Compressive properties of cell structures manufactured by photo-curing technology liquid polymer resins - Polyjet Matrix

Rudnik Mateusz

Mechanik

2022

R. 95, nr 1

12--14

The article presents the results of compressive strength tests of cylindrical samples with a hexagonal cell structure. The samples were made of MED 610 material using the photo-curing technology liquid polymer resins. The compressive strength was estimated on the basis of a static compression test of the printed elements. It has been shown that the PolyJet Matrix 3D printing technology enables the printing models with a thin-walled cell structure, which, while maintaining the appropriate strength properties, can be used in the design and production of certain utility models.

Przedstawiono wyniki badań wytrzymałości na ściskanie próbek cylindrycznych o heksagonalnej strukturze komórkowej. Próbki wykonano z materiału MED 610 z zastosowaniem techniki fotoutwardzania ciekłych żywic polimerowych. Wytrzymałość na ściskanie oszacowano na podstawie statycznego testu ściskania elementów drukowanych. Wykazano, że technologia druku PolyJet Matrix 3D umożliwia drukowanie modeli o cienkościennej strukturze komórkowej, co - pod warunkiem zachowania odpowiednich właściwości wytrzymałościowych - może być wykorzystane przy projektowaniu i produkcji niektórych wzorów użytkowych.

Mechanical properties and abrasive wear behaviors of in situ nano-TiCx/Al–Zn–Mg–Cu composites fabricated by combustion synthesis and hot press consolidation

Gao Y. Y., Qiu F., Shu S. L., Wang L., Chang F., Hu W., Han X., Li Q., Jiang Q. C.

Archives of Civil and Mechanical Engineering

2018

Vol. 18, no. 1

179--187

The in situ nano-TiCx/Al–Zn–Mg–Cu composites with different TiCx content (20, 25 and 30 vol.%) were successfully fabricated by combustion synthesis and hot press consolidation in Al–Ti–C/CNTs systems. The compressive properties and abrasive wear resistance of the composites improved with the increase in the TiCx content. The transformation of carbon source from pure C black to the mixture of C black and CNTs to pure CNTs in Al–Ti–C/CNTs systems leaded to a significant improvement in the compressive properties and wear resistance of the composites as well as a significant decrease in the average size of TiCx particles. The average size of the nano-TiCx particles in 30 vol.% TiCx/Al–Zn–Mg–Cu composite synthesized by the carbon source of CNTs reached 81 nm, moreover, the yield strength (σ0.2), the ultimate compression strength (σUCS) and the fracture strain (ɛf) of the composite reached 597 MPa, 882 MPa and 21.7%, respectively.