Wyniki wyszukiwania - BazTech

1

Mechanical properties of Ti6Al7Nb alloy quenched from the single phase β range

Dąbrowski R.

Rudy i Metale Nieżelazne Recykling

|

2015

|

R. 60, nr 3

115--119

EN

Mechanical properties of the two-phase titanium alloy Ti6Al7Nb, after the heat treatment based on soaking this alloy in the single phase β range, quenching in water or oil and ageing at two selected temperatures, were determined in the paper. The alloy mechanical properties were determined in tensile and impact tests, supported by the fractographic analysis of fractures. In addition, its hardness was measured and the analysis of changes occurring in the microstructure was performed for all variants of the alloy heat treatment. Regardless of the applied cooling rate of the alloy from a temperature of 1040 °C followed by ageing at 500 and 650 °C, none essential changes were noticed in its microstructure. It was shown that applying less intensive cooling medium (oil) instead of water (before ageing) decreases strength properties indicators, i.e. tensile strength and yield strength as well as hardness (only slightly). The decrease of the above mentioned indicators is accompanied by an increase of impacts strength. Fractures of samples after tensile and impact tests have a similar nature regardless of the applied heat treatment.

PL

W artykule określono własności mechaniczne dwufazowego stopu tytanu Ti6Al7Nb po obróbce cieplnej polegającej na wygrzewaniu stopu w zakresie jednofazowym, oziębianiu w wodzie lub oleju oraz starzeniu przy wybranych dwóch temperaturach. Własności mechaniczne stopu wyznaczono w próbie rozciągania i w próbie udarności, które poparto analizą fraktograficzną przełomów. Dodatkowo, dla wszystkich wariantów obróbki cieplnej stopu zmierzono twardość i dokonano analizy zmian zachodzących w mikrostrukturze. Niezależnie od zastosowanej szybkości oziębiania badanego stopu od temperatury 1040 °C i następnego starzenia przy 500 i 650 °C, nie odnotowano istotnych zmian zachodzących w jego mikrostrukturze. Wykazano, że zastosowanie mniej intensywnego ośrodka chłodzącego (oleju) zamiast wody (przed zabiegiem odpuszczania), obniża wskaźniki własności wytrzymałościowych, tj. wytrzymałość na rozciąganie i umowną granicę plastyczności, a także nieznacznie twardość. Obniżeniu ww. wskaźników towarzyszy wzrost udarności. Przełomy próbek rozciąganych i udarnościowych niezależnie od zastosowanej obróbki cieplnej mają podobny charakter.

2

Effect of Heat Treatment on the Mechanical Properties of Two-Phase Titanium Alloy Ti6Al7Nb

Dąbrowski R.

Archives of Metallurgy and Materials

|

2014

|

Vol. 59, iss. 4

1713--1716

EN

Mechanical properties of the two-phase titanium alloy Ti6Al7Nb, after the heat treatment based on soaking this alloy in the α + β range, cooling in water or oil and ageing at two selected temperatures, were determined in the hereby paper. The alloy mechanical properties were determined in tensile and impact tests, supported by the fractographic analysis of fractures. In addition, its hardness was measured and the analysis of changes occurring in the microstructure was performed for all variants of the alloy heat treatment. Regardless of the applied cooling rate of the alloy, from a temperature of 970°C followed by ageing at 450 and 650°C, none essential changes were noticed in its microstructure. It was shown that applying less intensive cooling medium (oil) instead of water (before tempering) decreases strength properties indicators, i.e. tensile strength and yield strength as well as hardness (only slightly). The decrease of the above mentioned indicators is accompanied by an increase of an elongation and impacts strength. Fractures of tensile and impact tests are of a ductile character regardless of the applied heat treatment.

PL

Wartykule określono własności mechaniczne dwufazowego stopu tytanu Ti6Al7Nb po obróbce cieplnej polegającej na wygrzewaniu stopu w zakresie dwufazowym, oziębianiu w wodzie lub oleju oraz starzeniu przy wybranych dwóch temperaturach. Własności mechaniczne stopu wyznaczono w próbie rozciągania i w próbie udarności, które poparto analizą fraktograficzną przełomów. Dodatkowo, dla wszystkich wariantów obróbki cieplnej stopu zmierzono twardość i dokonano analizy zmian zachodzących w mikrostrukturze. Niezależnie od zastosowanej szybkości oziębiania badanego stopu od temperatury 970°C i następnego starzenia przy 450 i 650°C, nie odnotowano istotnych zmian zachodzących w jego mikrostrukturze. Wykazano, że zastosowanie mniej intensywnego ośrodka chłodzącego (oleju) zamiast wody (przed zabiegiem odpuszczania), obniza wskaźniki własności wytrzymałościowych, tj. wytrzymałość na rozciąganie i umowną granice plastyczności, a także nieznacznie twardość. Obniżeniu ww. wskaźników towarzyszy wzrost wydłużenia oraz udarności. Przełomy próbek rozciąganych i udarnościowych niezależnie od zastosowanej obróbki cieplnej mają charakter ciągliwy.

3

Wpływ azotowanego jarzeniowostopu Ti6Al2Cr2Mo na strukturę warstw wierzchnich i wytrzymałość zmęczeniową

Jeleńkowski T., Wierzchoń T., Gołębiewski M.

Zeszyty Naukowe Politechniki Świętokrzyskiej. Mechanika

|

2003

|

Z. 78

197-206

PL

W artykule przedstawiono wyniki badań strukturalnych, wytrzymałości zmęczeniowej i faktograficznych warstw wierzchnich wytworzonych na stopie tytanu Ti6Al2Cr2Mo w warunkach procesu azotowania jarzeniowego w połączeniu z różną obróbką cieplną przeprowadzoną w trakcie chłodzenia. Analizowano cechy morfologiczne skladników fazowych, budowę przełomów zmęczeniowych. Stwierdzono, że najlepszą wytrzymałość zmęczeniową otrzymano po procesie azotowania jarzeniowego w stałej temperaturze, po którym próbki były chłodzone w próżni. Niższe wartości wytrzymałości zmęczeniowej w pozostałych procesach upatruje się w strukturze warstwy azotków i cech morfologicznych pierwotnej fazy α obecnej w warstwie dyfuzyjnej.

EN

The paper presents the results of examinations of the Ti6Al2Cr2Mo titanium alloy after subjecting it to glow discharge assisted nitriding followed, during the cooling stage, by various heat treatment operations. The properties examined included: the structure, the fatigue strength and the fracture properties of the surface layers produced during this combined treatment. The morphological features of the phase components, the structure of the fatigue fractures and the fractures of cylindrical samples cooled to the temperature of liquid nitrogen were also examined. The best fatigue strength was obtained in the samples that had been nitrided at a constant temperature and then cooled in vacuum. The samples subjected to the other processes showed a lower fatigue strength, which can be attributed to the fact that the structure of the nitrided layer produced by them and the morphological features of the primary α phase present in the diffusion layer were less advantageous.

4

Wpływ parametrów geometrycznych mikrostruktury na właściwości mechaniczne dwufazowych stopów tytanu

Juszczyk B., Kościelna A., Szkliniarz W.

Inżynieria Materiałowa

|

2003

|

R. XXIV, nr 2

79--83

PL

W pracy przedstawiono wyniki badań określające zależności pomiędzy właściwościami mechanicznymi dwufazowego stopu tytanu Ti-6Al-2Mo-2Cr-Fe a parametrami geometrycznymi jego mikrostruktury, kształtowanymi w procesach obróbki cieplnej. Celem ustalenia tych relacji wykonano badania właściwości mechanicznych i mikrostruktury stopu po obróbce cieplnej w różnych warunkach. Wyznaczono parametry geometryczne charakteryzujące morfologię pierwotnej fazy alfa i ich współczynniki zmienności. Stosując metody statystyki matematycznej i regresji wielokrotnej określono zależności pomiędzy właściwościami mechanicznymi i parametrami geometrycznymi wydzieleń pierwotnej fazy alfa badanego stopu.

EN

The research result of relationship between mechanical properties and geometrical parameters of microstructure two-phases titanium alloy, forming during heat treatment processes was presented in this article. To estimate relation used proper set of the research, measurements and analytical methods. Made an investigation of the mechanical properties and microscopy observation of specimen put on different variants of heat treatment. It was found that the geometrical parameters characterised primary alpha-phase and their factors of variability. It used the mathematical statistic and multiple regressions to found relation between mechanical properties of the research alloy and geometrical parameters precipitation primary alpha-phase.

5

Microstructure of the diffusion layer obtained in Ti6Al2Cr2Mo alloy during glow discharge nitriding

Jeleńkowski J., Major B., Gołębiewski M., Wierzchoń T.

Advances in Materials Science

|

2003

|

Vol. 3, nr 2(4)

28--34

EN

This paper presents the results of metallographic, X-ray, and TEM examinations of the microstructure and the sub-structure of the diffusion layer that underlies the TiN + Ti2N layer produced by glow discharge nitriding of the Ti6Al2Cr2Mo alloy. The metallographic examinations show that a two-phase zone α + β - its thick-ness increasing with the increasing process temperature - can be observed underneath the nitride layer after half an hour of nitriding at 940ºC, when the core of the sample has an α - phase structure. The presence of the glow discharge assisting the nitrid-ing process accelerated the thickening of both the nitride zone and the diffusion layer. Morphology of α - phase grains changed as well. The grain lengh-to-thickness ratio decreased. X-ray examinations revealed the presence in the substrate structure of two kinds of solid solution with the α titanium matrix. TEM analysis showed a state of certain ordering of the crystalline lattice and, locally, a tweed-type structure of the β phase.

6

Characteristics of hot deformation of two phase titanium alloy Ti-5Al-5Mo-5V-1Cr-1Fe.

Kubiak K.

Advances in Manufacturing Science and Technology

|

2003

|

Vol. 27, nr 4

31-43

EN

This paper presents the influence of deformation conditions (temperature and strain rate) on resistance of plastic flow and critical strain of Ti-5Al-5Mo-5V-1Cr-1Fe alloy. Based on the results from sequential deformation with a torsion plastometer the relative volume of the recrystalized phase. The actual deformation temperature was measured with a pyrometric method and an infrared mapping method. Changes of the alloy microstructure were assessed with and optical microscope and a transmission electron microscope.

PL

W pracy przedstawiono wpływ warunków odkształcania temperatury i prędkości na opór plastycznego płynięcia oraz odkształcenie graniczne stopu Ti-5Al-5Mo-5V-1Cr-1Fe. Na podstawie wyników próby odkształcania sekwencyjnego na plastometrze skrętnym wyznaczono objętość względną fazy zrekrystalizowanej. Określono rzeczywistą temperaturę odkształcania metodą pirometryczną i termowizyjną. Zmiany mikrostruktury stopu badano metodą mikroskopii optycznej i transmisyjnej mikroskopii elektronowej.