Evolution of the composition of CaO-Al2O3-SiO2 inclusions during addition of calcium or calcium-silicon into liquid steel

Kalicka Z.

Archives of Metallurgy

2002

Vol. 47, iss. 4

375-383

Basing on the data of Al2O3 and SiO2, thermodynamic activities in SiO2 containing calcium aluminates of three formulae CaO Al2O3 12CaO 7Al2 O3 and 3CaO Al2 O3 , (shortly denoted as C1A1, C12A7 and C3A1), at 1873K for the wide range of SiO2 mole fractions [1], we propose their activities expressed as functions of CaO contents provided there is no change in SiO2 mole fraction. The proposed relations allow to follow the change of the inclusions and steel composition during calcium treatment when calcium or calcium-silicon are added. An evolution of inclusion and steel compositions during calcium treatment was investigated starting from the partly modified inclusions C1A1-SiO2 with (...). It was shown that the change of calcium alurninosilicates composition is slightly different for the pure calcium and calcium-silicon additions. With the calcium treatment the mole fraction of SiO2 in inclusions is decreasing less significant.

Na podstawie danych literaturowych aktywności Al2O3 i SiO2 w glinianach wapnia CaO Al2O3 12CaO 7Al2O3 oraz 3CaO Al2 O3 zawierajacych dodatek Al2O3 w 1873K zaproponowano wyrażenie tych aktywności w funkcji % mas. CaO dla wybranych wartości ułamka molowego SiO2. Umożliwiło to zbadanie zmiany składu wtrąceń glinokrzemianów wapnia oraz równowagowych stężeń pierwiastków w stali przy dodawaniu wapnia lub wapniokrzemu w procesie modyfikacji wtrąceń. Ewolucję składu wtrąceń rozważono zakładając wtrącenia już częściowo zmodyfikowane C1A1 z dodatkiem SiO2 (...). Wykazano, że skład wtrąceń zmienia się nieco inaczej w przypadku dodawania samego wapnia w porównaniu z dodawaniem wapniokrzemu (przy tej samej ilości wprowadzonego wapnia). Spadek zawartości ułamka molowego SiO2 jest mniejszy w przypadku wapniokrzemu.

Assessment of the equilibrium modification of the nonmetallic inclusions containing Al2O3 and SiO2 by use of calcium-silicon

Kalicka Z.

Metallurgy and Foundry Engineering

2001

Vol. 27, no. 1

31-44

The equilibrium between the calcium aluminate inclusions, containing some amounts of silicon dioxide, and the activities of silicon, aluminium, calcium and oxygen in liquid steel at 1873 K were considered. The possibilities of existence in the equilibrium state of various inclusions in steel depending on the concentration of the soluble oxygen and the total aluminium content, as the sum of soluble and insoluble aluminium, were estimated. Assuming the modification of aluminium oxide by calcium-silicon, where the weight ratio of silicon to calcium is about two, amounts of the silicon dioxide appearing in the inclusions after modification were calculated. In the case when silicon, as well as silicon dioxide, was present in steel before the calcium-silicon treatment, the contents of silicon dioxide in the inclusions formed were calculated for different levels of the total silicon contents in steel.

Rozważono równowagę pomiędzy wtrąceniami glinianów wapnia C12A7 i C3A1 zawierającymi rozpuszczony dwutlenek krzemu SiO2 w różnych ilościach, a aktywnością krzemu, glinu, wapnia i tlenu w stali o temperaturze 1873 K. Oceniono możliwość równowagowego istnienia w stali wtrąceń o różnych składach w zależności od zadanego stężenia tlenu rozpuszczonego oraz zawartości glinu całkowitego, będącego sumą glinu rozpuszczonego i związanego. Zakładając, że wtrącenia tlenku glinu modyfikowane są do glinianów wapnia przy użyciu wapniokrzemu, w którym krzemu jest masowo około dwa razy więcej niż wapnia, można zbadać ile jednocześnie wytworzy się dwutlenku krzemu, będącego składnikiem powstałych zmodyfikowanych wtrąceń. W przypadku, gdyby w stali był już krzem, wliczając wtrącenia SiO2, określono jakie składy wtrąceń tlenkowych mogą pojawić się w stali w zależności od zawartości krzemu całkowitego przed dodaniem wapniokrzemu.