Effect of Ti, Nb, Cr and B on structure and mechanical properties of high aluminium cast iron

Kopyciński D.

Archives of Foundry Engineering

2013

Vol. 13, iss. 1

77--80

In this work, a method was investigated to eliminate the presence of undesirable Al4C3 phases in a high-aluminium alloys, and thus improve the production process. The melting conditions employed in this work enabled the formation of a Fe-Al-C liquid solution. Moreover, titanium additions into the liquid allowed the precipitation of TiC. According to this reaction, the extent of carbon removal from the melt is strongly influenced by the amount of Ti additions. Hence, proper titanium levels can result in total removal of carbon from the liquid. Notice from this figure that Ti additions above 4.5%, totally eliminate the undesirable Al4C3 precipitates. Making Cr, Ti, B additions reduces size of FeAl alloys grains. In addition, this work indicates that the high-aluminium cast iron posses high oxidation resistance, exceeding that of high-chromium cast iron and chromium cast steels. Finally, the alloy ductility can be enhanced by additions of dopants such as B and Cr. Hence, additions of 0.03% B and 0.03%B-5% Cr combined with a heat treatment were implemented. As a result, the alloy ductility was significantly improved, where the strain of up to 5.3%, (B alone) or 15% (B-Cr) were obtained.

Composite zones produced in situ in the Ni3Al phase

Olejnik E., Janas A., Sikora G., Tokarski T., Nowak J.

Archives of Foundry Engineering

2013

Vol. 13, iss. 1

107--112

The study presents the results of research on the development of composite zones in castings based on the intermetallic phase of Ni3Al. Composite zones were obtained by placing packets with substrates for the reaction of titanium carbide in a foundry mould. To provide a variable carbides content in the composite zone, two compositions of the packets were prepared. The first packet contained only substrates for the reaction of TiC synthesis; the second one also contained a filler. The resulting composite zones in castings were examined for the filler effect on changes in the volume fraction, size and morphology of carbides in the zone. In addition, the effect of filler on the mechanical properties of the zone was verified, observing changes of Vickers hardness in this area. It was found that the presence of filler in the composition of the packet for synthesis reduced the content of carbides, as well as their size and morphology. Lower surface content of carbides reduced hardness of the zone, which enabled smooth control of the mechanical properties. At the same time, the use of the selected filler did not disturb the course of the TiC carbide synthesis.