The effect of starting orientations and initial morphology on texture formation in duplex steel SAF 2205

Ryś J., Witkowska M.

Archives of Metallurgy and Materials

2009

Vol. 54, iss. 3

789-803

The present investigations concern the rolling texture formation and changes in morphology of two-phase structure in cold-rolled mid-alloy duplex stainless steel SAF 2205 with addition of nitrogen. The preliminary thermo-mechanical treatment included hot-rolling with subsequent solution annealing at the temperature 1150C. Afterwards the steel was cold-rolled within the wide range of reductions by applying two different variants, with rolling directions perpendicular and parallel to the direction of hot-deformation. Texture analysis indicates that austenite shows tendency to develop the textures similar to those in one-phase austenitic steels regardless of the applied cold-rolling variant and the final rolling textures of ferrite significantly differ from the typical textures of ferritic steels. Formation of the texture close to the {110}<112> alloy-type texture was observed in austenite and the orientation changes proceeded gradually over a wide range of reductions, especially for the cold-rolling variant perpendicular to the direction of hot-deformation. On the other hand the major component of the ferrite starting texture, i.e. the rotated cubic orientation {001}<110> and the character of texture spread, which is different for both rolling variants, remained essentially unchanged up to high deformations. It is concluded that the starting orientations of both constituent phases after the preliminary treatment and the band-like morphology of the ferrite-austenite structure considerably influence formation of the cold-rolling textures in the examined duplex type steel.

Prezentowane badania dotyczą rozwoju tekstur walcowania i zmian morfologii struktury dwufazowej w walcowanej na zimno średnio-stopowej nierdzewnej stali duplex w gatunku SAF 2205 z dodatkiem azotu. Wstępna obróbka cieplno-mechaniczna obejmowała walcowanie na gorąco oraz wyżarzanie i przesycanie z temperatury 1150C. Stal poddano następnie walcowaniu na zimno w szerokim zakresie deformacji, stosując dwa różne warianty z kierunkami walcowania prostopadłym i równoległym do kierunku odkształcenia na gorąco. Analiza tekstur wskazuje, że niezależnie od zastosowanego wariantu walcowania na zimno austenit wykazuje tendencje do tworzenia tekstur odpowiadających tym w jednofazowych stalach austenitycznych natomiast końcowe tekstury walcowania ferrytu różnią się istotnie od typowych tekstur stali ferrytycznych. W austenicie obserwuje się rozwój tekstur zbliżonych do tekstury typu stopu {110}<112>, a w przypadku wariantu walcowania na zimno prostopadle do kierunku odkształcenia na gorąco zmiany orientacji zachodza stopniowo w szerokim zakresie odkształceń. Z kolei główna składowa tekstury początkowej ferrytu, tzn. orientacja skręcona sześcienna {001}<110> jak również charakter rozmycia tekstury ferrytu, odmienny dla obu wariantów walcowania, pozostają zasadniczo nie zmienione do wysokich odkształceń. Należy stwierdzić, że orientacje początkowe obu faz po obróbce wstępnej oraz pasmowa morfologia ferrytu i austenitu wywierają istotny wpływ na tworzenie się tekstur odkształcenia podczas walcowania na zimno badanej stali typu duplex.

Rolling texture development in nitrogen alloyed ferritic-austenitic steel of duplex type

Ryś J., Witkowska M.

Archives of Metallurgy and Materials

2008

Vol. 53, iss. 1

221-228

The present research concerns the rolling texture formation in the X2CrNiMoN22-6-3 steel, which chemical composition corresponds to the commercial mid-alloy duplex steel grade SAF 2205. The applied thermo-mechanical treatment included hot-rolling and subsequent solution annealing at the temperature 1150°C. After the preliminary treatment the two-phase structure consisted of about 40% of austenite volume fraction within the ferrite matrix. Subsequently the steel was cold-rolled within the range up to 85% of reduction, perpendicularly to the direction of hot-deformation. Analysis of the rolling texture formation in both constituent phases indicates that the examined steel shows tendency to develop the textures close to those in single phase steels. In both phases however the process proceeds in different way and the final textures display certain important differences in comparison to the typical ferrite and austenite textures. In the case of ferrite the major component of the initial texture remains stable up to high deformations and the final texture essentially does not exhibit the fibrous character. On the other hand a gradual formation of the texture close to an alloy-type texture is observed in austenite and the orientation changes proceed over a wide deformation range. It is concluded that the band-like morphology of the ferrite-austenite structure and the initial orientations resulting from the change of rolling direction strongly influence the formation of the final rolling textures.

Prezentowane badania dotyczą rozwoju tekstury walcowania w stali X2CrNiMoN22-6-3, której skład chemiczny odpowiada średnio-stopowej stali duplex w gatunku SAF 2205. Zastosowana obróbka cieplno-mechaniczna obejmowała walcowanie na gorąco oraz przesycanie z temperatury 1150°C. Po obróbce wstępnej struktura dwufazowa składała się z okolo 40% austenitu w osnowie ferrytu. Następnie stal poddano walcowaniu na zimno w zakresie do 85% defonnacji, prostopadle do kierunku odkształcenia na gorąco. Analiza tworzenia się tekstur walcowania w obu składowych fazach wskazuje, że badana stal wykazuje tendencje do rozwoju tekstur zbliżonych do tych w stalach jednofazowych. Jednak w obu fazach proces ten zachodzi w odmienny sposób a koncowe tekstury wykazują pewne istotne różnice w porównaniu do typowych tekstur ferrytu i austenitu. W przypadku ferrytu, główna składowa tekstury początkowej pozostaje stabilna do wysokich odkształceń a tekstura końcowa zasadniczo nie wykazuje charakteru włóknistego. Z kolei w austenicie obserwuje się stopniowy rozwój tekstury zbliżonej do tekstury typu stopu a zmiany orientacji zachodzą w szerokim zakresie odkształceń. Stwierdzono, że pasmowa morfologia ferrytu i austenitu oraz orientacje początkowe wynikające ze zmiany kierunku walcowania wywierają istotny wpływ na tworzenie się końcowych tekstur odkształcenia.