The Analysis of Microhardness Variations of Hydroformed P265TR1 Steel Axisymmetric Elements from Tubes

Miłek T.

Archives of Foundry Engineering

|

2020

|

Vol. 20, iss. 3

74--78

EN

The paper discusses the effect of upsetting ratio on distribution of the microhardness in longitudinal sections of hydroformed axisymmetric elements made from P265TR1 steel. The experimental research of hydroforming was carried out at a special stand which included a press with tooling and a hydraulic feeding system of oil. The measurements of microhardness were taken with a MATSUZAWA MMT-X3 Vickers hardness tester at a load of 100 g. The samples used in the tests were prepared from tube segments with a thin-wall ratio of 0.045. In the experiment, steel components were formed at upsetting coefficients of 0.07 and 0.09. For an established course of pressure and upsetting force, a series of steel components with exact representation of the die-cavity was formed. The paper provides a comparison of the microhardness distributions in three zones of longitudinal sections of axisymmetric elements at different degrees of material deformation. The greatest values of microhardness occurred in the area of cap for components at an upsetting coefficient 0.09.

2

Unconventional forming of tube ends

Moravec J.

Hutnik, Wiadomości Hutnicze

|

2017

|

Vol. 84, nr 8

377--379

EN

Machine tools have found application in the field of forming and unconventional forming in cases when such machine tools can be appropriately used for various tasks. Forming of tube ends is one of these tasks. The paper presents author’s solution for forming apparatus used in experimental work. These results have confirmed the suitability of using a lathe for the given above-mentioned tasks.

PL

Obrabiarki znalazły zastosowanie w procesach złożonego i niekonwencjonalnego kształtowania, pod warunkiem właściwego wykorzystania tych maszyn do różnych operacji technologicznych. Do tych operacji zalicza się kształtowanie końców rur. W artykule przedstawiono autorskie rozwiązanie dotyczące konstrukcji obrabiarki do kształtowania końców rur. Obrabiarkę tą wykorzystano w pracach eksperymentalnych. Wyniki eksperymentów potwierdziły możliwość aplikacji wykorzystania tokarki dla wyżej wymienionych zadań.

3

Research on inner surface of hydroformed tubes

Ceclan V. A., Grozav S. D., Kuric I.

Advances in Science and Technology. Research Journal

|

2017

|

Vol. 11, no 4

311--317

EN

In this paper a reserch regarding the surfece of hydroforming tubs, made by aluminium and cooper is presented. Tube hydroforming is very important production method considering that metal tubes are widely used in a great variety of engineering products, such as automobile, aircraft, air conditioner, air compressor, exhaust systems, fluid lines. The results show that the surface of tubes it is influence of the hydroforming process. the material of the tube in research of surface is also very important.

4

A comparative analysis methodology of calculation of strength tubesheets by european standards and guidelines for UDT

Celarek A., Talaga J.

Czasopismo Techniczne. Mechanika

|

2016

|

Y. 113, iss. 2-M

43--53

EN

This paper presents comparison of calculation methods of the required thickness of the tube sheet in the shell and tube heat exchanger compatible with the standards of the European standard PN - EN 13445-3, and the guidelines of the Polish Office of Technical Inspection (UDT). Details of the methods are illustrated by numerical examples – (calculations) for the selected design of the tubesheet.

PL

W artykule przedstawiono porównanie metod obliczeniowych wymaganej grubości ściany sitowej w płaszczowo-rurkowym wymienniku ciepła zgodnych ze standardami normy europejskiej PN-EN 13445-3 i wytycznymi polskiego Urzędu Dozoru Technicznego. Szczegóły metod zilustrowano przykładami liczbowymi dla wybranych konstrukcji dna sitowego.

5

Trace metal concentrations in free-ranger, tube-dweller chironomid larvae and a weakly polluted fluvial sediment

Grzybkowska M., Dukowska M., Michałowicz J., Leszczyńska J.

Oceanological and Hydrobiological Studies

|

2015

|

Vol. 44, No. 4

445--455

EN

The objective of this study was to analyze macroinvertebrate assemblages dominated by Chironomidae (Diptera) and to assess the protective nature of these midges’ larval tubes against trace metals in the weakly polluted Bzura River. This low order lowland river flows through the Łódź City Municipal Area and is supplied by a large amount of organic matter from ecotones and a polluted roadside. Determination of metal content in sediments and chironomid tissue and tubes was conducted using atomic absorption spectroscopy. Our study has shown that the composition of chironomid assemblages was not determined by trace metals but rather by high organic enrichment, which caused the dominance of two species representing the same trophic group − gathering collectors − but differing in behavior. One of them belongs to free-rangers (Prodiamesa olivacea), while the other (Chironomus riparius) to tube-dweller larvae. Although the accumulation of certain trace metals in the tubes was found, the larvae of both types of behavior had a similar concentration of metals in their tissues, which proves effective metal detoxification in these insects.

6

Zwiększenie trwałości rolek do formowania rur

Haduch Suski Z., Lozano Andrade J., García Rodríguez A., González H. R., Rodríguez E.

Tribologia

|

2014

|

nr 6

43--66

PL

Przemysł wytwarzania rur stosuje różne metody i techniki ich produkcji, jednak formowanie rur stalowych ze szwem ma największe osiągnięcia na rynku. Podstawowe narzędzie do ich formowania, czyli rolki są tradycyjnie wykonywane ze stali narzędziowych o wysokiej zawartości chromu, na przykład stali narzędziowej D2. Jednak jakość rur nowej generacji wykonywanych ze stali o wyższej wytrzymałości i twardości wymaga zastosowania nowych materiałów przewyższających właściwości mechaniczne stali D2. Zaistniała więc konieczność zmian technologii, przeprojektowania narzędzi, przebadania nowych materiałów i opracowania odpowiedniej obróbki cieplnej, zapewniając im dłuższą żywotność i zmniejszenie przestojów w celu spełnienia oczekiwań produkcyjnych. W niniejszym projekcie zostały przeanalizowane i ocenione najlepsze opcje przedstawione na rynku narzędzi do pracy na zimno w celu zwiększenia żywotności istniejących narzędzi (stal D2). Ocenę przeprowadzono w warunkach laboratoryjnych zbliżonych maksymalnie do parametrów produkcyjnych. Wykorzystano tester do badań tribologicznych (T-05) i wykonano badania dynamiczne (próba Charpy'ego). Wykazano przydatność nowych materiałów i możliwość uzyskania oszczędności.

EN

Industries engaged in roll forming of tubes apply different methodologies and innovating technologies in order to perform this task, but tubes with welded seams are more profitable. The basic tooling used to roll-form tubes, or rolls, are usually made of a tool steel with a high Chromium content, namely, D2 steel. However, in order to produce higher quality tubes of high-strength steels, higher mechanical properties than those shown by D2 steel are required. As a consequence, new technologies, designs, materials, and heat treatments have emerged so the new requirements are met. This has a direct impact on the costs incurred and the productivity of metalmechanic industries. In this project, various cold work steels were analysed and compared with D2 steel, in order to improve the tool life of rolls for roll forming of tubes. Tribological testing was done with a T-05 block-on-ring setup with testing conditions similar to those in real life. Charpy testing was done in order to obtain impact toughness. The obtained results are of great importance, because they may result on significant cost reductions.

7

Optymalizacja obróbki cieplnej typu TRIP rur ze stali 34MnB5 przeznaczonych do zastosowań w konstrukcji półosi samochodowych

Wiewiórowska S., Muskalski Z., Włoch K.

Hutnik, Wiadomości Hutnicze

|

2014

|

Vol. 81, nr 8

623--626

PL

Obecne wymagania stawiane materiałom konstrukcyjnym stosowanym w motoryzacji są ściśle związane z ich własnościami i dąży się, by stale stosowane do produkcji elementów konstrukcyjnych posiadały odpowiednio wysokie własności wytrzymałościowe powiązane z wysokimi własnościami plastycznymi. Warunek ten spełniają stale typu TRIP. W pracy przedstawiono wyniki optymalizacji procesu dwuetapowej obróbki cieplnej dla rur stosowanych w konstrukcji półosi samochodowych, prowadzonej w celu uzyskania struktury typu TRIP. W badaniach stosowano stal gatunku 34MnB5.

EN

The current requirements for construction materials used in the automotive industry are closely related to their properties, the objective is to steel use for production of structural elements have high strength properties related with high plastic properties. The TRIP steel meet this condition. The optimization two-stage heat treatment process for tubes use in construction of automotive drive half-shafts has been shown in the work. The 34MnB5 grade steel was used for research.

8

Deposit attack in tubes of power plant steam boilers

Balitskii A., Ripey I., Chmiel J.

Problemy Eksploatacji

|

2010

|

nr 4

79-89

EN

This article presents the results of the inspection of damaged tubes of steam boilers, the damage being a result of deposit attack. Changes in the chemical composition of feedwater, i.e. its hardness increased due to leaks in brass tubes of the turbine condenser, result in the formation of scale on the tube material, followed by corrosion, overheating and numerous defects. Only during one of the necessary stops, damage of varying degree to over 20 tubes was detected, from a pit (or crack initiation) to fractures of a few tubes. The results of visual inspection and mechanical and metallographic tests of the damaged tubes are given.

PL

W pracy przedstawiono wyniki badań uszkodzeń rur kotłów parowych, interpretowanych jako wynik procesów korozji podosadowej. Jako główne przyczyny uszkodzeń wskazuje się obecność w wodzie kotłowej związków żelaza (III) oraz związków miedzi (pochodzących z układu skraplacza turbiny), których osady stanowią obszary katodowe, stymulujące rozwój wżerów stanowiących anody. Przedstawiono wyniki inspekcji wizualnej rur, badań właściwości mechanicznych, badań mikrostruktury oraz analiz chemicznych.

9

On the problem of material properties in numerical simulation of tube hydroforming

Sadłowska H., Kocańda A.

Archives of Civil and Mechanical Engineering

|

2010

|

Vol. 10, no 4

77-83

EN

Hydroforming is a cost effective way of shaping various metals and alloys into lightweight, structurally stiff and strong pieces. The largest applications of hydroforming can be found in the automotive and aerospace industries. Among them, exhaust system components such as T-shapes or X-shapes connectors have been often manufactured by tube hydroforming. Typical tube hydroforming operation is made by a controlled application of internal pressure and axial feeding of tube material into deformation zone. The loading path of internal pressure versus axial feeding is the most important. It can be found by means of FEM simulation of the process to limit costs of experiments. However, the appropriate numerical model requires experimental data on tube material properties. Some simplifications to use sheet metal properties instead of tube properties have not been reliable. Especially cold worked tubes with small diameters require special methods to determine material properties in axial and circumferential directions. Such methods have been presented in the paper including some remarks on specimens' preparation, experimental set-up and image processing for getting strain values.

PL

Kształtowanie hydromechaniczne rur należy do nowoczesnych procesów obróbki plastycznej i jest stosowane ze względu na swoje liczne zalety: materiałooszczędność, zwiększenie sztywności i wytrzymałości elementów, zmniejszenie kosztów produkcji. Kształtowanie hydromechaniczne polega na rozpęczaniu materiału cieczą pod ciśnieniem w celu uzyskania zadanego przez matrycę kształtu. Często w procesach tych stosowana jest również dodatkowa siła osiowa, której zadaniem jest uzyskanie większych odkształceń formowanej rury. Warunkiem prawidłowo zaprojektowanego procesu jest odpowiednie złożenie przebiegu ciśnienia rozpęczającego i siły osiowej w czasie trwania kształtowania. W tym celu wykorzystuje się Metodę Elementów Skończonych, co pozwala obniżyć koszty związane z projektowaniem procesu. Warunkiem zbudowania prawidłowego procesu jest wykorzystanie danych doświadczalnych, a w szczególności danych materiałowych. Uzyskanie tych danych jest utrudnione w przypadku rur, szczególnie jeśli planuje się wykorzystanie rur bezszwowych o niewielkich średnicach. W takim przypadku istnieje potrzeba znalezienia nowych metod określania własności mechanicznych, nie tylko na kierunku osiowym, ale także na obwodzie rury. W referacie została zaprezentowana metoda określania własności mechanicznych rur na kierunku osiowym i obwodowym dla rur stalowych.

10

XV Konferencja naukowo-techniczna "Technologie produkcji rur w przemyśle metali nieżelaznych"

Zasadziński J.

Rudy i Metale Nieżelazne

|

2008

|

R. 53, nr 11

663-663

11

Study of the hot forming conditions of HSLA steel on the tensile testing machine

Kozelsky P., Melecky J., Schindler I., Cagala M.

Hutnik, Wiadomości Hutnicze

|

2008

|

Vol. 75, nr 8

486-488

EN

The aim of the conducted experimental work was to study the deformation behaviour in the hot state and causes that lead to failure of compactness of a microalloyed steel determined for the tube production. The results of the formability testing are presented, performed by measurements of the strength and plastic properties by means of the tensile test performed at the forming temperatures and displacement speed of the cross beam in the range of 6 to 300 mm/min. It was shown that in the case of this material it is not essentially possible to avoid a defect formation after its cooling by a change of the forming speed.

PL

Celem przeprowadzonego eksperymentu było zbadanie technologicznej plastyczności stali HSLA w warunkach przeróbki plastycznej na gorąco, jak również przyczyn pękania stali mikroskopowych stosowanych do produkcji rur. Zaprezentowano zależność wytrzymałości i właściwości plastycznych badanej stali od warunków odkształcania. Próby rozciągania prowadzono dla temperatur z zakresu przeróbki plastycznej na gorąco tej stali z prędkością w zakresie od 6 do 300 mm/min. Wykazano, że w przypadku badanej stali zmiana prędkości kształtowania nie wpływa w istotny sposób na możliwość uniknięcia defektów po operacji chłodzenia.

12

Pomiar temperatury w linii technologicznej zgrzewania stalowych rur z powłoką Al-Si

Żaba K., Nowak S.

Rudy i Metale Nieżelazne

|

2007

|

R. 52, nr 8

473-481

PL

Przedstawiono fizyczne podstawy bezstykowych pomiarów temperatury oraz oceną możliwości wykonania ciągłego pomiaru temperatury w linii technologicznej zgrzewania, z uwzględnieniem analizy metod pomiaru. Zamieszczono wyniki badań temperatury w strefie oraz linii zgrzewania za pomocą pirometru i kamery termowizyjnej.

EN

The paper presents the analysis of temperature measurement, evaluates the possibilities of continuous temperature measurement on process lines and the determination of temperature distribution. Tests were made during welding smooth and perforated pipes with Alusi coatings. The results of the temperature measurement helped to determine the working point of the line, i.e. the selection of optimum values of each process parameter. In the case of continuous measurement the results are used to control the process. The Information about the thermal field, its distribution along the circuit and the welding line can also be of interest, especially for the thermal flow area (SWC), where structural changes not only in the weld but also in its vicinity are observed. Pipe cracking outside the weld can be the result of this phenomenon. In order to make control of the SWC possible we should aim at gaining the best possible knowledge about the process. Tests covered continuous measurements of the maximum temperature in the welding area (the point where two edges of the open-joint tubes are in contact with each other) with a pyrometer placed in the line and observations with an infrared camera which were to determine the thermal field.

13

Ocena jakości rur spawanych laserowo

Nowak S., Żaba K., Krawczyk B.

Rudy i Metale Nieżelazne

|

2007

|

R. 52, nr 3

146-150

PL

Przedstawiono wyniki wstępnych prób laserowego, wzdłużnego spawania rur ze stali ferrytycznej. Celem prób było sprawdzenie możliwości uzyskania wyrobów spełniających wysokie wymagania przemysłu motoryzacyjnego.

EN

In the article results of first efforts of laser welding tubes of high-alloy steels (ferritic) about the 12 % Cr contents were described. Testing abilities was an aim of attempts of getting products meeting high requirements of the automotive industry. Laser welding such tubes is an alternative solution with respect to HF welding. He has this majority that he is increasing the probability of getting the connector, assuring more distant processing pipes. In the particular a plasticity is eliminating faults in the welding zone, limiting him. In the first stage attempts to weld ø 50'1.5 mm pipes were made, on the post for classical welding around migrating with the warhead. During attempts a power of the bundle, a speed, a breadth of the crack, moving the edge were being changed. As part of attempts they stated, that conditions of the lawsuit, in this case the power, the speed and putting the edge of the fricative pipe strongly are influencing the quality of the product. Attempts permitted for working guidelines out for examinations in the line of welding. Examinations in the production line were made on the laser installed at the Employer. In the article findings of, underlying examinations were described to the assessment of the quality of tubes.

14

Badania doświadczalne hydromechanicznego rozpęczania rur spawanych laserowo

Hyrcza-Michalska M., Grosman F.

Prace Naukowe Politechniki Warszawskiej. Mechanika

|

2007

|

z. 216

121--126

PL

W referacie przedstawiono wyniki badań procesu swobodnego, hydromechanicznego rozpęczania rur spawanych laserowo. Próbki rurowe do badań pozyskiwano poprzez gięcie w procesie walcowania blach stalowych w gatunkach DX56D+Z, H180BD+Z oraz FE 450 DP F. uzyskane w ten sposób rury szczelinowe łączono laserem. Aby umożliwić badania procesu kształtowania wsadów rurowych przy zastosowaniu metody rozpęczania ciśnieniem cieczy, zaprojektowano i zbudowano stanowisko badawcze do rozpęczania rur spawanych laserowo. Próby rozpęczania były realizowane do momentu utraty stateczności odkształcenia lub pękania rury. Na rozpęczonych rurach mierzono rozkłady odkształceń lokalnych przy zastosowaniu metody siatek koordynacyjnych. W referacie przedstawiono porównanie rozkładów odkształceń lokalnych dla trzech rur, wykonanych z różnych blach.

EN

The paper presents the results of unbounded hydro-bulging process testing of laser welded tubes. Tubular samples have been made in the process of bending and rolling the steel strips of DX56D+Z, H180BD+Z and FE 450 DP F grades. Open-joint tubes have been welded by laser. A test stand for examining the process of tubular blanks forming, applying the method of bulging by liquid from inside, was designed and built. The hydro-bulging tests have been carried out until the strain stability was lost and there was a crack on the tube. The local strain distributions on hydro-bulging tubular blanks were measured by the co-ordination net method. The comparison of local strain distributions for three tubes, made of different materials, is present in this paper.

15

Badania odporności korozyjnej rur z powłoką Al-Si przeznaczonych na elementy układów wydechowych. Badania laboratoryjne

Żaba K., Nowak S., Kąc S.

Rudy i Metale Nieżelazne

|

2005

|

R. 50, nr 12

679-685

PL

W artykule zamieszczono wyniki niestandardowych, specjalnie opracowanych testów, odwzorowujacych warunki pracy układów wydechowych. Próbki taśmy, rur oraz elementów układu wydechowego poddano działaniu zmiennego środowiska pracy w różnych czasie. Stan próbek oceniano wizualnie (dokumentacja fotograficzna) oraz za pomocą skaningowego mikroskopu elektronowego.

EN

Welded pipes with aluminium-silicon coatings are used to manufacture exhaust systems parts because in their case steel strength features are connected with corrosion and high temperature resistance of the coating. Under the conditions of intensive corrosion impact resulting from periodical heating and cooling, and the influence of the environment which contains chloride ions, SO(4)(-) and others, with a different in time thickness of the electrolyte layer, in the presence of contamination having hygroscopic properties, the protective action of the coating is the result of corrosion resistance of passivated aluminium. Silicon addition increases high temperature resistance significantly and diminishes problems of application. The coating contains ca 9 % of Si and has a standard thickness ca 20 mun. As in the case of a fire-applied zinc coating, it has two layers, with an intermediate layer of an alloy of the base and coating components. If the coating, and, especially its alloy layer, leaks, then corrosion cells will be created. In these cells, uncovered steel surfaces having lower electrochemical potential make up anodes. The coating will not provide protection then. The paper presents the results of non-standard, specially prepared tests which reflect working conditions of exhaust systems. Samples of strips, pipes and parts of exhaust systems have been exposed to variable working environment in different times. The tests consisted of two stages: -testing corrosion resistance of the samples under snowy and snow mud conditions, -testing the changes in the coating and base after 40,000 km exploitation of the exhaust system. Samples were evaluated visually (photo documentation) and with a scanning electron microscope.

16

Wyznaczanie lokalnych współczynników wnikania ciepła na membranowych powierzchniach konwekcyjnych i rurach wzdłużnie ożebrowanych

Taler J., Cebula A.

Prace Naukowe Politechniki Warszawskiej. Mechanika

|

2003

|

z. 202

263--272

PL

Membranowe powierzchnie konwekcyjne i rury wzdłużnie ożebrowane, szeroko stosowane w kotlach parowych i wodnych mogą być wykorzystywane do budowy parowych podgrzewaczy powietrza, podgrzewaczy wody i konwekcyjnych przegrzewaczy pary. W pracy przedstawiono metodę wyznaczania lokalnych wspólczynników wnikania ciepła od strony powietrza lub spalin bazującej na pomiarze rozkładu temperatury na powierzchni zewnętrznej. Na podstawie przeprowadzonych badań eksperymentalnych wyznaczono rozkłady lokalnych wspólczynników wnikania ciepła oraz wyprowadzono korelacje na średni wspólczynnik wnikania ciepła od strony powietrza dla rur wzdłużnie ożebrowanych i powierzchni membranowych. Przeprowadzono również symulację komputerową zjawisk przepływowo-cieplnych po stronie powietrza za pomocą programu Fluent. otrzymując w ten sposób rozkład temperatury i prędkości w modelowanych wymiennikach.

EN

The paper presents the results of measurements and calculations of heat transfer coefficients in banks of fin tubes (longitudinaIly ribbed) and membrane type pipe banks. The local and mean heat transfer coefficients on the circumference of exchanger pipes are determined. Correlation formulas for the Nusselt number (Nu) as a function of the Reynolds number (Re) are derived. The experiments were carried out in the range of Re = 5,000 to Re = 50,000.

17

Analiza stanu naprężenia podczas swobodnego ciągnienia rur przez ciągadła kształtowe

Knapiński M.

Prace Naukowe Politechniki Warszawskiej. Mechanika

|

2003

|

z. 201

91--96

PL

W procesie ciągnienia produkowane są wyroby precyzyjne o bardzo zawężonych tolerancjach grubości ścianki i eliptyczności średnicy wewnętrznej i zewnętrznej. Szczególnie trudną do wyeliminiowania w procesie ciągnienia wadą wsadu jest różnościenność rur wsadowych. Metodą pozwalającą na wyrównywanie grubości ścianki na obwodzie rury jest ciągnienie swobodne [1,2]. W pracy przeprowadzono symulację komputerową procesu ciągnienia swobodnego rur o założonej, zmiennej grubości ścianki na obwodzie rury. Analizę przeprowadzono dla 3 typów ciągadeł: stożkowego o kącie 2 alfa=30 st, parabolicznego wklęsłego oraz parabolicznego wypukłego. Obliczenia prowadzono w oparciu o program komputerowy FORGE3 z zastosowaniem sztywno-plastycznego modelu odkształcanego metalu. w wyniku symulacji komputerowych uzyskano obrazy stanu naprężeń promieniowych i obwodowych panujących w ściance rury o zmiennej grubości na obwodzie w obszarze odkształcenia. Analiza stanu naprężenia pozwala wyjaśnić mechanizm wyrównywania grubości ścianki na obwodzie rury podczas ciągnienia swobodnego.

EN

A computer simulation of the process of sink drawing of tubes with a present, variable wall thickness over the tube perimeter has been performed within the present study. The analysis was conducted for three types of drawing die: a conical drawing die of an angle 2(alfa)=30st., an concave parabolic drawing die, and and a convex parabolic drawing die. Computations were performed by using the FORGE3 computer program with the use of rigid-plastic model of deformed metal. As a result of computer simulations, the pictures of the state of radial and circumferential stresses occuring in the deformation region of the tube wall with a variable thickness over the perimeter were obtained. The analysis of the state of stress makes it possible to explain the mechanism of wall thickness equalisation on the tube perimeter during sink drawing.