Modification of polyamide 6 fibers with water-glass in the bath method

Gawłowski A., Fabia J., Ślusarczyk C., Brzozowska-Stanuch A., Graczyk T., Janicki J.

Polimery

2017

T. 62, nr 11-12

861--867

High temperature (HT) bath method was used to produce the flame-retardant polyamide 6 (PA6) fibers, analogous to dyeing using dispersed dyes. The modification process was carried out in a bath containing flame-retardant and a surfactant (dispersant). An ecological commercial product – so-called soda water-glass, i.e., aqueous sodium silicate solution (WG) – was used as flame-retardant. The resulting flame-retardant effect was evaluated on the basis of the limiting oxygen index (LOI) method. The thermal properties of the examined fibers were determined using differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). Basic mechanical testing of fibers was also performed. Fiber burning residues were characterized on the basis of photographs obtained by scanning electron microscopy (SEM). Changes in the supermolecular structure of PA6 fibers after the modification were discussed using wide-angle X-ray scattering (WAXS). As a result of the proposed modification of PA6 fibers a small but sustained increase in the flame-retardant effect was obtained.

Włókna z poliamidu 6 (PA6) o zmniejszonej palności wytworzono z zastosowaniem metody kąpielowej HT (high temperature), prowadzonej w sposób analogiczny do barwienia włókien barwnikami zawiesinowymi. Kąpiel modyfikująca zawierała uniepalniacz oraz środek powierzchniowo czynny (dyspergator). Środkiem uniepalniającym był ekologiczny produkt handlowy o nazwie szkło wodne sodowe – wodny roztwór krzemianu sodu (WG). Uzyskany efekt trudnozapalności oceniano na podstawie wyznaczonego indeksu tlenowego (LOI). Właściwości termiczne badanych włókien określano za pomocą różnicowej kalorymetrii skaningowej (DSC) i analizy termograwimetrycznej (TGA). Wykonano też podstawowe badania wytrzymałości mechanicznej włókien. Pozostałości po spaleniu włókien charakteryzowano na podstawie fotografii uzyskanych techniką elektronowej mikroskopii skaningowej (SEM). Zmiany w strukturze nadcząsteczkowej włókien PA6 poddanych modyfikacji oceniano z wykorzystaniem szerokokątowej dyfraktometrii rentgenowskiej (WAXS). W wyniku zaproponowanej modyfikacji uzyskano niewielkie, ale trwałe zmniejszenie palności włókien PA6.

Mechanical Properties of PA 6 Fibres Modified with Copolyamides and Nanoclays

Kristofič M, Ujhelyiová A, Vassová I, Michlík P, Brejka O, Ryba J

Fibres & Textiles in Eastern Europe

2011

Vol. 19, no. 4 (87)

41—45

This contribution deals with the preparation of concentrates consisting of copolyamides from ε-caprolactam and nylon salts prepared from adipic acid and 1-(2-aminoethyl) piperazine, and from adipic acid and diethylenetriamine, as well as the evaluation of their basic properties. PA 6 fibres modified with 5, 10 and 20 wt. % of these concentrates were prepared by two drawing processes, and their mechanical properties,( tensile strength, Young modulus and elongation at break) and orientation factors were evaluated. With respect to their thermal properties, all the concentrates are more or less semicrystalline compounds suitable as additives for semicrystalline PA 6 fibres. Mechanical properties depend on the type of concentrate and conditions of the drawing process. A lower amount of concentrate in modified fibres and concentrates with a lower amount of comonomers in copolyamide, Cloisite nanoadditive, a lower speed of drawing and an optimal drawing ratio assure the same or better mechanical properties, mainly the tensile strength, in comparison with non modified PA 6 fibres.

Opisano sporządzanie koncentratów opartych na poliamidzie otrzymanym z ε-kaprolaktamu i kwasu nylonowego oraz 1-(2-aminoetylenu) piperazyny, kwasu adypinowego i dietylenotriaminy oraz badano ich właściwości. Wyprzędziono przy zróżnicowanym rozciagu włókna poliamidowe z udziałm 5, 10 i 20% wyżej wspomnianego koncentratu a nastęnie okreśono ich włściwości mechaniczne (wytrzymałść właściwą wydłżenie przy zerwaniu, moduł oraz współczynnik orientacji. Wszystkie koncentraty są mniej lub bardziej krystaliczne i mogą być stosowane do otrzymywania częściowo krystalicznych włóien PA6. Właściwości mechaniczne zależą od ilości dodanego koncentratu oraz parametrów procesu rozciągania. Niższa ilość koncentratu i koncentraty o mniejszej ilości komonomeru w kopoliamidzie, dodatek Cloisite, niższą prędkość rozciągania i optymalny stopień rozciąu zapewniają takie same lub lepsze właściwości (głónie wytrzymałść właściwą w stosunku do włókien niemodyfikowanych.