Comparative analysis of cyclic properties of 30 HGSA steel under constant-amplitude and incremental step loading.

Mroziński S.

Archive of Mechanical Engineering

|

2006

|

Vol. LIII, nr 2

191-205

EN

The paper there presents the analysis of low-cycle fatigue test results of 30 HGSA alloy steel obtained with the use of two methods. In the standard method, fatigue tests were performed with the use of many specimens, and in the simplified method, the results were defined in an incremental step test using one specimen. Test results were analysed taking into account the influence of loading form on the course of a stabilization process with defined material data. The analysis of the stabilization process in diversified conditions of loading was performed by comparison of the stress amplitude sigma a and strain amplitude epsilon ap for the same levels of total strain amplitude epsilon ac. Basing on the tests, one could state that both methods of defining the cyclic properties lead to qualitatively and quantitatively convergent results. The results exhibit qualitative similarity as far as the character of courses of changes determined in different periods of life of n' and K' parameters of the cyclic strain chart is concerned, and quantitative similarity of the values of determined parameters.

PL

W pracy zamieszczono analizę wyników niskocyklowych badań zmęczeniowych stali stopowej 30HGSA uzyskanych dwiema metodami: metodą standardową polegającą na realizacji prób zmęczeniowych z wykorzystaniem wielu próbek oraz metodą uproszczoną w której wyniki określa się w próbie stopniowego wzrostu przy wykorzystaniu jednej próbki. Wyniki badań analizowano w aspekcie wpływu postaci obciążenia na przebieg procesu stabilizacji oraz na wyznaczone dane materiałowe. Analizę procesu stabilizacji w zróżnicowanych warunkach obciążenia prowadzono porównując amplitudy naprężenia sigma a i amplitudy odkształcenia epsilon ap dla tych samych poziomów amplitudy odkształcenia całkowitego epsilon ac. Na podstawie badań stwierdzono, że obydwie metody określania własności cyklicznych prowadzą do jakościowo i ilościowo zbieżnych wyników. Cechuje je prawdopodobieństwo jakościowe w zakresie charakteru przebiegu zmian wyznaczanych w różnych okresach trwałości parametrów wykresu cyklicznego odkształcenia n' i K' oraz prawdopodobieństwo ilościowe w zakresie wartości wyznaczanych parametrów.

2

Wpływ sekwencji programu obciążenia na przebieg procesu stabilizacji stali 45

Mroziński S.

Zeszyty Naukowe. Mechanika / Akademia Techniczno-Rolnicza w Bydgoszczy

|

2004

|

Z. 54(243)

197-207

PL

W pracy zamieszczono wyniki oraz analizę niskocyklowych badań zmęczeniowych stali 45 w warunkach obciążeń programowanych blokowych o różnej sekwencji poziomów. Podczas badań stosowano cztery typy programów: stopniowo narastające, stopniowo malejące, stopniowo rosnące a następnie malejące oraz obciążenia o nieregularnym następstwie poziomów. Wyniki badań analizowano w aspekcie wpływu postaci programu obciążenia na przebieg procesu stabilizacji. Analizę procesu stabilizacji prowadzono porównując amplitudę naprężenia dla wybranych stopni programu w kolejnych blokach. Analiza porównawcza tego parametru uwidoczniła podobieństwo przebiegu procesu stabilizacji podczas obciążeń programowanych oraz stałoamplitudowych.

EN

Results and low-cycle fatigue tests analysis of 45 steel in conditions of block programmed loading with a different sequence of levels were presented in the paper. During tests four types of programs were applied: gradually increasing, gradually decreasing, gradually increasing and decreasing, and irregular. The sequence of levels in the block loading program was the parameter, which diversified the applied programs. The results of tests were analysed in the aspect of influence of loading program character on the course of the stabilization process. The analysis of the stabilization process was performed by comparing the stress loading amplitude for the chosen levels of the program in the following blocks. The comparative analysis showed similarity of the stabilization processes both under the programmed and the constant - amplitude loading.

3

Własności cykliczne stopowej stali spiekanej po nawęglaniu próżniowym

Kaleta J., Kotowski P., Widanka K.

Zeszyty Naukowe Politechniki Świętokrzyskiej. Mechanika

|

1999

|

Z. 68, t. 1

213--220

PL

W pracy porównano własności cykliczne stopowej stali spiekanej z Cr, Mn i Mo o trzech różnych gęstościach w stanie spiekanym i po obróbce cieplno-chemicznej (nawęglaniu próżniowym). Próbki badano w jednoosiowym stanie naprężenia przy zastosowaniu symetrycznego sinusoidalnego widma obciążenia (R=-1) o częstotliwości f=25 Hz. Widmo obejmowało szeroki zakres obciążeń poczynając od obszaru sprężystego aż do zakresu znacznych odkształceń plastycznych. Wielkością sterującą była amplituda odkształcenia σa. Przeprowadzono badania zarówno przy ustalonym jak i narastającym widmie obciążenia. Do wyznaczania energii ΔW i odkształcenia plastycznego obciążenia εpl zastosowano specjalną metodę dynamicznej pętli histerezy. Metoda pozwoliła na pomiar bardzo małych kątów przesunięcia fazowego ϕ, co jest charakterystyczne dla stali spiekanych. Wykazano, iż zastosowana obróbka cieplno-chemiczna spowodowała wzrost własności wytrzymałościowych oraz spadek własności plastycznych. Zmiany własności były uzależnione silnie od gęstości.

EN

Cyclic properties of the alloyed P/M steel with Cr, Mn and Mo with three different densities, in sintered state and after vacuum carburizing are compared. Specimens were tested in one-directional sinusoidal tension-compression (R=-1, f=25 Hz) over a range of load (step-by-step method). The tests were carried out under stress amplitude control conditions. Special method of measurements of hysteresis loop area ΔW and plastic strain εpl was used. The method remains valid in the range of extremely small angles ϕ up to 1 x 10-4 rad. It was shown that proposed case hardening treatment method results in higher cyclic properties.