Synthesis and characterization of one-component, moisture curing polyurethane adhesive based on Rokopol® D2002

Wadas Jadwiga, Oliwa Rafał, Pilch-Pitera Barbara, Byczyński Łukasz, Heneczkowski Maciej, Florjańczyk Zbigniew, Plichta Andrzej, Rokicki Gabriel

Polimery

2020

T. 65, nr 7-8

568--571

One-part, moisture curing polyurethane (PUR) adhesives based on poly(oxypropylene)diol Rokopol® and 4,4’-diphenylmethylene diisocyanate (MDI) modified with di-isononyl phthalate and a number of inorganic fillers and additives such as carbon black, thixotropic agent, dispersants and dibutyltin dilaurate as curing catalyst were developed. Adhesive curing was followed using dynamic oscillation rheometry and effect of some components on viscoelastic properties of curing materials was discussed. The cured materials were characterized by means of differential scanning calorimetry (DSC) and water contact angle measurements. The adhesive performance of obtained materials in bonding aluminum was evaluated by tensile shear bond strength tests.

Opracowano jednoskładnikowe kleje na osnowie diizocyjanianu 4,4’-metylenodifenylu (MDI) i polioksypropylenodiolu z środkami pomocniczymi (ftalanem diizononylu jako plastyfikatorem, napełniaczami: talkiem, haloizytem, modyfikowanym bentonitem; dyspergatorami, sadzą pigmentową i katalizatorem utwardzania – dilaurynianem dibutylocyny). Proces sieciowania analizowano za pomocą reometru z dynamiczną oscylacją. Metodą różnicowej kalorymetrii skaningowej wyznaczano temperaturę zeszklenia, ponadto określano kąt zwilżania i właściwości adhezyjne otrzymanych materiałów przeznaczonych do łączenia spoin Al/Al.

Studies on the effect of curing conditions on the curing rate and mechanical properties of moisture-cured poly(urethane-urea) elastomers containing oligocarbonate segments

Kozakiewicz J., Rokicki G., Przybylski J., Sylwestrzak K., Parzuchowski P. G., Tomczyk K. M.

Polimery

2011

T. 56, nr 7-8

564-570

In this paper the results of studies on the effect of the curing conditions on the mechanical properties, appearance and curing rate of poly(urethane-urea) elastomer (PURE) obtained by moisture-curing of the corresponding urethane prepolymer (URE) synthesized from isophorone diisocyanate (IPDI) and oligocarbonate diol (OCD) are presented. OCD was synthesized from dimethyl carbonate and 1,6-hexanediol. A designed experiment was conducted where two parameters [curing temperature (Tc—X1) and relative air humidity (RH—X2)] were changed at the same time according to the standard 22 model. The results were analyzed by Statistica computer programme and were presented in the form of X1-X2 graphs. The graphs were produced for a set of Y parameters characterizing the properties of PURE (mechanical properties, curing rate and sample appearance). The Y = f(X1, X2) equations were also obtained. The results showed the distinct dependence of the curing rate and PURE properties on curing parameters and allowed to select a range of optimum curing conditions.

W artykule przedstawiono wyniki badań nad wpływem warunków utwardzania wilgocią na właściwości mechaniczne, wygląd oraz szybkość utwardzania elastomeru poli(uretano-mocznikowego) (PURE) otrzymanego w wyniku utwardzania wilgocią odpowiedniego prepolimeru uretanowego (URE) syntezowanego z izoforonodiizocyjanianu (IPDI) i oligowęglanodiolu (OCD). OCD otrzymano z węglanu dimetylu i 1,6-heksanodiolu. Przeprowadzono zaplanowane zgodnie ze standardowym modelem 22 doświadczenie czynnikowe, w którym zmieniano dwa parametry [temperaturę utwardzania (Tc—X1) i wilgotność względną powietrza (RH—X2)]. Wyniki analizowano za pomocą programu komputerowego Statistica i przedstawiono je w postaci wykresów szeregu parametrów Y charakteryzujących właściwości PURE (właściwości mechaniczne, szybkość utwardzania, wygląd próbki) w zależności od parametrów X1-X2. Otrzymano również równania opisujące funkcje Y = f(X1, X2). Wyniki pokazały, że istnieje wyraźna zależność szybkości utwardzania i właściwości PURE od parametrów utwardzania. W szczególności zauważono, że nie tylko wytrzymałość na rozciąganie, ale także wydłużenie przy zerwaniu wzrasta ze wzrostem Tc i RH. Analiza wyników doświadczenia czynnikowego umożliwiła wybór optymalnego zakresu parametrów Tc = 70—75 °C i RH = 60 %, których zastosowanie pozwala uzyskać przezroczyste, pozbawione pęcherzy elastomery o znakomitych właściwościach mechanicznych.