Microstructure And Properties Of WC-Co HVAF Coatings Obtained From Standard, Superfine And Modified By Sub-Micrometric Carbide Powders

Myalska H., Szymański K., Moskal G.

Archives of Metallurgy and Materials

2015

Vol. 60, iss. 2A

759--766

In this paper, microstructure and some properties of various coatings based on WC-Co obtained by the High Velocity Air Fuel technique are discussed. Initially, two WC-Co 83-17 powders of standard and superfine size were examined as a feedstock for a coatings deposition on a steel substrate. A standard Amperit 526.074 powder and an Inframat superfine powder were applied. Then three different sub-micrometric powders, WC, Cr3C2 and TiC were applied to modify the microstructure of WC-Co (Amperit 526.074). The aim of the investigations was to compare the microstructure and basic properties of coatings deposited from different components. The influence of sub-micrometric additions on mechanical properties of basic coatings was analyzed. Microstructure characterization of powders by using SEM and characterization of their technological properties as well, are presented. For all manufactured coatings obtained by a High Velocity Air Fuel method, the microhardness, porosity, adhesion to a substrate, and fracture toughness were determined. An improvement in WC-Co coating properties, as a result of sub-micrometric carbides addition, was revealed.

W pracy zostały omówione niektóre właściwości oraz mikrostruktura powłok typu WC-Co otrzymywanych metodą naddźwiękowego natrysku cieplnego w atmosferze powietrza (High Velocity Air Fuel). Początkowo, analizowano dwa proszki typu WC-Co 83-17 o standardowym rozmiarze ziarna oraz drobnym ziarnie pod kątem osadzania powłok na podłożu stalowym. Zastosowano standardowy proszek Amperit 526.074 oraz proszek drobnoziarnisty Inframat. Następnie trzy proszki submikrokrometryczne WC, Cr3C2 oraz TiC zastosowano w celu zmodyfikowania mikrostruktury proszku WC-Co (Amperit 526.074). Celem badań było porównanie mikrostruktury i różnych właściwości powłok natryskiwanych cieplnie z różnych proszków. Analizowano wpływ dodatków submikrometrycznych na właściwości mechaniczne powłok podstawowych. Scharakteryzowano morfologię proszków przy użyciu mikroskopu skaningowego oraz scharakteryzowano ich właściwości technologiczne. Dla wszystkich wytworzonych powłok uzyskanych za pomocą metody natrysku naddźwiękowego określono mikrotwardość, porowatość, przyczepność do podłoża i odporności na kruche pękanie. Ujawniono poprawę właściwości powłok WC-Co w wyniku wprowadzenia dodatków węglików submikrometrycznych.

The deposition of WC-Co coatings by EBPVD technique

Richert M. W., Mazurkiewicz A., Smolik J. A.

Archives of Metallurgy and Materials

2012

Vol. 57, iss. 2

511-515

The WC-Co carbides are widely used to deposit protective coatings on engineering surfaces against abrasion, erosion and other forms of wear existence. The nanostructure coatings offer high strength, a low friction coefficient and chemical and thermal stability. WCo coatings were deposited using EBPVD technique realized in original technological process implemented in the hybrid multisource device, produced in the Institute for Sustainable Technologies - National Research Institute in Radom (Poland). The different kind of precursor sources was used. Depending on the source of precursors nanostructure of coatings forms continuous film or consist from nano-carbides. Nanocrystalline WC-Co coatings show hardness in the range of 510-1266 HV. The microstructure of coatings were observed by transmission electron microscopy (TEM). The phase consistence were determined byBrucker D8 Discover-Advance Diffractometer. The paper presents the original technological equipment, methodology, and technological parameters for the creation of the nanocomposite coatings WC.

Węgliki WC-Co są szeroko używane do osadzania na powierzchniach inżynierskich jako ochrona przeciwko tarciu, erozji i innym formom zużycia. Powłoki nanostrukturalne wykazują wysoka wytrzymałość, niski współczynnik tarcia oraz chemiczną i termiczną stabiność. Powłoki WC-Co zostały osadzane techniką EBPVD przy użyciu oryginalnego technologicznego procesu z hybrydowym źródłem prekursorów, w Instytucie Technologii Eksploatacji w Radomiu (Polska). Użyto różnego rodzaju źródeł prekursorów. W zależności od rodzaju użytego źródła prekursorów nanostrukturalne powłoki były zbudowane z ciągłych warstw lub z nano-weglików. Mikrotwardość nanokrystalicznych powłok mieściła się w zakresie 510-1266 μHV. Mikrostruktura powłok była obserwowana transmisyjnym mikroskopem elektronowym (TEM). Skład fazowy powłok określono za pomocą aparatu rentgenowskiego Brucker D8 Discover-Advance Diffractometer. Artykuł prezentuje oryginalne technologiczne urządzenie, metodologię i technologiczne parametry pozwalające na wytworzenie nanokompozytowej powłoki WC.