniowych warstw niklowych Ni, Ni-P oraz warstw kompozytowych Ni-Si3N4, Ni-P-Si3N4 wytwarzanych metodami chemicznymi i elektrochemicznymi na podłożu stalowym. Podano wyniki analizy granulometrycznej, składu fazowego oraz udziału objętościowego dyspersyjnego składnika ceramicznego materiału kompozytowego warstw. Przedstawiono topografię powierzchni warstw niklowych oraz warstw kompozytowych przed i po próbie ścierania. Badania warstw Ni, Ni-P oraz warstw kompozytowych Ni-Si3N4, Ni-P-Si3N4 wykazały, że wbudowanie dyspersyjnej fazy ceramicznej zmniejsza wielokrotnie ich zużycie ścierne.

EN

The paper is aimed on the presentation of results obtained by studies of the abrasion wear of surface layers Ni and Ni-P as well as of composite layers Ni-Si3N4 and Ni-P-Si3N4 produced by the electroless and electrochemical methods on the steel base. Results of granulometric analysis, phase compositions and volumetric rate of the disperse ceramic component of the surface layers before and after abrasion wear examinations are reported. In conclusion, it has been checked that the disperse phase Si3N4 involved into Ni and Ni-P surface layers importantly decreases their abrasion wear.