Rolling texture development in two-phase steel with small amount of ferrite.

Bunsch A., Ryś J., Ratuszek W., Kowalska J.

Inżynieria Materiałowa

|

2001

|

R. XXII, nr 4

246-249

EN

A development of deformation textures was investigated in two-phase steel containing about 10% of ferrite volume fraction. The steel of this type was subjected to cold-rolling within the range up to 90% of deformation by applying high and low reductions per pass. Results of X-ray measurements indicate at different mechanisms of the rolling texture formation depending on the applied mode of deformation. From the X-ray phase analysis and the examination of the orientation distribution functions it follows that deformation induced (gamma->alpha) phase transformation exerts significant effect on the texture development of both phases when small reductions per pass are employed.

PL

Badania dotyczyły rozwoju tekstur odkształcenia w stali dwufazowej zawierającej około 10% objętościowych ferrytu. Stal tego typu poddano walcowaniu na zimno w zakresie do 90% deformacji przy zastosowaniu dużych i małych odkształceń częściowych. Rezultaty badań rentgenowskich wskazują na różne mechanizmy tworzenia tekstur walcowania zależnie od zastosowanego sposobu odkształcenia. W oparciu o wyniki analizy fazowej oraz analizę funkcji rozkładu orientacji widocznym jest, że indukowana odkształceniem przemiana fazowa (gamma->alfa) wywiera istotny wpływ na rozwój tekstury walcowania obu faz przy zastosowaniu małych odkształceń jednostkowych.

2

Microtexture investigations in austenitic-ferritic steels using EBSD technique.

Jura J., Bunsch A., Ratuszek W.

Inżynieria Materiałowa

|

2001

|

R. XXII, nr 4

408-411

PL

Celem pracy było określenie możliwości wykorzystania techniki wstecznego rozproszenia elektronów (EBSD) do badań mikrostruktury stali dwufazowych. Stosując technikę EBSD dokonano identyfikacji faz oraz pomiarów lokalnych orientacji w dwóch różnych stalach austenityczno-ferrytycznych. Na podstawie pomiarów lokalnych orientacji wyznaczono rozkłady dezorientacji występujących w badanym materiale oraz wyznaczono tekstury krystalograficzne. Uzyskane wyniki porównano z wynikami obserwacji mikroskopowych oraz uśrednionymi teksturami tego typu materiałów.

EN

The main aim of this work was to investigate the possibility of applying the Electron Back Scattering Diffraction (EBSD) technique for microstructure observations in two-phase steel. Phase identification and local orientation measurements were done in two different austenite-ferrite steels with the use of EBSD. On the basic of the measured local orientation, the disorientation distributions as well as crystallographic textures were calculated. The obtained results were compared with ealier microscopic observations and textures measured in two-phase steels of this type.

3

Annealing textures in heavy deformed austenitic-ferritic steel

Ratuszek W., Ryś J., Witkowska M., Chruściel K.

Inżynieria Materiałowa

|

2001

|

R. XXII, nr 5

761-764

EN

A development of annealing textures was examined in two-phase austenitic-ferritic steel predeformed by rolling up to 95% of reduction. X-ray investigations of the centre layers of the sheets, included the phase analysis, the measurements of pole figures and calculations of the orientation distribution functions (ODF's). The experimental data indicate that significant differences in the rolling and annealing textures in comparison to one-phase steels are due to the two-phase character of the structure and the phase instability of austenitic-ferritic steels. It was concluded that the phase transformations proceeding in the course of deformation and annealing treatment exert considerable effect on the occurrence and the intensity of the particular texture components in both phases.

PL

Badania dotyczyły rozwoju tekstur wyżarzania w dwufazowych stalach austenityczno-ferrytycznych wstępnie odkształconych na drodze walcowania do 95% deformacji. Badania rentgenowskie warstw środkowych blach obejmowały analizę fazową, pomiary figur biegunowych i obliczenia funkcji rozkładu orientacji (FRO). Uzyskane wyniki wskazują, że istotne różnice w rozwoju tekstur walcowania i wyżarzania w stosunku do stali jednofazowych wynikają z dwufazowego charakteru struktury i niestabilności fazowej stali austenityczno-ferrytycznych. Wywnioskowano, że przemiany fazowe zachodzące w trakcie procesów odkształcenia i wyżarzania w zasadniczy sposób wpływają na występowanie oraz intensywność głównych składowych tekstury obu faz.