Wyniki wyszukiwania - BazTech

1

The Magnetization Reversal Processes of Bulk (Nd, Y)‑(Fe, Co)‑B Alloy in the As-Quenched State

Dośpiał M., Nabiałek M., Szota M., Gondro J.

Archives of Metallurgy and Materials

|

2015

|

Vol. 60, iss. 3A

1587--1590

EN

The magnetization reversal processes of bulk Fe64Co5Nd6Y6B19 alloy in the as-quenched state have been investigated. From the analysis of the initial magnetization curve and differential susceptibility versus an internal magnetic field it was deduced, that the main mechanism of magnetization reversal process is the pinning of domain walls at the grain’s boundaries of the Nd2Fe14B phase. Basing on the dependence of the reversible magnetization component as a function of magnetic field it was found that reversible rotation of a magnetic moment vector and motion of domain walls in multi-domain grains result in high initial values of the reversible component. The presence of at least two maxima on differential susceptibility of irreversible magnetization component in function of magnetic field imply existence of few pinning sites of domain walls in Fe64Co5Nd6Y6B19 alloy. The dominant interactions between particles have been determined on the basis of the Wohlfarth dependence. Such a behavior of Wohlfarth’s plot implies that the dominant interaction between grains becomes short range exchange interactions.

PL

W pracy przedstawiono wyniki badań własności magnetycznych i mechanizmów przemagnesowania masywnego stopu Fe64Co5Nd6Y6B19 w stanie po zestaleniu. Z krzywych pierwotnego namagnesowania i ich podatności różnicowej określono, że głównym mechanizmem przemagnesowania jest kotwiczenie ścian domenowych. Na podstawie zależności składowych odwracalnych namagnesowania od pola magnetycznego stwierdzono, że procesy odwracalne takie jak obroty wektora namagnesowania oraz ruch ścian domenowych w wielodomenowych ziarnach mają znaczny wpływ na zmiany namagnesowania dla początkowych wartości pól magnetycznych. Obecność maksimów w zależności składowej nieodwracalnej podatności magnetycznej świadczy, że głównym mechanizmem przemagnesowania w badanych magnesach jest kotwiczenie ścian domenowych na licznych centrach kotwiczenia znajdujących się na granicach ziaren fazy Nd2Fe14B oraz na defektach strukturalnych. W celu określenia oddziaływań między ziarnami określono zależność Wohlfartha. Zależność ta nie jest spełniona dla badanego magnesu, świadczy to o istnieniu oddziaływania wymiennego między ziarnami magnesu.

2

Dependence of the Structure And Magnetic Properties of Cast Plate-Shaped Nd60Fe30Al10 Samples on Their Thickness

Michalski B., Kaszuwara W., Latuch J., Pawlik P.

Archives of Metallurgy and Materials

|

2015

|

Vol. 60, iss. 3A

1623--1627

EN

The hard magnetic Nd-Fe-Al alloys are inferior to Nd-Fe-B magnets as far as the magnetic properties are concerned, but their great advantage is that they need no additional annealing to achieve good magnetic properties. These properties depend on the cooling rate from the melting state, and on the thickness of the sample - the best values are achieved at the quenching rates at which the samples have a thickness of 0.3-2 mm. The present study is concerned with the correlation between the magnetic properties of the plate-shaped Nd60Fe30Al10 samples and their size - thickness. Two casting ways: with the melt stream perpendicular direction and parallel to the surface of the plates were used. The plates were produced by pressure casting and suction casting. The studies have shown that the cooling rates depends on local propagation on liquid metal in the mold resulting in heterogeneity of structure and properties.

PL

Stopy Nd-Fe-Al nie posiadają tak wysokich właściwości magnetycznych jak Nd-Fe-B. Ich dużą zaletą jest natomiast możliwość otrzymywania bezpośrednio poprzez odlewanie. Właściwości magnetyczne zależą od szybkości chłodzenia ciekłego stopu, co w praktyce określa się rozmiarem odlewanej próbki. Przy odlewaniu do form metalowych optymalny zakres wymiaru w kierunku odprowadzania ciepła to 0,3-2 mm. W niniejszej pracy zbadano zależność właściwości magnetycznych stopu Nd60Fe30Al10 od grubości próbek w postaci płytek w zależności od sposobu odlewania (wtryskiwanie cieczy pod ciśnieniem i odlewanie z zasysaniem) oraz kierunku strumienia cieczy (prostopadle lub równolegle do powierzchni płytki). Badania wykazały, że szybkość chłodzenia zależy lokalnie od sposobu rozchodzenia się cieczy w formie, co skutkuje niejednorodnością mikrostruktury i właściwości.

3

High-coercivity Nd-Fe-B Powders Obtained by High-Temperature Milling

Kaszuwara W., Michalski B., Orlowski P.

Archives of Metallurgy and Materials

|

2014

|

Vol. 59, iss. 1

47--50

EN

The possibility of employing high temperature milling (600°C) for the production of highly coercive Nd-Fe-B powders was examined. The materials were the Nd12Fe82B6, alloy which was subjected to mechanical milling and the powders of the constituent elements of this alloy which were processed by mechanical alloying. The processes were conducted in the two variants: the first variant consisted of mechanical milling performed at a high temperature which was maintained during the entire process, and the other variant included preliminary milling carried out at room temperature and then the milling temperature was increased. All the processes gave nanocrystalline powders with hard magnetic properties. The powders produced by mechanical milling had better properties than those produced by mechanical] alloying as they were more homogeneous and contained smaller amounts of the α-Fe phase.

PL

W pracy badano możliwości zastosowania procesu mielenia w wysokiej temperaturze (600°C) do otrzymywania wyso- kokoercyjnych proszków Nd-Fe-B. Mieleniu poddano stop Nd12Fe82B6,. a także zastosowano metodę mechanicznej syntezy stopów tzn. mielono proszki pierwiastków składników stopu. Procesy prowadzono w dwóch wariantach: cały proces odbywał się w podwyższonej temperaturze lub stosowano wstępne mielenie w temperaturze pokojowej, a następnie mielenie w wysokiej temperaturze. We wszystkich procesach uzyskano nanokrystalicze proszki o właściwościach magnetycznie twardych Proszki uzyskane w procesie mielenia stopu miały właściwości lepsze od proszków otrzymanych w procesie mechanicznej syntezy stopów, ponieważ były bardziej jednorodne i posiadały mniejszy udział fazy α-Fe.

4

Influence of heat treatment on magnetic properties of nanocrystalline Nd9Fe84Zr1B6 ribbons received by rapid solidification method

Ceglarek A., Płusa D., Pawlik P., Dośpiał M.

Archives of Metallurgy and Materials

|

2012

|

Vol. 57, iss. 1

229-232

EN

The effect of the annealing on the phase composition and magnetic properties of nanocomposite melt-spun Nd9Fe84Zr1B6 ribbons has been investigated. From the X-ray diffraction studies confirmed be thermomagnetic curves measurements results that the microstructure of the material investigated is composed of a mixture of magnetically hard Nd2Fe14B and soft α-Fe, Fe3B nanosized grains. The small amount of undesirable Nd2Fe23B3 metastable phase has been found which do not decompose at the highest annealing temperature. The hysteresis loop measurements certify that the ribbon annealed at 863K show the best coupling between the hard and soft magnetic phases and thus the highest coercivity of 0.38T. The grain sizes increase with increasing annealing temperature causing the coercivity to be decrease.

PL

Zbadano wpływ wygrzewania na skład fazowy i właściwości magnetyczne taśm nanokompozytowych Nd9Fe84Zr1B6 otrzymanych metodą szybkiego chłodzenia cieczy na wirującym miedzianym bębnie. Badania mikrostruktury potwierdzają zależności krzywych termomagnetycznych, z których wynika, że stop składa się z ziaren o rozmiarach nanometrycznych faz: magnetycznie miękkich α-Fe, Fe3B oraz magnetycznie twardej Nd2Fe14B. Stwierdzono niewielką ilość niepożądanej metastabilnej fazy, która nie ulega rozkładowi przy najwyższej temperaturze wygrzewania. Pomiary pętli histerezy magnetycznej dla taśmy wygrzanej w temperaturze 863K świadczą o najsilniejszych oddziaływaniach pomiędzy fazami, twardą i miękką. Rozmiar ziaren wzrasta we wzrostem temperatury wygrzewania, powodując spadek koercji. Koercja taśmy wygrzanej w temperaturze 863K ma największą wartość, wynoszącą 0.38T oraz najmniejszy rozmiar ziarna fazy Nd2Fe14B.