The effect of natural fillers on the mechanical properties and flammability of low-density polyethylene

Samujło Bronisław

Polimery

|

2023

|

Vol. 68, nr 7-8

396--402

EN

The effect of 10-40 wt% natural fillers (pumpkin husks, bean sorting waste, pine sawdust) on the mechanical properties and flammability of LDPE was examined. As the filler content increased, the hardness slightly increased and the tensile strength and relative elongation decreased. The tensile modulus more than doubled (pumpkin husks, pine sawdust). The linear combustion rate increased unfavorably, but the assumed flammability class HB40 was achieved, except for LDPE filled with 40 wt% pine sawdust (HB75). At the same time, the temperature in the combustion area decreased in the vertical flammability test.

PL

Zbadano wpływ naturalnych napełniaczy (łuski dyni, odpady sortownicze fasoli, trociny sosnowe) stosowanych w ilości 10-40% mas. na właściwości mechaniczne i palność LDPE. Wraz ze wzrostem zawartości napełniacza nieznacznie zwiększała się twardość, a zmniejszała wytrzymałość na rozciąganie i wydłużenie względne. Moduł sprężystości przy rozciąganiu zwiększył się ponad dwukrotnie (łuski dyni, trociny sosnowe). Niekorzystnie wzrosła liniowa szybkość spalania, ale uzyskano zakładaną klasę palności HB40, poza LDPE z dodatkiem 40% mas. trocin sosnowych (HB75). Jednocześnie obniżyła się temperatura w obszarze spalania w pionowym teście palności.

2

Reinforcement of compatibilized nanoclay/Inviya fibers to epoxy‑based glass fiber nanocomposites for high‑impact strength applications

Shelly Daksh, Nanda Tarun, Mehta Rajeev

Archives of Civil and Mechanical Engineering

|

2023

|

Vol. 23, no. 2

art. no. e84, 2023

EN

This research work is the first successful trial in which silanized nanoclay and compatibilized Inviya fibers were reinforced in epoxy-based glass fiber reinforced composites (EGFCs) resulting in significant improvements in impact strength without degrading tensile properties. Vacuum assisted resin infusion moulding (VARIM) technique was used for processing of multi-scale filler reinforced EGFCs. Inviya fibers were used, because of their high ‘elastic recovery’ and ‘stretchability’ (five times the original length) due to alternative flexible and rigid molecular structure. Nanoclay and Inviya fibers were subjected to compatibilization with different surface treatments. Compatibilization of fillers was confirmed through Fourier transform infrared spectroscopy (FTIR) and Field emission scanning electron microscopy-Energy-dispersive spectroscopy (FE-SEM/EDS) analysis. Nanoclay dispersion and morphology in EGFCs was ascertained through X-ray diffraction (XRD) and Transmission electron microscopy (TEM) analysis. Reinforcement of compatibilized Inviya fibres (First Method: maleic anhydride grafting, and Second Method: combination of phosphoric acid treatment followed by silanization) enhanced the impact strength by 132% and 150%, respectively, over the reference composition. FE-SEM micrographs of fracture surface of impact test specimens were utilized to identify the mechanisms causing improvement in impact behaviour.

3

The effect of basalt knitted fabric on the properties of green epoxy resin

Jamshaid Hafsa, Rajput Abdul Waqar, Zahid Bilal, Memon Sanam, Qureshi Raja Fahad, Aslam Sarmad, Nadeem Muhammad

Polimery

|

2022

|

Vol. 67, nr 2

67--71

EN

The influence of basalt fabric on the tensile mechanical properties and the impact resistance of green epoxy resin was investigated. Composites with parallel arrangement of insert yarns had better properties than in the case of their perpendicular arrangement. The properties were also influenced by the number of layers of the fabric. The tensile strength and impact resistance of the composites were better than the commercially available side mirror covers due to the superior properties of the basalt fiber.

PL

Zbadano wpływ tkaniny bazaltowej na właściwości mechaniczne przy rozciąganiu i odporność na uderzenie „zielonej” żywicy epoksydowej. Kompozyty o równoległym ułożeniu przędzy charakteryzowały się lepszymi właściwościami niż te o prostopadłym ułożeniu. Na właściwości miała również wpływ liczba warstw tkaniny. Wytrzymałość na rozciąganie i odporność na uderzenie kompozytów były lepsze niż dostępnych na rynku osłon lusterek bocznych ze względu na dobre właściwości włókna bazaltowego.

4

Effect of heat treatment on the tensile properties of incrementally processed modified polylactide

Kozik Bogdan, Dębski Mariusz, Bąk Piotr, Gontarz Małgorzata, Zaborniak Małgorzata

Polimery

|

2021

|

T. 66, nr 6

357--361

EN

The influence of temperature (80, 95 and 110°C) and annealing time (20, 25, 30 min) on the tensile strength and elongation at break of the modified polylactide (PLA Pro) processed by 3D printing (FFF – Fused Filament Fabrication) was investigated. The properties of PLA Pro were compared with properties of unmodified PLA and ABS. It was observed that the tensile strength was comparable for all annealed samples and was about 45 MPa. Moreover, the annealing process decreased the tensile strength of the modified PLA and increased the elongation at break, which may be related to a change in the degree of crystallinity. The modified PLA was characterized by tensile properties similar to ABS.

PL

Zbadano wpływ temperatury (80, 95 i 110°C) i czasu wygrzewania (20, 25, 30 min) na wytrzymałość na rozciąganie i wydłużenie względne przy zerwaniu modyfikowanego polilaktydu (PLA Pro) przetwarzanego metodą druku 3D (FFF – Fused Filament Fabrication). Właściwości PLA Pro porównano z właściwościami niemodyfikowanego PLA i ABS. Zaobserwowano, że wytrzymałość na rozciąganie była porównywalna dla wszystkich próbek i wynosiła około 45 MPa. Ponadto, proces wygrzewania spowodował zmniejszenie wytrzymałości na rozciąganie modyfikowanego PLA i zwiększył wydłużenie przy zerwaniu, co może być związane ze zmianą stopnia krystaliczności. Modyfikowany PLA charakteryzował się właściwościami mechanicznymi przy rozciąganiu podobnymi do ABS.

5

Measurement of the Uniformity of Thermally Bonded Points in Polypropylene Spunbonded Non-Wovens Using Image Processing and its Relationship With Their Tensile Properties

Emadi M., Tavanaie M. A., Payvandy P.

Autex Research Journal

|

2018

|

Vol. 18, no. 4

405--418

EN

This article aims at the image processing of surface uniformity and thermally bonded points uniformity in polypropylene spunbonded non-wovens. The investigated samples were at two different weights and three levels of non-uniformity. An image processing method based on the k-means clustering algorithm was applied to produce clustered images. The best clustering procedure was selected by using the lowest Davies-Bouldin index. The peak signal-to-noise ratio (PSNR) image quality evaluation method was used to choose the best binary image. Then, the non-woven surface uniformity was calculated using the quadrant method. The uniformity of thermally bonded points was calculated through an image processing method based on morphological operators. The relationships between the numerical outcomes and the empirical results of tensile tests were investigated. The results of image processing and tensile behavior showed that the surface uniformity and the uniformity of thermally bonded points have great impacts on tensile properties at the selected weights and non-uniformity levels. Thus, a sample with a higher level of uniformity and, consequently, more regular bonding points with further bonding percentage depicts the best tensile properties.

6

Surface and Structural Damage to PLA Fibres during Textile Pretreatments

Baig G. A., Carr C. M.

Fibres & Textiles in Eastern Europe

|

2016

|

Vol. 24, no. 2 (116)

52--58

EN

PLA knitted fabric was treated with sodium carbonate in the presence of non-ionic detergent at various concentrations and temperatures in a short liquor bath. The scoured fabric was subsequently treated with industrially important bleaching agents such as hydrogen peroxide, sodium chlorite and sodium hypochlorite at various levels of concentration and pH. The bleached PLA fabric was then evaluated in terms of surface and bulk properties. The structural damage was assessed in terms of tensile strength, while the surface morphology was investigated using scanning electron microscopy (SEM). The surface chemistry of PLA was studied using infra-red (IR) and x-ray photoelectron spectroscopies (XPS). The alkaline-oxidative conditions were deleterious to the integrity of PLA polymer at high temperature, while at low temperature there was a little damage. The acidic-oxidative conditions did not appreciably affect bulk or surface properties even at high temperature.

PL

Dzianiny wykonane z PLA poddano obróbce węglanem sodu w obecności niejonowych detergentów przy rożnych stężeniach i temperaturach. Dzianiny były równocześnie poddane działaniu przemysłowo ważnych środków bielących, takich jak: nadtlenek wodoru, chloryn sodu i podchloryn sodu przy rożnych poziomach stężenia i pH. Bielone dzianiny PLA były następnie oceniane biorąc pod uwagę właściwości powierzchni i wnętrza. Strukturalne uszkodzenia wewnętrzne były oceniane poprzez wytrzymałość na rozciąganie, podczas gdy morfologię powierzchni badano za pomocą SEM. Powierzchnie dzianin PLA badano również stosując spektrofotometrie IR i XPS. Działanie środków alkalicznych i utleniających miało wpływ uszkadzający na integralność polimeru PLA przy wyższych temperaturach, podczas gdy przy niskich temperaturach uszkodzenia były niewielkie.

7

Influence of the structures of polyamide 6 fibers on their ageing under intensive insolation conditions

Bieniek A., Lipp-Symonowicz B., Sztajnowski S.

Polimery

|

2009

|

T. 54, nr 11-12

840-844

EN

The effects of large doses of UV radiation, relating to actual operational use during 1, 2 or 5 summer seasons, on changes of chemical structures, crystalline structures, morphology and tensile properties of four types of polyamide 6 were investigated. The fibers differed in cross-section shape and mat degree caused by TiO2 addition. The fibers were tested using, among others, SEM and IR methods. Critical dissolution time (CDT) was also investigated.

PL

Zbadano wpływ naświetlania dużymi dawkami promieniowania UV (odpowiadającego rzeczywistemu użytkowaniu w ciągu 1, 2 lub 5 sezonów letnich) na zmiany budowy chemicznej, charakteru struktury krystalicznej (tabela 4) i morfologii oraz właściwości mechanicznych przy rozciąganiu (tabela 5) czterech rodzajów włókien z poliamidu 6 różniących się kształtem przekroju oraz - spowodowanym dodatkiem TiO2 - stopniem zmętnienia (tabela 1). Posługiwano się przy tym metodami SEM (rys. 1-4) i IR (tabela 2) a także pomiarem krytycznego czasu rozpuszczania (CDT, tabela 3).

8

Crosslinking of binary blends of ethylene/vinyl acetate copolymer and low density polyethylene or metallocene polyolefin elastomer as heat-shrinkable materials

Kudła S.

Polimery

|

2009

|

T. 54, nr 1

3-7

EN

The results of investigation of selected properties of peroxide crosslinked binary blends of ethylene/vinyl acetate copolymer and low density polyethylene or metallocene polyolefin elastomer as candidates for production of heat-shrinkable materials were presented. Analytical methods used - i.e. gel content, hot set test and rheometric investigations - as the measures of crosslinking degree, oxidation induction time and tensile properties measurements, before and after accelerated degradation, proved that the tested recipes were good starting points for further technological work. Some aspects of analytical determination of crosslinking degree are discussed.

PL

Przedstawiono wyniki badań o charakterze technologicznym, prowadzonych w celu opracowania receptur materiałów przeznaczonych do produkcji wyrobów termokurczliwych. Jako podstawowy komponent polimerowy stosowano dwuskładnikowe mieszaniny, w których użyto kopolimeru etylen/octan winylu oraz polietylenu małej gęstości bądź elastomerycznego kopolimeru etylen/okten; ponadto, badane układy zawierały stabilizatory termiczne oraz napełniacz nieorganiczny (wodorotlenek magnezowy bądź glinowy) (tabela 1). Ocenę produktów opierano na wynikach badań ich następujących właściwości: stopnia usieciowania trzema metodami (liczba żelowa, pomiar wydłużenia trwałego w podwyższonej temperaturze, pomiary reometryczne), charakterystyki wytrzymałościowej przy rozciąganiu oraz odporności termooksydacyjnej (tabele 1-3, rys. 1). Podkreślono przy tym, że wnioskowanie o stopniu usieciowania na podstawie pomiaru jedynie liczby żelowej jest dalece niewystarczające. Stwierdzono korzystny wpływ wprowadzenia kopolimeru etylen/octan winylu na osiągnięty maksymalny stopień usieciowania.

9

Budowa chemiczna i właściwości fizyczne usieciowanych poliuretanów segmentowych

Janik H., Balas A.

Polimery

|

2009

|

T. 54, nr 3

195-201

PL

Przedmiotem badań były poliuretany (PUR) segmentowe otrzymywane w dwuetapowej syntezie oligomerycznego ...-dihydroksy(adypinianu etylenowo-butylenowego) oraz dwóch różnych aromatycznych diizocyjanianów: 4,4'-diizocyjanianu difenylenometanu (MDI) albo MDI modyfikowanego diizocyjanianem karbodiimidu. Na etapie przedłużania łańcucha, oprócz typowo używanego do tego celu 1,4-butanodiolu, stosowano sieciujący triol - 1,3-dihydroksy-2-(hydroksymetyleno)propan (TMP). Budowę chemiczną otrzymanych PUR scharakteryzowano metodą IR. Określono wpływ składu PUR (rodzaj diizocyjanianu a także stosunek diol/triol w układzie sieciującym i jego ilość) na ich pęcznienie równowagowe w dimetyloformamidzie oraz właściwości mechaniczne. Wyniki przedyskutowano z punktu widzenia specyfiki struktury powstającej sieci.

EN

Segmental polyurethanes (PUR) obtained in two-stage syntheses from oligomeric ?,?-dihydroxy(ethylene-butylene adipate) and two different aromatic diisocyanates: diphenylmethane 4,4'-diisocyanate (MDI) or MDI modified with carbodiimide diisocyanate were the subjects of investigations. For chain extending the curing triol 1,3-dihydroxy-2-(hydroxymethylene)propane (TMP) was used, besides typical 1,4-butanediol (Table 1). The chemical structures of PUR obtained were characterized by IR method (Table 4, Fig. 1). The effects of PUR compositions (type of diisocyanate, diol/triol ratio in the curing system and its amount) on the equilibrium swelling in dimethylformamide (Table 2 and 3) as well as mechanical properties (Table 5) were determined. The results were discussed from the point of view of peculiarity of structure of the network forming.