The effect of mechanochemical processing on formation of Ca-α-SiAlON:Eu2+ powders

Michalik D., Pawlik T., Sopicka-Lizer M., Lisiecki R.

Materiały Ceramiczne

2016

T. 68, nr 4

300--304

The Ca-α-SiAlON:Eu2+ powders were developed by combining mechanochemical processing (MCP) of the initial powders with the subsequent solid state reaction in the reducing atmosphere of a graphite furnace. The photoluminescence (PL) spectra of the mono-phase Ca-α-SiAlON:Eu2+ phosphor powder were compared to the mono-phase powders produced without the MCP step. Specimens were synthesized in the temperature range of 1450-1650 °C for 2 h under a nitrogen flow. Mechanochemical processing of the initial mixture of nitrides led to their surface oxidation and formation of a larger amount of the oxynitride liquid. On the other hand launching the Eu2+ ions among additives during MCP and the subsequent Ca-Al-Si-Eu-O-N eutectic liquid formation during the thermal treatment is responsible for a higher optical performance of the resultant phosphor.

W badaniach uzyskano luminescencyjne proszki Ca-α-sialon:Eu2+ dwuetapową metodą obróbki mechano-chemicznej (MCP) prekursorów sialonowych i ich następczej syntezy metodą reakcji w stanie stałym w piecu grafitowym z przepływem azotu. Uzyskany materiał charakteryzował się budową jednofazową. W artykule porównano właściwości luminescencyjne proszków sialonowych, wytworzonych metodą wspomaganą procesem MCP, z proszkiem pozyskanym metodą konwencjonalną. Badane próbki syntezowano w temperaturach z zakresu 1450-1650 °C w czasie 2 godzin w przepływie azotu. Proces MCP zastosowany do prekursorów sialonowych prowadził do częściowego powierzchniowego utlenienia się proszków i tworzenia większej ilości fazy ciekłej. Z drugiej strony MCP w układzie Ca-Al-Si-Eu-O-N sprzyja tworzeniu się eutektyki ułatwiającej proces dyfuzji jonów europu, co jest odpowiedzialne za polepszenie właściwości optycznych badanego luminoforu.

The effect of synthesis parameters on luminescence properties of Ca-α-Sialon: Eu2+

Michalik D., Sopicka-Lizer M., Pawlik T., Lisiecki R.

Archives of Metallurgy and Materials

2013

Vol. 58, iss. 4

1309--1312

The goal of this study was to investigate influence of the synthesis parameters on the luminescence properties of Ca-α-Sialon doped with Eu2+. The compound of Eu0.07Ca0.73Si9.6Al2.4O0.8N15.2 was prepared by the solid state reaction method from the mixture of the relevant oxides, Si3N4 and CaCO3. Synthesis was carried out in the temperature range of 1600-1700°C for 2-8 h in a reduction atmosphere (N2+CO). The structure and morphology of obtained powders were analyzed by XRD and SEM/EDS methods, respectively. Content of nitrogen/oxygen was also measured. Optical properties were investigated by excitation, emission and reflection spectra. Obtained results show strong influence of synthesis temperature on the phase composition and intensity of emission of Ca- -Sialon:Eu2+ powder compound.

Celem badań było przeanalizowanie wpływu parametrów syntezy wysokotemperaturowej na właściwości ceramicznego proszku Ca- α -sialon domieszkowanego europem. Związek o stechiometrycznym wzorze Eu0.07Ca0.73Si9.6Al2.4O0.8N15.2 został przygotowany metodą reakcji w fazie stałej z odpowiednich tlenków. Si3N4 and CaCO3 oraz CaCO3. Reakcje wysokotemperaturowe prowadzono w zakresie temperatur 1600-1700 C przez 2-8h w atmosferze redukcyjnej (N2+CO). Morfologię oraz skład chemiczny proszków zbadano przy użyciu skaningowego mikroskopu elektronowego z przystawką do mikroanalizy rentgenowskiej (SEM/EDS). Skład fazowy analizowano przy pomocy metod dyfrakcji rentgenowskiej (XRD). Określono stosunek tlen/azot w otrzymanych związkach. Scharakteryzowano zmiany właściwości optycznych na podstawie widm wzbudzenia, emisji oraz odbicia dyfuzyjnego (PL). Otrzymane wyniki prezentują wpływ temperatury syntezy na skład fazowy oraz intensywność emisji luminoforu Ca-α-Sialon: Eu2+.