The effect of firing temperature on colour and structural properties of malayaites with Cr

Luxová J., Havlík M. R., Sulcová P.

Materiały Ceramiczne

|

2016

|

T. 68, nr 3

193--198

EN

Malayaites are calcium tin silicate compounds derived from natural occurring mineral the malayaite which has the chemical formula CaSnSiO5. Malayaites are characterized by monoclinic crystal structure consisting of chains of distorted SnO6 octahedra connected with tops of SiO4 tetrahedra, forming a framework containing chains of CaO7 polyhedra. This incurred structure is then stable for bond of metal ion and takes part in the final pigment colouring. In this contribution the compounds with the chemical formula of Ca(SnCr)SiO5±δ (molar ratio of Cr/Sn = 0.015) were prepared. For the synthesis the classical ceramic method was used, i.e. procedures of calcination in an electric furnace at the temperatures 1200-1500 °C for 4 h (one-step calcination) and multiple calcination (two-step calcination) for obtaining products with higher quality. Therefore, the objective of this work was to compare samples which were prepared by the one-step and also two-step calcination procedures. The two-step calcination procedure was carried out at two temperatures, during which the first calcination was always held at 1100 °C for 4 hours. The second calcination was performed for 4 h at an appropriate temperature from the range 1200-1500 °C. The colour properties were studied by a spectrophotometer ColorQuest XE (HunterLab, USA). The colour moved from pink to burgundy in dependence on temperature of calcination. The phase composition of tested compounds was verified by using X-ray diffraction analysis with using a diffractometer D8 Advance (Bruker, GB). A particle size distribution of heat treatment samples was measured by Mastersizer 2000/MU (Malvern Instruments, Ltd., GB). The signal was evaluated on the basis of Fraunhofer bending. Thermal stability was investigated by heating microscope EM201-12 (Hesse-Instruments, Germany).

PL

Malayaity to związki krzemianowe wapnia i cyny otrzymane z naturalnie występującego minerału malayaitu o wzorze chemicznym CaSnSiO5. Malayaity mają jednoskośną strukturę krystaliczną składającą się z łańcuchów zniekształconych oktaerów SnO6 połączonych z wierzchołkami tetraedrów SiO4, tworząc szkielet zawierający łańcuchy wielościanów CaO7. Struktura ta stabilnie wiąże jony metalu i bierze udział w ostatecznym barwieniu pigmentu. W tym przyczynku przygotowano związki o wzorze chemicznym Ca(SnCr)SiO5±δ i stosunku molowym Cr/Sn = 0,015. Do syntezy wykorzystano metodę klasyczną, tzn. procedury prażenia w piecu elektrycznym przez 4 h w temperaturach 1200-1500 °C (kalcynacja jednoetapowa) i prażenia wielokrotnego (dwuetapowa kalcynacja) w celu otrzymania produktów o wyższej jakości. Dlatego, celem tej pracy było porównanie próbek, które przygotowano za pomocą procedur kalcynacji jedno- i dwuetapowej. Procedura dwuetapowa zaostała przeprowadzona w dwóch temperaturach, w jej trakcie pierwsza temperatura prażenia była zawsze utrzymywana w 1100 °C przez 4 h; drugie prażenie miało miejsce w odpowiedniej temperaturze z przedziału 1200-1500 °C i trwało przez 4 h. Właściwości barwne badano za pomocą spektrofotometru ColorQuest XE (HunterLab, USA). Barwa przesunęła się od różowej do burgundu w zależności od temperatury prażenia. Skład fazowy badanych związków weryfikowano z użyciem dyfrakcyjnej analizy rentgenowskiej, stosując dyfraktometr D8 Advance (Bruker, GB). Rozkład wielkości cząstek zmierzono za pomocą analizatora Mastersizer 2000/MU (Malvern Instruments, Ltd., GB). Sygnał opracowano na podstawie przybliżenia Fraunhofera. Stabilność termiczną badano z użyciem mikroskopu EM201-12 (Hesse-Instruments, Germany).

2

Synthesis and characterization of the Bi2Ce2-xZrxO7 pigments

Tesitelova K., Sulcová P., Kolackova I.

Materiały Ceramiczne

|

2016

|

T. 68, nr 3

204--207

EN

This contribution is focused on the synthesis, characterization and optical properties of new inorganic pigments, being environment-friendly and enable to substitute some toxic metals in interesting colour compounds. The pigments were prepared by the solid-state reaction. The colour properties of prepared applications were investigated depending on the content of Zr and temperature of calcination (800-1000 °C after step 50 °C). The optimum conditions for the pigments synthesis were determined. The pigments were evaluated from the standpoint of their particle sizes. Characterization of Bi2Ce2-xZrxO7 pigments (x = 0 to 2 after step 0.25) suggests that they have a potential to be alternative yellow or orange colourants for paints, plastics, ceramics and building materials.

PL

Praca skupia się na syntezie, charakterystyce i właściwościach optycznych nowych, nieorganicznych pigmentów, przyjaznych środowisku naturalnemu i umożliwiających zastąpienie metali toksycznych interesującymi związkami barwnymi. Pigmenty przygotowano za pomocą reakcji w fazie stałej. Właściwości barwne przygotowanych substancji badano w zależności od zawartości Zr i temperatury kalcynacji (800-1000 °C z krokiem 50 °C). Określono optymalne warunki syntezy pigmentów. Pigmenty oceniono w odniesieniu do rozmiaru ich ziarna. Charakterystyki pigmentów Bi2Ce2-xZrxO7 (x = 0 to 2 z krokiem 0,25) wskazują, że mają one potencjał żółtego lub pomarańczowego barwnika do farb, plastyków, ceramiki i materiałów budowlanych.

3

Study of ceramic pigments with perovskite structure

Dohnalová Ż., Sulcová P., Gorodylova N.

Materiały Ceramiczne

|

2016

|

T. 68, nr 3

188--192

EN

Our attention was focused on preparation of inorganic pigments based on the perovskite structure of SrSnO3, in which part of tin ions was substituted by ions of terbium and titanium or terbium and cerium. The particle size (d50) of all pigments is between 2-3 μm. Powders with the general formula SrSn0.6-xTixTb0.4O3, where x = 0.1-0.6, provide an intensive yellow colour hue in application into an organic binder, and white glossy surfaces in application into a ceramic glaze. A SrSn0.4Ti0.2Tb0.4O3 sample offers the best colour parameters in application into the organic binder: the highest amount of yellow hue (b* = 58.95) and the highest saturation (C = 59.05). Powders with the general formula SrSn0.6-xCexTb0.4O3, where x = 0.1-0.6, also provide an intensive yellow colour hue in application into the organic binder and dark yellow-orange glossy surfaces in application into the ceramic glaze. The most interesting yellow colour hue has powder SrSn0.4Ce0.2Tb0.4O3 applied into the organic binder. In application into the ceramic glaze, an increase of cerium ions content in pigment shifts the hue from yellow to dark orange.

PL

Uwagę skupiono na przygotowaniu nieorganicznych pigmentów opartych na perowskitowej strukturze SrSnO3, w której część jonów cyny podstawiono jonami terbu i tytanu lub terbu i ceru. Rozmiar cząstek (d50) wszystkich pigmentów mieścił sie pomiędzy 2-3 μm. Proszki o wzorze ogólnym SrSn0.6-xTixTb0.4O3, gdzie x = 0.1-0.6, dostarczają intensywny odcień koloru żółtego w zastosowaniu do spoiwa organicznego i białe połyskujące powierzchnie w zastosowaniu do szkliwa ceramicznego. Próbka SrSn0.4Ti0.2Tb0.4O3 oferuje najlepsze parametr barwne w zastosowaniu do spoiwa organicznego: największy udział odcienia żółtego (b* = 58.95) i największe nasycenie (C = 59.05). Proszki o wzorze ogólnym SrSn0.6-xCexTb0.4O3, gdzie x = 0.1-0.6, również dostarczają intensywny odcień koloru żółtego w zastosowaniu do spoiwa organicznego i ciemne żółto-pomarańczowe powierzchnie w zastosowaniu do szkliwa ceramicznego. Najbardziej interesujący odcień koloru żółtego ma proszek SrSn0.4Ce0.2Tb0.4O3 zastosowany do spoiwa organicznego. W zastosowaniu do szkliwa ceramicznego wzrost stężenia jonów ceru w pigmencie przesuwa odcień żółty do ciemnopomarańczowego.

4

Colour properties of pigments based on YMnO3

Burkovicova A., Dohnalova Z., Sulcova P.

Materiały Ceramiczne

|

2015

|

T. 67, nr 1

9--14

EN

Inorganic pigments of the YMnx(CuSn)1-xO3±δ (CuSn) and YMnx(NiSn)1-xO3±δ (NiSn) type, where x = 0.9, 0.5, 0.1, were prepared by wet mechanical activation. Influence of composition and calcination temperature on the colour properties, particle size distribution and phase purity was examined. The pigments were applied into a ceramic glaze and organic matrix. With the calcination temperature increasing from 1000 °C to 1200 °C and with the decreasing content of Mn, the colour of the pigment powders changed from black to dark green in case of CuSn and from black to dark brown in case of NiSn. Particle size distributions (PSD) of the prepared powders varied in the interval suitable for pigment applications. A complete solid solution (hexagonal YMnO3) was obtained only in the case of YMn0.9(CuSn)0.1O3±δ. The effect of mineralizers (AlF3, Na3AlF6, H3BO3, Na2CO3) on the colour properties and phase composition was also investigated. The prepared powders were compared with the industrially produced pigments.

PL

Wykorzystując aktywację mechaniczną na mokro, przygotowano nieorganiczne pigmenty typu YMnx(CuSn)1-xO3±δ (CuSn) i YMnx(NiSn)1-xO3±δ (NiSn), gdzie x = 0,9, 0,5, 0,1. Zbadano wpływ składu i temperatury kalcynacji na właściwości barwne, rozkład wielkości cząstek i czystość fazową. Pigmenty zastosowano w szkliwie ceramicznym i osnowie organicznej. Wraz ze zwiększaniem temperatury kalcynacji od 1000 °C do 1200 °C i zmniejszaniem zawartości Mn, barwa proszków zmieniała się od czarnej do ciemnozielonej w przypadku pigmentów CuSn i od czarnej do ciemnobrązowej w przypadku pigmentów NiSn. Rozkłady wielkości cząstek (PSD) przygotowanych proszków zmieniały się w zakresie odpowiednim do zastosowania w roli pigmentów. Tylko w przypadku YMn0,9(CuSn)0,1O3±δ otrzymano Wyłącznie roztwór stały (heksagonalny YMnO3). Zbadano również wpływ mineralizatorów (AlF3, Na3AlF6, H3BO3, Na2CO3) na właściwości barwne i skład fazowy. Przygotowane proszki porównano z przemysłowo wytwarzanymi pigmentami.

5

The effect of lanthanides on colour properties of the Ln2Zr1.5V0.5O7 pigments

Bukovska L., Sulcova P., Vondrasek M.

Materiały Ceramiczne

|

2011

|

T. 63, nr 2

244-247

EN

New yellow and orange ceramic pigments based on the pyrochlore solid solution of Ln2Zr1.5V0.5O7 were synthesized as high-temperature environment friendly inorganic materials. This work is focused on mixed oxides based on ZrO2, which are doped by rare earth elements. The optimum conditions for their synthesis were determined. Their colour properties were investigated depending on the content of various lanthanides and temperature of calcination. The richest hues were obtained by using holmium and thulium. All pigments give the yellow colour in ceramic glazes but Ho and Er provide orange hues. The pigments were evaluated from the standpoint of their structure, colour, ability to colour ceramic glaze, and particle size.

PL

Zsyntezowano nowe pigmenty, żółte i pomarańczowe, oparte na roztworze stałym Ln2Zr1.5V0.5O7 typy pirochloru jako nieorganiczne wysokotemperaturowe materiały przyjazne dla środowiska. W pracy skupiono się na tlenkach mieszanych ZrO2 domieszkowanego pierwiastkami ziem rzadkich. Określono optymalne warunki syntezy tych związków. Ich właściwości barwne badano w zależności od zawartości lantanowców i temperatury kalcynacji. Najbogatsze odcienie uzyskano przy użyciu tlenków holmu i tulu. Wszystkie pigmenty dają kolor żółty w szkliwach ceramicznych, ale Ho i Er dostarczają odcieni pomarańczowych. Pigmenty oceniono z punktu widzenia ich struktury, barwy, zdolności do barwienia szkliwa ceramicznego oraz wielkości cząstek.

6

Study of compounds based on SrMxSn1-xO3šx/2

Adolfova L., Sulcova P., Dohnalova Z., Trojan M.

Materiały Ceramiczne

|

2011

|

T. 63, nr 2

248-250

EN

Inorganic pigments of SrMxSn1-xO3šx/2 type (where M = V, Cr), based on a pseudo cubic structure of SrSnO3, have been prepared by the solid state reaction between SrCO3, SnO2 and oxides V2O5 or Cr2O3 in the temperature range 1300-1500°C with nominal compositions: x = 0.05, 0.1, 0.3. The resultant materials were characterised by XRD, TG-DTA, and colourimetric techniques were used. The pigments containing vanadium as chromophore give creamy, sand and yellow colour into an organic matrix. The increase of temperature caused the creation of pigments with deeper and brighter colour hue. The presence of chromium in compounds produces colour hues from reddish brown to brown. The compounds with higher content of chromium have the lower chroma colour hue.

PL

Pigmenty nieorganiczne typu SrMxSn1-xO3šx/2 (gdzie M = V, Cr), oparte na pseudo-regularnej strukturze SrSnO3, o nominalnym składzie: x = 0,05, 0,1, 0,3, zostały przygotowane za pomocą reakcji w stanie stałym pomiędzy SrCO3, SnO2 i tlenkami V2O5 lub Cr2O3 w zakresie temperatury 1300–1500°C. Otrzymane materiały scharakteryzowano za pomocą metod XRD, TG-DTA, wykorzystano też technikę kolorymetryczną. Pigmenty zawierające wanad jako chromofor dają w organicznej matrycy kolory śmietankowy, piaskowy i żółty. Wzrost temperatury spowodował powstanie pigmentów o głębszym i jaśniejszym odcieniu. Obecność chromu w związkach wywoływała odcienie od brązowo-czerwonawego do brązowego. Związki z wyższą zawartością chromu miały odcień o mniejszym nasyceniu barwy.

7

Influence of preparation methods on colourfulness of Ce1-(x+y)TbxTiyO2

Strnadlova L., Sulcova P., Vecera J.

Materiały Ceramiczne

|

2011

|

T. 63, nr 2

239-243

EN

Compounds based on CeO2 were synthesized as high-temperature environment-friendly inorganic pigments with interesting hues. The pigments have been prepared by using the solid state reaction and suspension mixing of raw materials. The goal was to develop conditions for the synthesis of this type of pigments and to determine the influence of preparation methods on the colouring effects of these compounds. The colour properties were investigated depending on the method of preparation, calcination temperature and concentration of Ti4+ ions. All prepared pigments were applied into organic matrix and ceramic glaze. The pigments were evaluated from the standpoint of their structure, colour properties and particle sizes. Our results indicated that these compounds can provide light orange colour hues that are stable in ceramic glazes and dark brown colour shades in the organic matrix.

PL

Związki oparte na CeO2 zsyntezowano jako wysokotemperaturowe, przyjazne dla środowiska, nieorganiczne pigmenty o interesujących barwach. Pigmenty wytworzono wykorzystując reakcję w fazie stałej oraz mieszanie surowców w zawiesinie. Celem było opracowanie warunków syntezy tego typu pigmentów i określenie wpływu metody preparatyki na efekty barwne otrzymanych związków. Właściwości barwne zbadano w zależności od zastosowanej metody wytwarzania, temperatury kalcynacji i stężenia jonów Ti4+. Pigmenty oceniano po względem ich struktury, barwy i rozmiaru cząstek. Uzyskane wyniki wskazały, że otrzymane związki mogą dostarczać odcieni jasnopomarańczowych, które są trwałe w szkliwach ceramicznych, oraz odcieni ciemnego brązu w osnowie organicznej.

8

New arylhydrazonothiazolidin-5-one disperse dyes for dyeing polyester fibers

Metwally M.A., Khalifa M.E., Attia E.A., Amer F.A.

Polish Journal of Chemical Technology

|

2010

|

Vol. 12, nr 1

1-6

EN

A series of new thiazolidin-5-one disperse dyes was synthesized from the reactions of 2-substituted 3-phenylthiazolidinones with various aryldiazonium chlorides. The synthesized dyes were characterized by UV-visible absorption, IR, NMR and MS spectroscopy. The dyes gave orange to reddish-violet shades with very good depth on polyester fibers. The dyed fabrics show moderate to good fastness to light and very good to excellent fastness to washing and perspiration. Also, the assessment of color coordinates was discussed.

9

Mechaniczne i optyczne właściwości dekoracyjnych warstw azotków i węglikoazotków tytanu wytwarzanych metodą Arc-PVD.

Kula P., Januszewicz B.

Inżynieria Materiałowa

|

2002

|

R. XXIII, nr 5

698-706

PL

W niniejszej pracy przedstawiono wyniki badań właściwości mechanicznych oraz optycznych twardych warstw, o charakterze dekoracyjnym, węglików i węglikoazotków tytanu nanoszonych na podłoża stalowe metodą Arc-PVD. Przedstawiono także wyniki prób wykorzystania skanera komputerowego jako urządzenia do szybkiego jakościowego badania właściwości barwnych wytworzonych powłok.

EN

The results of researches on mechanical and optical properties of hard, decorative titanium nitride and carbonitride layers deposited onto steel substrates by means of Arc-PVD method are shown in this paper. The results of an attempt of scanner use as a device for quick, qualitative measurement of colour properties of deposited layers are also presented in this paper.