Investigation on Evolution of Microstructures and Characterization During FSW of AZ80A Mg Alloy

Sevvel P., Jaiganesh V.

Archives of Metallurgy and Materials

2017

Vol. 62, iss. 3

1779--1785

Experimental investigation was conducted to find out microstructural characteristic changes arising in the weldments AZ80A Mg alloys obtained using the friction stir welding. Tools with three different pin profile geometries were employed during this investigation at constant tool rotational speed and feed rate. Tensile tests are performed and the tensile fracture surfaces are examined using the Scanning Electron Microscope (SEM) and the obtained SEM images are used for microstructural investigations. From the experimental results, it was observed that the geometry of the tool pin plays a significant role in producing essential stirring action there by regulating the flow of the plasticized material and leading to the formation of small sized grains having equally distributed fine strengthening precipitates. These structured grains have a direct reflecting impact in increasing the hardness and mechanical properties of the fabricated joints at the nugget zone of the friction stir welded AZ80A Mg alloy joints.

Effect of tool geometry and welding speed on mechanical properties and microstructure of friction stir welded joints of aluminium alloys AA6082-T6

Patil H. S., Soman S. N.

Archive of Mechanical Engineering

2014

Vol. LXI, nr 3

455--468

Friction stir welding is a solid state innovative joining technique, widely being used for joining aluminium alloys in aerospace, marine automotive and many other applications of commercial importance. The welding parameters and tool pin profile play a major role in deciding the weld quality. In this paper, an attempt has been made to understand the influences of welding speed and pin profile of the tool on friction stir welded joints of AA6082-T6 alloy. Three different tool pin profiles (tapered cylindrical four flutes, triangular and hexagonal) have been used to fabricate the joints at different welding speeds in the range of 30 to 74 mm/min. Microhardness (HV) and tensile tests performed at room temperature were used to evaluate the mechanical properties of the joints. In order to analyse the microstructural evolution of the material, the weld’s cross-sections were observed optically and SEM observations were made of the fracture surfaces. From this investigation it is found that the hexagonal tool pin profile produces mechanically sound and metallurgically defect free welds compared to other tool pin profiles.

Spawanie tarciowe z przemieszaniem (FSW) jest innowacyjną techniką spawalniczą stosowaną szeroko przy łączeniu stopów aluminiowych w lotnictwie, przemyśle okrętowym, motoryzacyjnym i w wielu innych istotnych komercyjnie zastosowaniach. Parametry spawania i profil trzpienia narzędzia grają główną rolę gdy chodzi o jakość spawu. W pracy podjęto próbę zbadania wpływów szybkości spawania i profilu trzpienia na spawanie tarciowe z przemieszaniem stopu AA6082-T6. Trzy różne profile trzpienia (zwężający się cylindryczny z czterema żłobkami, trójkątny i sześciokątny) były używane do wykonania spawów przy różnych szybkościach spawania w zakresie od 30 do 74 mm/min. W celu oceny właściwości mechanicznych spawów wykonano badanie mikrotwardości (HV) oraz testy na rozciąganie w temperaturze pokojowej. Dla oceny mikrostrukturalnej ewolucji materiału przeprowadzono obserwacje przekrojów spawu metodą optyczną, a obserwacje powierzchni pęknięć przy pomocy elektronowego mikroskopu skaningowego (SEM). Na podstawie badań stwierdzono, że zastosowanie sześciokątnego profilu trzpienia narzędzia daje spawy solidne mechanicznie i wolne od defektów, lepsze niż dla pozostałych profili trzpienia.