Investigations of Flame Retardant Properties of Zinc Borate Accompanying with Huntite and Hydromagnesite in Polymer Composites

Atay Hüsnügül Yilmaz, Icin Öykü, Kuru Buket

Inżynieria Mineralna

|

2020

|

no. 1, vol. 1

79--86

EN

Fires have been a danger to human beings for the centuries. As people lost their lives and property in fires, they tried to fight the fire and their efforts in this area continued increasingly. Unfortunately, it is still not possible to completely reset the risk of starting the fire. But it seems likely to extinguish immediately after the fire has started, and this is very important to save people’s lives. Scientists have been working in this field in recent years; they are concentrated on producing fire-resistant materials using different materials. This can be provided by different ways; either fire-resistant material can be produced new, or the fire resistivity can be provided by incorporating the additive material into a flammable material. In our previous studies, we used huntite and hydromagnesite minerals to give fire resistance property to polymer materials, very successful results were obtained. In this study, huntite and hydromagnesite minerals were used for accompanying with zinc borate in polypropylene composites in order to increase the flame retardant property of a polymeric materials. Different content of minerals were blended with polypropylene, and composites were produced by twin-screw extruder for observing synergistic effect. Scanning electron microscopy (SEM) analyses were conducted to determine the structural and morphological properties of the composites. Thermal properties were determined according to thermogravimetric analysis (TGA). Tensile and three point bending tests were carried out to obtain mechanical properties. Flame retardant performance was evaluated according to UL 94 vertically flammability test. It was concluded that very good synergistic effects were obtained that zinc borate was significantly influential with huntite/hydromagnesite in the flammability characteristics of composites because higher char formation is observed with zinc borate addtion. Moreover, the zinc borate reduced the smoke generated during combustion.

PL

Pożary od wieków stanowią zagrożenie dla ludzi. Gdy ludzie stracili życie i mienie w wyniku pożarów, próbowali zwalczyć pożar, a ich wysiłki w tej dziedzinie były coraz bardziej skuteczne Niestety, nadal nie jest możliwe całkowite wyeliminowanie ryzyka rozpoczęcia pożaru. Ważne jest ugaszenie pożaru natychmiast po wybuchu aby uratować ludzkie życie. Naukowcy pracują w tej dziedzinie w ostatnich latach; koncentrują się na wytwarzaniu materiałów ognioodpornych przy użyciu różnych surowców. Można to zapewnić na różne sposoby; albo materiał ognioodporny może być wytworzony jako nowy, albo ognioodporność może być zapewniona przez włączenie materiału dodatkowego do materiału łatwopalnego. W badaniach używano minerałów huntite i hydromagnesitu, aby nadać materiałom polimerowym właściwości ognioodpornych, osiągając bardzo udane wyniki. W artykule przedstawiono wyniki wykorzystania minerałów huntitu i hydromagnezytu w obecności boranu cynku w kompozytach polipropylenowych w celu zwiększenia właściwości ognioodpornych materiałów polimerowych. Różne ilości minerałów zmieszano z polipropylenem, a kompozyty wytworzono za pomocą wytłaczarki dwuślimakowej w celu zaobserwowania efektu synergicznego. Przeprowadzono analizy skaningowej mikroskopii elektronowej (SEM) w celu określenia właściwości strukturalnych i morfologicznych kompozytów. Właściwości termiczne określono za pomoca analizą termograwimetryczną (TGA). Przeprowadzono próby rozciągania i zginania trzypunktowego w celu określenia właściwości mechanicznych. Działanie zmniejszające palność oceniono zgodnie z testem palności w pionie UL 94. Stwierdzono, że uzyskano bardzo dobre efekty synergiczne, boran cynku miał znaczący wpływ na huntit i hydromagnezyt i zmianę charakterystyki palności kompozytów, ponieważ obserwuje się podwyśzone powstawanie węgla drzewnego przy dodawaniu boranu cynku. Ponadto boran cynku zmniejszył ilość dymu powstający podczas spalania

2

Wpływ dodatku hydroksytlenku glinu na krytyczny czas redukcji widzialności w dymie powstałym ze spalania oraz pirolizy żywicy epoksydowej

Węsierski T., Łukaszek-Chmielewska A., Konecki M., Drzymała T.

Polimery

|

2015

|

T. 60, nr 11-12

723--729

PL

Zbadano wpływ dodatku 5 % mas. hydroksytlenku glinu [AlO(OH)] na wydłużenie krytycznego czasu redukcji widzialności w strefie dymu wydzielanego podczas spalania lub pirolizy żywicy epoksydowej (Epidian 5).

EN

The effect of the addition of 5 wt % aluminum hydroxide oxide [AlO(OH)] to epoxy resin Epidian 5 on the improvement in evacuation conditions from a smoke-filled area during the burning or pyrolysis of the resin has been investigated. An increase in the critical time of visibility reduction was observed.

3

Obtaining magnesium hydroxide of micro- or nanostructure on the basis of technical raw materials

Radomski P., Jarosiński A., Madejska L.

Gospodarka Surowcami Mineralnymi

|

2014

|

T. 30, z. 4

133--141

EN

This paper presents the initial results of efforts to obtain high-purity magnesium hydroxide with micro or nano-structure from technical raw materials. Magnesium hydroxide can be used in the plastic industry as a flame retardant additive. Mg(OH)2 should be characterized by high surface area (above 100 m2/g), high disintegration, and high purity. In the research, technical magnesium sulfate was used which was purified by hydrolytic methods before obtaining the magnesium hydroxide. Heptahydrate, the specific raw material for magnesium hydroxide synthesis, was crystallized from purified solutions. The study was conducted for magnesium sulfate concentration in an interval of 0.2–2.0 mol/dm3 and a sodium hydroxide interval of 0.4–0.5 mol/dm3. The precipitate was analyzed by the SEM method and BET, and its purity was tested using the colorimetric technique.

PL

W pracy przedstawiono wstępne wyniki otrzymywania wodorotlenku magnezu o wysokiej czystości i mikro- lub nanostrukturze na bazie surowców technicznych. Wodorotlenek magnezu może znaleźć potencjalne zastosowanie w przemyśle tworzyw sztucznych jako dodatek opóźniający zapłon. Musi cechować się wysoką powierzchnią właściwą (powyżej 100 m2/g), silnym rozdrobnieniem oraz wysoką czystością. W badaniach stosowano techniczny siarczan magnezu, który przed procesem otrzymywania wodorotlenku magnezu oczyszczano z zastosowaniem metod hydrolitycznych. Z oczyszczonych roztworów krystalizowano sól siedmiowodną, która była surowcem do otrzymywania wodorotlenku magnezu. Badania prowadzono dla różnych stężeń siarczanu magnezu 0,2–2,0 mol/dm3, jako czynnik strącający stosowano wodorotlenek sodu w przedziale stężeń 0,4–0,5 mol/dm3. Otrzymany osad analizowano przy użyciu technik SEM oraz BET, czystość określano technikami kolorymetrycznymi.

4

Nanonapełniacze krzemionkowe modyfikowane fosforem o właściwościach uniepalniających

Pytel A., Zielecka M., Bujnowska E., Wenda M., Cyruchin K.

Zeszyty Naukowe Politechniki Poznańskiej. Budowa Maszyn i Zarządzanie Produkcją

|

2010

|

Nr 12

291-295

PL

Niniejsza praca odnosi się do nanonapełniaczy krzemionkowych modyfikowanych fosforem wykazujących właściwości uniepalniąjące. Opracowano innowacyjną metodę otrzymywania na-noproszku w procesie zol-żel z wykorzystaniem dietylofosfatoetylotrietoksysilanu (SiP) wprowadzającego do krzemionki fosfor. Produkty charakteryzowały się jednolitą nanometryczną wielkością, co ułatwia ich rozprowadzenie w polimerze. Nanokompozyty z nanonapełniaczami będącymi przedmiotem badań wykazują dobre właściwości uniepalniąjące potwierdzone m.in. wyższą wartością indeksu tlenowego, niż polimery bez napełniacza, czy małym ubytkiem masy przy badaniu metodą termograwimetryczną. Wprowadzenie nanokrzemionki modyfikowanej fosforem poprawia właściwości mechaniczne (lepsza wytrzymałość na rozciąganie, zginanie, większa sprężystość i udarność).

EN

The paper addresses to phosphorous modified nanosilica as flame retardant filler. An innovative method of nanopowders manufacturing was developed, based on sol-gel process with diethyl-phosphatoethyltriethoxysilane (SiP) incorporating phosphorous into silica. Received materials are characterized by uniform particle size, which facilitates their homogeneous distribution in polymer matrix. Polymer nanocomposites containing the above nanofiller have good flame retardancy compared with pure polymer, their oxygen index value increases and loss weight in thermo- gravimetric analysis decreases. Addition of phosphorous modified nanosilica does not reduce polymer quality, but improve the key properties especially mechanical (better tensile and flexural strength, improved stiffness and impact strength).

5

Układ katalityczny "Visico-Ambicat" umożliwiający sieciowanie polietylenu w temperaturze pokojowej

Krasowski W.

Polimery

|

2001

|

T. 46, nr 10

704-708

PL

Zbadano możliwość wyeliminowania, w produkcji kabli napowietrznych niskich napięć o izolacji polietylenowej, stosowanej dotychczas energochłonnej operacji sieciowania polietylenu w gorącej wodzie lub w parze. Możliwość taką stworzyło pojawienie się układu katalitycznego "Visico-Ambicat" pozwalającego na sieciowanie PE w temperaturze pokojowej w warunkach dostępu wilgoci. Na pierwszym etapie pracy przeprowadzono badania laboratoryjne mieszanek tego układu katalitycznego z PE bazowym, stosując paski wytłoczone w wytłaczarce laboratoryjnej; określono przy tym właściwości mechaniczne i elektryczne tych mieszanek (tabele 1-4). Uzyskanie pozytywnych wyników uzasadniło wykonanie na drugim etapie pracy prototypowego kabla z wykorzystaniem omawianej mieszanki. Kabel poddano pełnym badaniom zgodnie z zakładową normą (tabela 5), również uzyskując zadowalające rezultaty.

EN

A new catalytic system (VISICO-AMBICAT) allows to eliminate the crosslinking of PE in hot water or in steam as a step in the fabrication of PE-coated low-tension aerial cables. PE can be crosslinked in the presence of moisture at room temperature. As step I, basis PE-VISICO-AMBICAT blends were extruded in a laboratory extruder to produce the strips to be used to measure the mechanical and electrical properties (Tables 1-4). As step II, the blend was used to coat a prototype cable. The cable was tested in compliance with a Branch Standard (Table 5). Results were positive.