Wyniki wyszukiwania - BazTech

1

The B-Li System. Calorimetric and Theoretical Studies

Dębski A., Braga M. H., Gąsior W.

Archives of Metallurgy and Materials

|

2015

|

Vol. 60, iss. 4

2513--2520

EN

The standard enthalpy of formation of the B78Li22 alloy was measured with the use of the water reaction calorimetric method at 25 °C (298 K). An X-ray diffraction study of the prepared sample was conducted. The obtained diffraction pattern was different from the patterns for the B3Li and B14Li3 phases. The standard enthalpy of formation obtained for the B78Li22 alloy was -39.0 ± 0.7 kJ/mole of atoms. This value corresponds well with the formation enthalpies of the phases from the boron-lithium system. Theoretical calculations of the standard enthalpy of formation were conducted for the B78Li22 alloy and the phases from B-Li system, which were investigated earlier. A discussion of the deviations observed between both sets of data (experimental and calculated) was performed. Additionally, DTA studies were performed for 14 alloys of the concentrations from 40 to 100 at. % of Li.

PL

Standardowa entalpia tworzenia stopu B78Li22 została zmierzona metodą kalorymetrii reakcyjnej wodnej. Próbka stopu po wyżarzaniu była poddana badaniom strukturalnym metodą dyfrakcji promieniowania rentgenowskiego. Uzyskany dyfraktogram jest inny od dyfraktogramów dla faz B3Li ora B14Li3. Zmierzona standardowa entalpia tworzenia stopu B78Li22 wyniosła -39.0 ± 0.7 kJ/mol atomów. Wartość ta dobrze koreluje z entalpią tworzenia faz z układu bor-lit. Przeprowadzone zostały również obliczenia teoretyczne standardowej entalpii tworzenia dla stopu B78Li22 oraz faz z układu B-Li, wcześniej badanych. Zaobserwowane rozbieżności między teoretycznymi i eksperymentalnymi wartościami entalpii tworzenia zostały przedyskutowane. Ponadto, wykonano pomiary DTA dla 14 stopów o stężeniach od 40 do 100 % at. Li.

2

Metody analizy termicznej jako uniwersalne narzędzie w przemyśle

Szumera M., Grabowski G., Rutkowski P.

Laboratorium - Przegląd Ogólnopolski

|

2013

|

nr 3-4

64--66

PL

W 2009 roku w Akademii Górniczo-Hutniczej w Krakowie na Wydziale Inżynierii Materiałowej i Ceramiki rozpoczęło działalność Wydziałowe Laboratorium Badań Termofizycznych. Laboratorium wyposażone jest w nowoczesną, zaawansowaną aparaturę do analizy termicznej (TG, DTA-TG, DSC-TG, DIL, LFA), umożliwiającą wykonywanie pomiarów przy narzuconym reżimie temperaturowym oraz w określonej atmosferze gazowej. Pozwala to na dokonywanie charakterystyki badanych materiałów m.in. pod względem ich czystości, polimorfizmu, zmian strukturalnych, stabilności termicznej, procesu starzenia, własności termoplastycznych.

EN

In 2009, at the Academy of Mining and Metallurgy in Krakow, Department of Materials Science and Ceramics Faculty, the Thermophysical Research Laboaratory began its operations. The laboratory is equipped with modern and sophistical equipment for thermal analysis (TG, DTA-TG, DSC-TG, DIL, LFA), allowing for measurements at imposed temperature regime and in particular gas atmosphere. This allows to obtain, among others, the characteristics of the tested materials in terms of purity, polymorphism, structural changes, thermal stability, the aging process, thermoplastic properties.

3

Heat Capacities of Some Binary Intermetallic Compounds in Al-Fe-Ni-Ti System

Onderka B., Sypień A., Wierzbicka-Miernik A., Czeppe T., Zabdyr L. A.

Archives of Metallurgy and Materials

|

2010

|

Vol. 55, iss. 2

435-439

EN

High- and low-temperature Cp measurements were carried out for binary: AlNi3, FeTi and Ni3Ti intermetallic compounds employing various DSC methods and equipment; two different sample preparation techniques were used as well. Low temperature interval ranged from 103 to 623 K, and high temperature range was spread from 313 to 873 K. Results were then fitted to Kelley equation: Cp = a + bźT + cźT-0.5 + dźT-1 + eźT-3 + fźT-2 and Cp vs T curves were presented as graphs.

PL

Przeprowadzono nisko- i wysokotemperaturowe pomiary ciepła właściwego dwuskładnikowych związków międzymetalicznych: AlNi3, FeTi oraz Ni3Ti za pomocą różnych metod i sprzętu różnicowej kalorymetrii skaningowej; zastosowano również dwie różne metody przy-gotowania próbek do badań. Pomiary niskotemperaturowe przeprowadzono w zakresie 103 do 623 K, natomiast zakres pomiarów wysokotemperaturowych leżał w granicach: 313 do 873 K. Wyniki badań opisano równaniem Kelley’a: Cp = a + bźT + cźT-0.5 + dźT-1 + eźT-3 + fźT-2 a krzywe Cp w funkcji temperatury przedstawiono na wykresach.